Block copolymers and process for their preparation
Assignee: Goodrich Corp
•
Filing: 1982-09-29
•
Granted: 1984-05-29
•
Expires: 2002-09-29
Abstract
Abstract Under particular conditions, a cationic ring-opening polymerization of an (single) oxirane monomer selected from the group consisting of an acyclic glycidyl ether, a cyclic glycidyl ether, and a haloalkyl epoxide, in the presence of a hydroxyl-terminated prepolymer ("HTP") and a particular catalyst, produces a polymerization having `living polymerization` characteristics, provided the OH groups are aliphatic OH groups and not aromatic OH groups. The result is an AB or ABA type block copolymer the molecular weight (mol wt) of which is directly proportional to the conversion of the monomer to the block copolymer. The HTP which may be a mono-, di-, tri-, or tetra-hydroxyl-terminated prepolymer, serves as a chain propagator which initially furnishes OH groups as propagation sites. Linear block copolymers or branched block copolymers are formed, depending upon the structure of the HTP. Where one segment of an AB or ABA type block contains halogen, the segment may be aminated. If the other segment is hydrophobic, the aminated block copolymer is amphiphilic.
Inventors
- 👤 Yoshihisa Okamoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 02:23
CPC Classifications
C; C08; C08G; C08G65/00; C08G65/02; C08G65/04; C08G65/32; C08G65/329; C08G65/333; C08G65/33303; C08G65/33306
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
279 words
A block copolymer of a hydroxyl-terminated prepolymer (HTP) and an oxirane monomer, said block copolymer having the structure R.sup.1 --O--[A].sub.a --H].sub.b (III) wherein, R 1 represents the residue of said HTP which originally contains from 1 to about 4 terminal aliphatic hydroxyl groups; A represents the residue of a single ring-openable oxirane monomer selected from the group consisting of (i) an aliphatic or aromatic glycidyl ether having the structure ##STR5## wherein R 2 and R 3 is each independently selected from the group consisting of hydrogen, alkyl having from 1 to about 40 carbon atoms, haloalkyl, alkenyl having from 2 to about 40 carbon atoms, haloalkenyl, alkoxyalkyl having from 1 to about 40 carbon atoms, aryl (Ar) or substituted aryl (Ar-Q), wherein Q is selected from the group consisting of alkyl, haloalkyl each having from 1 to about 10 carbon atoms, alkenyl and haloalkenyl each having from 2 to about 10 carbon atoms; and, (ii) a haloalkyl epoxide having the structure ##STR6## wherein X is halogen atom and R 4 and R 5 is each independently selected from the group consisting of hydrogen and alkyl having from 1 to about 4 carbon atoms; so that the molecular weight of the resulting block copolymer is directly proportional to the amount of monomer converted; and, a represents an integer in the range from about 5 to about 100; b represents an integer in the range from 1 to about 4; so that the molecular weight of each of the segments of the copolymer is in the range from about 500 to about 10,000, and the molecular weight of the block copolymer is in the range from about 500 to about 500,000.
Claim 2
Dependent Claim
279 words
A block copolymer of a hydroxyl-terminated prepolymer (HTP) and an oxirane monomer, said block copolymer having the structure R.sup.1 --O--[A].sub.a --H].sub.b (III) wherein, R 1 represents the residue of said HTP which originally contains from 1 to about 4 terminal aliphatic hydroxyl groups; A represents the residue of a single ring-openable oxirane monomer selected from the group consisting of (i) an aliphatic or aromatic glycidyl ether having the structure ##STR5## wherein R 2 and R 3 is each independently selected from the group consisting of hydrogen, alkyl having from 1 to about 40 carbon atoms, haloalkyl, alkenyl having from 2 to about 40 carbon atoms, haloalkenyl, alkoxyalkyl having from 1 to about 40 carbon atoms, aryl (Ar) or substituted aryl (Ar-Q), wherein Q is selected from the group consisting of alkyl, haloalkyl each having from 1 to about 10 carbon atoms, alkenyl and haloalkenyl each having from 2 to about 10 carbon atoms; and, (ii) a haloalkyl epoxide having the structure ##STR6## wherein X is halogen atom and R 4 and R 5 is each independently selected from the group consisting of hydrogen and alkyl having from 1 to about 4 carbon atoms; so that the molecular weight of the resulting block copolymer is directly proportional to the amount of monomer converted; and, a represents an integer in the range from about 5 to about 100; b represents an integer in the range from 1 to about 4; so that the molecular weight of each of the segments of the copolymer is in the range from about 500 to about 10,000, and the molecular weight of the block copolymer is in the range from about 500 to about 500,000.
Claim 3
Dependent Claim
98 words
The block copolyer of claim 1 wherein said HTP is a mono-, di-, tri, or tetra-hydroxyl terminated prepolymer having a molecular weight in the range of from 500 to about 15,000, and said R 1 is the residue of said prepolymer which is selected from the group consisting of a poly(alkylene ether) having at least 4 carbon atoms in a repeating unit, a polyalkadiene in which the repeating unit has from 4 to about 5 carbon atoms, a polyalkane, and a copolymer of said alkadiene with a vinyl aromatic monomer having from 8 to about 10 carbon atoms.
