Heat distortion-resistant thermoplastic semi-conductive composition
Assignee: Millennium Petrochemicals Inc
•
Filing: 1982-06-15
•
Granted: 1984-05-29
•
Expires: 2002-06-15
Abstract
Abstract A heat distortion-resistant thermoplastic semi-conductive composition which includes ethylene-vinyl acetate and/or an ethylene acrylate ester copolymer, and an admixture of high density polyethylene and linear low density polyethylene in addition to the electrically conductive component and other additives normally forming part of such compositions.
Inventors
- 👤 Anthony Barlow
- 👤 Lawrence A. Meeks
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 01:54
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/20; H01B1/24; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/294; Y10T428/2942; Y10T428/2947
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
111 words
A heat distortion-resistant non-crosslinked thermoplastic semiconductive composition comprising a copolymer selected from the group consisting of ethylene-vinyl acetate copolymer and ethylene-acrylate ester copolymer, an admixture of high density polyethylene and linear low density polyethylene and carbon black, said ethylene copolymer being present in an amount of from about 20 to about 60 weight percent, said admixture of polyethylene homopolymers being present in an amount of from about 10 to about 45 weight percent with the low density polymer constituting about 40 to about 75 percent of said admixture, all other percentages being based on the weight of the total composition and the carbon black concentration being present in a conductive amount.
Claim 2
Dependent Claim
111 words
A heat distortion-resistant non-crosslinked thermoplastic semiconductive composition comprising a copolymer selected from the group consisting of ethylene-vinyl acetate copolymer and ethylene-acrylate ester copolymer, an admixture of high density polyethylene and linear low density polyethylene and carbon black, said ethylene copolymer being present in an amount of from about 20 to about 60 weight percent, said admixture of polyethylene homopolymers being present in an amount of from about 10 to about 45 weight percent with the low density polymer constituting about 40 to about 75 percent of said admixture, all other percentages being based on the weight of the total composition and the carbon black concentration being present in a conductive amount.
Claim 3
Dependent Claim
29 words
The composition of claim 1 wherein the conductive component, carbon black, is present in said composition in an amount of from about 25 to about 35 percent by weight.
Claim 4
Dependent Claim
27 words
The composition of claim 1 wherein said admixture is present in an amount of from about 15 to about 35 percent by weight of said total composition.
Claim 5
Dependent Claim
39 words
The composition of claim 1 or 2 wherein said copolymer is ethylene-vinyl acetate copolymer containing vinyl acetate monomer in an amount of from about 7 to about 45 percent by weight based on the total weight of said copolymer.
Claim 6
Dependent Claim
31 words
The composition of claim 3 wherein the amount of said vinyl acetate monomer is from about 12 to about 28 percent by weight based on the total weight of said copolymer.
Claim 7
Dependent Claim
31 words
The composition of claim 4 wherein the amount of said vinyl acetate monomer is from about 17 to about 19 percent by weight based on the total weight of said copolymer.
Claim 8
Dependent Claim
29 words
The composition of claim 1 or 2 wherein said ethylene-vinyl acetate copolymer further contains a minor amount of one or more other monomers copolymerizable with ethylene and vinyl acetate.
Claim 9
Dependent Claim
39 words
The composition of claim 1 or 2 wherein said copolymer is ethylene-acrylate ester copolymer containing acrylate ester monomer in an amount of from about 7 to about 45 percent by weight based on the total weight of said copolymer.
Claim 10
Dependent Claim
31 words
The composition of claim 8 wherein the amount of said acrylate ester monomer is from about 12 to about 28 percent by weight based on the total weight of said copolymer.
Claim 11
Dependent Claim
31 words
The composition of claim 8 wherein the amount of said acrylate ester monomer is from about 17 to about 9 percent by weight based on the total weight of said copolymer.
Claim 12
Dependent Claim
13 words
The composition of claim 8 wherein said acrylate ester monomer is ethyl acrylate.
Claim 13
Dependent Claim
13 words
The composition of claim 8 wherein said acrylate ester monomer is methyl acrylate.
Claim 14
Dependent Claim
37 words
The composition of claim 12 wherein said percent by weight of linear low density polyethylene is from about 60 to about 70 percent by weight of said admixture of high density polyethylene and linear low density polyethylene.
Claim 15
Dependent Claim
31 words
The composition of claim 1 which further comprises an antioxidant in an amount of from about 0.2 to about 1.0 percent by weight based on the total weight of said composition.
Claim 16
Dependent Claim
10 words
The composition of claim 13 wherein said antioxident is 4,4'-thiobis-6-tert-butyl-meta-cresol.
Claim 17
Dependent Claim
31 words
The composition of claim 1 which further comprises a lubricant in an amount of from about 0.1 to about 0.5 percent by weight based on the total weight of said composition.
Claim 18
Dependent Claim
11 words
The composition of claim 16 wherein said lubricant is calcium stearate.
Claim 19
Dependent Claim
32 words
An insulated electrical conductor comprising an electrically conductive core, a layer of insulative material immediately surrounding said core, and a semi-conductive shield comprising the composition of claim 1 surrounding said insulative layer.
Claim 20
Dependent Claim
13 words
The conductor of claim 18 wherein said core is a high voltage conductor.
Claim 21
Dependent Claim
15 words
The conductor of claim 18 or 19 wherein said insulative layer comprises a crosslinked polyolefin.
Claim 22
Dependent Claim
12 words
The conductor of claim 20 wherein said crosslinked polyolefin is crosslinked polyethylene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-29 | 1987-11-28 | 1988-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-29 | 1991-11-28 | 1992-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-29 | 1995-11-28 | 1996-05-29 | $7700.00 | Window Closed / Lapsed |