Magnetic recording medium and method
Assignee: TDK Corp
•
Filing: 1982-06-01
•
Granted: 1984-05-29
•
Expires: 2002-06-01
Abstract
Abstract The invention provides a novel magnetic recording tape comprising a film base, a magnetic coating layer on one surface and a backing layer on the other surface, the backing layer containing an abrasive powder having a hardness of at least 4 in the Mohs scale, such as silicon carbide and the like, dispersed in a binder matrix formed by curing a radiation-sensitive polymer by irradiating with a high energy radiation, such as electron beams accelerated at a voltage of 100 to 750 kilovolts. Coating of the film base with a coating composition to form the backing layer is performed on the surface of the film base having been provided with the magnetic coating layer on the other surface and the radiation-curing of the backing layer is performed prior to winding the tape into a roll to give a specified tensile modulus so that the magnetic recording tape is freed from the problem of the phenomenon of dropout owing to the absence of any particulate material adhering to the tape surface as is sometimes unavoidable in the conventional manufacturing process. The product tape is also quite free from scratch formation by virtue of the presence of the abrasive powder in the backing layer also contributing to the decrease of dropout.
Inventors
- 👤 Yukihiro Isobe
- 👤 Kazushi Tanaka
- 👤 Masaharu Nishimatsu
- 👤 Osamu Shinoura
- 👤 Yuichi Kubota
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:49
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/708; G11B5/7085; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/25; Y10T428/252; Y10T428/256; Y10T428/257; Y10T428/26; Y10T428/266
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
100 words
A magnetic recording medium which comprises a film base, a magnetic coating layer provided on a surface of the film base and a backing layer provided on the other surface of the film base having a tensile modulus at 100% elongation from 25 to 300 kg/cm 2 and containing an abrasive powder having a hardness of at least 4 in the Mohs scale dispersed in a matrix of a radiation-sensitive polymeric binder cured by the irradiation with a high energy radiation, the amount of abrasive powder being from 5 to 350 parts by weight per 100 parts of polymeric binder.
Claim 2
Dependent Claim
100 words
A magnetic recording medium which comprises a film base, a magnetic coating layer provided on a surface of the film base and a backing layer provided on the other surface of the film base having a tensile modulus at 100% elongation from 25 to 300 kg/cm 2 and containing an abrasive powder having a hardness of at least 4 in the Mohs scale dispersed in a matrix of a radiation-sensitive polymeric binder cured by the irradiation with a high energy radiation, the amount of abrasive powder being from 5 to 350 parts by weight per 100 parts of polymeric binder.
Claim 3
Dependent Claim
39 words
The magnetic recording medium as claimed in claim 1 wherein the abrasive powder is selected from the group consisting of silicon carbide, alumina, chromium oxide, crystalline silicon dioxide, garnet, zinc oxide, titanium dioxide, α-iron(III) oxide, boron nitride and zircon.
Claim 4
Dependent Claim
41 words
The magnetic recording medium as claimed in claim 1 wherein the radiation-sensitive polymeric binder is a thermoplastic resin modified to be radiation-sensitive or a blend of a thermoplastic resin modified to be radiation-sensitive and a thermoplastic elastomer or a prepolymer thereof.
Claim 5
Dependent Claim
22 words
The magnetic recording medium as claimed in claim 3 wherein the thermoplastic elastomer or a prepolymer thereof is modified to be radiation-sensitive.
Claim 6
Dependent Claim
33 words
The magnetic recording medium as claimed in claim 1 wherein the radiation-sensitive polymeric binder is a blend of a thermoplastic resin and a thermoplastic elastomer or a prepolymer thereof modified to be radiation-sensitive.
Claim 7
Dependent Claim
24 words
The magnetic recording medium as claimed in claim 1 wherein the baking layer has a thickness in the range from 1 to 5 μm.
Claim 8
Dependent Claim
21 words
The magnetic recording medium as claimed in claim 1 wherein the abrasive powder has a particle diameter not exceeding 4 μm.
Claim 9
Independent Claim
161 words
A method for the preparation of a magnetic recording medium comprising a film base, a backing layer provided on a surface of the film base and a magnetic coating layer provided on the other surface of the film base which comprises the steps of (a) coating a surface of the film base having been provided with a magnetic coating layer on the other surface with a coating composition comprising a radiation-sensitive polymeric binder and an abrasive powder having a hardness of at least 4 in the Mohs scale dispersed in the polymeric binder to form a coating layer the amount of abrasive powder being from 5 to 350 parts of weight per 100 parts of polymeric binder, and (b) irradiating the coating layer for the backing layer with a high energy radiation to cure the radiation-sensitive polymeric binder to such an extent that the resultant backing layer has a tensile modulus at 100% elongation from 25 to 300 kg/cm 2 .
Claim 10
Independent Claim
161 words
A method for the preparation of a magnetic recording medium comprising a film base, a backing layer provided on a surface of the film base and a magnetic coating layer provided on the other surface of the film base which comprises the steps of (a) coating a surface of the film base having been provided with a magnetic coating layer on the other surface with a coating composition comprising a radiation-sensitive polymeric binder and an abrasive powder having a hardness of at least 4 in the Mohs scale dispersed in the polymeric binder to form a coating layer the amount of abrasive powder being from 5 to 350 parts of weight per 100 parts of polymeric binder, and (b) irradiating the coating layer for the backing layer with a high energy radiation to cure the radiation-sensitive polymeric binder to such an extent that the resultant backing layer has a tensile modulus at 100% elongation from 25 to 300 kg/cm 2 .
Claim 11
Dependent Claim
37 words
The method as claimed in claim 8 wherein the abrasive powder is selected from the group consisting of silicon carbide, alumina, chromium oxide, crystalline silicon dioxide, garnet, zinc oxide, titanium dioxide, α-iron(III) oxide, boron nitride and zircon.
Claim 12
Dependent Claim
26 words
The method as claimed in claim 8 wherein the irradiation with the high energy radiation is carried out with electron beams accelerated in an electron accelerator.
Claim 13
Dependent Claim
29 words
The method as claimed in claim 10 wherein the electron beams are accelerated in the electron accelerator at an accelerating voltage in the range from 100 to 750 kilovolts.
Claim 14
Dependent Claim
42 words
The method as claimed in claim 10 wherein the irradiation with electron beams is carried out to such an extent that the radiation dose absorbed in the coating layer for the backing layer is in the range from 0.5 to 20 megarads.
Claim 15
Dependent Claim
23 words
The method as claimed in claim 8 wherein the step (b) is performed prior to winding the magnetic recording medium into a roll.
Claim 16
Dependent Claim
39 words
The method as claimed in claim 8 wherein the radiation-sensitive polymeric binder is a thermoplastic resin modified to be radiation-sensitive or a blend of a thermoplastic resin modified to be radiation-sensitive and a thermoplastic elastomer or a prepolymer thereof.
Claim 17
Dependent Claim
20 words
The method as claimed in claim 14 wherein the thermoplastic elastomer or a prepolymer thereof is modified to be radiation-sensitive.
References Cited (Backward Citations)
US3293066A
Cited
US3617378A
Cited
US3881046A
Cited
US4260466A
Cited
US4309482A
Cited
US4343831A
Cited
US4335183A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-29 | 1987-11-28 | 1988-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-29 | 1991-11-28 | 1992-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-29 | 1995-11-28 | 1996-05-29 | $7700.00 | Window Closed / Lapsed |