Claim 4
Dependent Claim
176 words
The block copolymer of claim 2 wherein said HTP is selected from the group consisting of mono-, and di-hydroxyl terminated (i) poly(butadienes) and poly(pentadienes) having a mol wt in the range from about 500 to about 15,000; (ii) poly(tetramethylene ether) and poly(pentamethylene ether) having a mol wt in the range from about 500 to about 10,000; (iii) polyalkane having a mol wt in the range from about 140 to about 700; (iv) poly(glycidyl ether) having the structure (I) with a mol wt in the range from about 500 to about 12,000 wherein the repeating unit is selected from the group consisting of an alkyl glycidyl ether having from 4 to about 12 carbon atoms; an aryl or aralkyl glycidyl ether having from 9 to about 20 carbon atoms; alkenyl or substituted alkenyl glycidyl ether having from 5 to about 12 carbon atoms; and (v) poly(haloalkylene ether) having the structure (II) with a molecular weight in the range of from about 500 to about 10,000 wherein the repeating unit has from 3 to about 8 carbon atoms.
Claim 5
Dependent Claim
85 words
The block copolymer of claim 3 wherein said alkyl glycidyl ether is selected from the group consisting of methyl glycidyl ether, propyl glycidyl ether and butyl glycidyl ether; said aryl glycidyl ether is phenyl glycidyl ether; said alkenyl glycidyl ether is selected from the group consisting of vinyl glycidyl ether, allyl glycidyl ether, butenylglycidyl ether, 4-vinylcyclcohexyl glycidyl ether, cyclohexenylmethyl glycidyl ether, and o-allyl-phenyl glycidyl ether; and said poly(haloalkylene ether) is selected from the group consisting of 1-chloro-2,3-epoxypropane(epichlorohydrin), 1-bromo-2,3-epoxypropane(epibromohydrin), 1-chloro-2,3-epoxybutane, 1-iodo-2,3-epoxyhexane, 3-chloro-4,5-epoxyoctane, 1-chloro-2,3-epoxycyclohexane; 1-bromo-2,3-epoxy-3-methylbutane; and, 2-chloro-2-methyl-3,4-epoxypentane.
Claim 6
Dependent Claim
31 words
The block copolymer of claim 4 wherein said HTP is selected from the group consisting of mono-, and di-hydroxyl-terminated poly(butadienes), poly(tetramethylene ether), poly(allyl glycidyl ether), poly(phenyl glycidyl ether), poly(isoprenes-co-styrene), and poly(butadines-co-styrene).
Claim 7
Dependent Claim
32 words
The block copolymer of claim 1 wherein segment A, and, optionally, R 1 , contains a reactive halogen capable of an addition reaction with an amine to yield an aminated block copolymer.
Claim 8
Dependent Claim
61 words
The block copolymer of claim 6 wherein said aminated block copolymer is an amphiphilic block copolymer having the structure ##STR7## wherein X represents a halogen, and R 3 6 is the residue of an amine selected from the group consisting of an alkylamine, dialkylamine, trialkylamine, cyclic alkylamine, fatty amine, polymeric amine, aromatic amine, polyetheramine, alkanolamine, thiazine, morpholine and a silane-containing amine.
Claim 9
Dependent Claim
26 words
The aminated block copolymer of claim 7 wherein A is epichlorohydrin, and said amine is a lower alkylamine having from 1 to about 6 carbon atoms.
Claim 10
Dependent Claim
18 words
The amphiphilic block copolymer of claim 7 wherein at least 20 percent of all reactive halogens are aminated.
Claim 11
Dependent Claim
37 words
The amphiphilic block copolymer of claim 7 wherein segment A is selected from the group consisting of allyl glycidyl ether, phenyl glycidyl ether and a lower alkyl glycidyl ether having from 1 to about 6 carbon atoms.
Claim 12
Dependent Claim
138 words
A process for the manufacture of a block copolymer having the structure (III) of a hydroxyl-terminated prepolymer (HTP) and an oxirane monomer, which process comprises, (i) polymerizing, a HTP with a single oxirane monomer selected from the group consisting of an acyclic glycidyl ether, a cyclic glycidyl ether, and a haloalkyl epoxide, in the presence of at least 0.001 part per 100 parts by weight of oxirane reactants of a catalyst selected from the group consisting of an HMF 6 acid, and, an oxonium salt of the HMF 6 acid, wherein M is an element selected from the group consisting of phosphorus, arsenic and antimony, at a temperature in the range from about 0° C. to about 100° C., and, (ii) recovering said block copolymer which is formed in an amount directly proportional to the conversion of monomer.
