Process for producing a non-woven fabric
Assignee: Carl Freudenberg KG
•
Filing: 1982-10-15
•
Granted: 1984-05-29
•
Expires: 2002-10-15
Abstract
Abstract This application discloses a process for producing a non-woven fabric which comprises applying a crosslinkable bonding agent to a portion of the surface of a fiber assembly, applying heat and pressure to drive the crosslinkable bonding agent into the fiber assembly and to densify the fiber assembly and subsequently crosslink the bonding agent.
Inventors
- 👤 Tadashi Miyazaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 17:40
CPC Classifications
D; D04; D04H; D04H1/00; D04H1/40; D04H1/58; D04H1/60; D04H1/62; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1039; Y10T156/1041; Y10T156/1043; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T442/00; Y10T442/20; Y10T442/2762; Y10T442/277; Y10T442/2861; Y10T442/2893
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
152 words
A process for preparing a pliable and durable non-woven fabric comprising: a. printing a crosslinkable bonding agent in a patterned fashion onto one surface of a non-woven fiber assembly, b. applying heat and pressure to the fiber assembly sufficient to cause the bonding agent on the surface of the fiber assembly to penetrate through the fiber assembly to the surface of the fiber assembly opposite to the surface to which the bonding agent was originally applied thereby densifying portions of the fiber assembly, said heat and pressure being insufficient to crosslink the bonding agent, and c. applying heat to the fiber assembly sufficient to crosslink the bonding agent and to provide a pliable non-woven fabric having a distinct unevenness between the bonded and unbonded parts, wherein the areas of fiber assembly to which bonding agent has not been applied have a thickness about equal to the original thickness of the fiber assembly.
Claim 2
Dependent Claim
152 words
A process for preparing a pliable and durable non-woven fabric comprising: a. printing a crosslinkable bonding agent in a patterned fashion onto one surface of a non-woven fiber assembly, b. applying heat and pressure to the fiber assembly sufficient to cause the bonding agent on the surface of the fiber assembly to penetrate through the fiber assembly to the surface of the fiber assembly opposite to the surface to which the bonding agent was originally applied thereby densifying portions of the fiber assembly, said heat and pressure being insufficient to crosslink the bonding agent, and c. applying heat to the fiber assembly sufficient to crosslink the bonding agent and to provide a pliable non-woven fabric having a distinct unevenness between the bonded and unbonded parts, wherein the areas of fiber assembly to which bonding agent has not been applied have a thickness about equal to the original thickness of the fiber assembly.
Claim 3
Dependent Claim
17 words
The method according to claim 1 wherein said fiber assembly comprises a fibrous web of synthetic fibers.
Claim 4
Dependent Claim
30 words
The method according to claim 1 wherein said crosslinkable bonding agent is selected from the group consisting of self-crosslinkable acrylic ester, self-crosslinkable acetate copolymer, and self-crosslinkable SBR or NBR rubber.
Claim 5
Dependent Claim
25 words
The method according to claim 1 wherein the crosslinkable bonding agent is applied to the fiber assembly by means of a rotary screen printing machine.
Claim 6
Dependent Claim
44 words
The method according to claim 4 wherein the crosslinkable bonding agent is in the form of a paste and after application to the fiber assembly is subjected to heat sufficient to remove the moisture from said paste, but insufficient to crosslink the bonding agent.
Claim 7
Dependent Claim
56 words
The method according to claim 1 wherein the crosslinkable bonding agent is applied in the form of a paste of an emulsion of the bonding agent, to the surface of a sheet or drum, moisture is removed from said paste, and then said paste is transferred from the surface of the sheet to the fiber assembly.
Claim 8
Dependent Claim
58 words
The method according to claim 5 or claim 6 wherein said fiber assembly to which said bonding agent has been applied is subjected to heat of about 150° to about 250° C. and a pressure of less than about 50 kg/cm 2 , to drive said bonding agent into said fiber assembly and to densify the fiber assembly.
Claim 9
Dependent Claim
17 words
The method according to claim 3 wherein the fiber assembly is comprised of polyethylene or rayon fibers.
Claim 10
Independent Claim
34 words
The method according to claims 5 or 6 wherein the crosslinkable bonding agent is applied to about 15% of the surface of the fiber assembly, and comprised a paste of self-crosslinkable acrylic ester emulsion.
Claim 11
Dependent Claim
97 words
The method according to claim 6 wherein a paste of a self-crosslinkable acrylic ester emulsion having a viscosity of about 15,000 cps is printed onto about a 30 to about a 70 g/m 2 assembly of polyester fibers of about 1 to 1.5 denier and about 38 to about 51 mm cut, such that the paste covers about 15% of the surface of the fiber assembly and has a dry weight of about 13 g/m 2 to about 30 g/m 2 , said fiber assembly having been compacted by hot-rolling prior to the application of said paste.
Claim 12
Dependent Claim
27 words
The method according to claim 10 further comprising the step of buffing the surface of the product of said process to provide a hairy structure and appearance.
Claim 13
Dependent Claim
15 words
The method according to claim 6 wherein the sheet comprises a silicone rubber conveyor belt.
Claim 14
Dependent Claim
43 words
The method according to claim 12 wherein the fiber assembly is comprised of about a 70 g/m 2 assembly of rayon fibers, and the crosslinkable bonding agent comprises a paste of a self-crosslinking acrylic ester emulsion which is printed onto the conveyor belt.
Claim 15
Dependent Claim
53 words
The process according to claim 1 wherein the bonding agent is caused to penetrate the fiber assembly by passing the bonding agent treated fiber assembly through calender rollers which apply a pressure of 50 Kg/cm 3 or less and a temperature of about 150° C. to about 250° C. to the fiber assembly.
Claim 16
Dependent Claim
40 words
The process according to claim 1 further comprising the step of compressing the fiber assembly prior to the application of the crosslinkable bonding agent, and then printing the bonding agent onto said portions of the surface of the fiber assembly.
Claim 17
Dependent Claim
15 words
The process according to claim 1 wherein the fiber assembly is comprised of polyester fibers.
Claim 18
Dependent Claim
16 words
The process according to claim 16 wherein the bonding agent comprises a self-crosslinking acrylic ester emulsion.
Claim 19
Dependent Claim
16 words
The process according to claim 1 wherein the bonding agent comprises a self-crosslinking acrylic ester emulsion.
References Cited (Backward Citations)
US4170680A
Cited
US4119746A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-29 | 1987-11-28 | 1988-05-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-29 | 1991-11-28 | 1992-05-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-29 | 1995-11-28 | 1996-05-29 | $7700.00 | Window Closed / Lapsed |