Claim 13
Dependent Claim
138 words
A process for the manufacture of a block copolymer having the structure (III) of a hydroxyl-terminated prepolymer (HTP) and an oxirane monomer, which process comprises, (i) polymerizing, a HTP with a single oxirane monomer selected from the group consisting of an acyclic glycidyl ether, a cyclic glycidyl ether, and a haloalkyl epoxide, in the presence of at least 0.001 part per 100 parts by weight of oxirane reactants of a catalyst selected from the group consisting of an HMF 6 acid, and, an oxonium salt of the HMF 6 acid, wherein M is an element selected from the group consisting of phosphorus, arsenic and antimony, at a temperature in the range from about 0° C. to about 100° C., and, (ii) recovering said block copolymer which is formed in an amount directly proportional to the conversion of monomer.
Claim 14
Dependent Claim
87 words
The process of claim 11 wherein said HTP is a mono-, di-, tri, or tetra-hydroxyl-terminated prepolymer having a molecular weight in the range of from about 200 to about 15,000, and said prepolymer is selected from the group consisting of a poly(alkylene ether) having at least 4 carbon atoms in a repeating unit, a poly(alkadienes) in which the repeating unit has from 4 to about 5 carbon atoms, and a copolymer of said alkadiene with a vinyl aromatic monomer having from 8 to about 10 carbon atoms.
Claim 15
Dependent Claim
176 words
The process of claim 12 wherein said block copolymer is selected from the group consisting of mono-, and di-hydroxyl-terminated (i) poly(butadienes) and poly(pentadienes) having a mol wt in the range from about 500 to about 15,000; (ii) poly(tetramethylene ether) and poly(pentamethylene ether) having a mol wt in the range from about 500 to about 10,000; (iii) polyalkane having a mol wt in the range from about 140 to about 700; (iv) poly(glycidyl ether) having the structure (I) with a mol wt in the range from about 500 to about 12,000 wherein the repeating unit is selected from the group consisting of an alkyl glycidyl ether having from 4 to about 12 carbon atoms, an aryl or aralkyl glycidyl ether having from 9 to about 20 carbon atoms, alkenyl or substituted alkenyl glycidyl ether having from 5 to about 12 carbon atoms; and, (v) a poly(haloalkylene ether) having the structure (II) with a mol wt in the range of from about 500 to about 10,000 wherein the repeating unit has from 3 to about 8 carbon atoms.
Claim 16
Dependent Claim
84 words
The process of claim 13 wherein (a) said alkyl glycidyl ether is selected from the group consisting of methyl glycidyl ether, propyl glycidyl ether; (b) said aryl glycidyl ether is phenyl glycidyl ether; (c) said alkenyl glycidyl ether is selected from the group consisting of vinyl glycidyl ether, allyl glycidyl ether, butenylglycidyl ether, 4-vinylcyclohexyl glycidyl ether, cyclohexenylmethyl glycidyl ether, and o-allyl-phenyl glycidyl ether; and, (d) said poly(haloalkylene ether) is selected from the group consisting of 1-chloro-2,3-epoxypropane(epichlorohydrin), 1-bromo-2,3-epoxypropane(epibromohydrin), 1-chloro-2,3-epoxybutane, 1-iodo-2,3-epoxyhexane, 3-chloro-4,5-epoxyoctane, 1-chloro-2,3-epoxycyclohexane, 1-bromo-2,3-epoxy-3-methylbutane, and, 2-chloro-2-methyl-3,4-epoxypentane.
Claim 17
Dependent Claim
32 words
The process of claim 14 wherein said HTP is selected from the group consisting of mono-, and di-hydroxyl-terminated poly(butadienes), poly(tetramethylene ether), poly(allyl glycidyl ether), poly(butyl glycidyl ether), poly(phenyl glycidyl ether) and poly(butadienes-co-styrene).
Claim 18
Dependent Claim
122 words
The process of claim 11 wherein segment A of said block copolymer contains a reactive halogen capable of an addition reaction with an amine, and, optionally, R 1 of said block copolymer contains a reactive halogen capable of an addition reaction with an amine, so as to have formed a halogen-containing block copolymer, said process including, in addition, contacting said halogen-containing block copolymer with a preselected amount of an amine sufficient to aminate a preselected amount of said reactive halogen, optionally in the presence of a solvent for said amine and said halogen-containing block copolymer, at a temperature in the range from about 40° C. to about 110° C., and a pressure in the range from about 50 to about 500 psig.
Claim 19
Dependent Claim
43 words
The process of claim 16 wherein said halogen-containing block copolymer includes a segment aminated with an amine selected from the group consisting of an alkylamine, dialkylamine, trialkylamine, cyclic alkylamine, fatty amine, polymeric amine, aromatic amine, polyetheramine, alkanolamine, thiazine, morpholine and a silane-containing amine.
Claim 20
Dependent Claim
30 words
The process of claim 17 wherein said halogen-containing block copolymer includes a segment aminated with an amine which is a lower alkylamine having from 1 to about 6 carbon atoms.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-29 | 1987-11-28 | 1988-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-29 | 1991-11-28 | 1992-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-29 | 1995-11-28 | 1996-05-29 | $7700.00 | Window Closed / Lapsed |