US4449134A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Composite ink jet drivers
Assignee: Xerox Corp
•
Filing: 1982-04-19
•
Granted: 1984-05-15
•
Expires: 2002-04-19
Abstract
Abstract An ink jet droplet exciter for generating pressure waves in a droplet generator. The preferred exciter is a composite made of PZT, Pb (Zr:Ti) O 3 , and a polyethylene supporting material. The mean diameter of the PZT particles is 7 mils and the entire exciter thickness is between 10 and 12 mils. The composite is pliable and can be made in sheets of a large enough area to provide droplet excitation for a multiple nozzle generator.
Inventors
- 👤 Doyle P. Skinner, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 18:37
CPC Classifications
B; B41; B41J; B41J2/00; B41J2/005; B41J2/01; B41J2/015; B41J2/02; B41J2/03; B41J2202/00; B41J2202/01; B41J2202/03; Y; Y10; Y10S; Y10S310/00; Y10S310/80; Y10T; Y10T29/00; Y10T29/42
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
184 words
A method of fabricating a composite ink jet drive member comprising the steps of: forming a planar base layer of polymeric material; applying a first, substantially uniformly thick layer of discrete particles of piezoelectric ceramic material to said base layer; covering said first layer of ceramic particles with a second planar layer of polymeric material to form a sandwich of ceramic particles between layers of polymeric material; exerting a pressure on said sandwich of ceramic particles at an elevated temperature to form a composite drive member having two outer surfaces, so that said layers of polymeric material are squeezed towards each other to fill interstices between said ceramic particles while concurrently causing the ceramic particles to be continuously connected throughout the thickness of the composite drive member in the direction that the pressure is applied, said ceramic particles adjacent the outer surfaces of the composite drive member having surface portions which extend through the polymeric material for electrical contact at the outer surfaces of the composite drive member; and poling said composite drive member with an electric field to cause a piezoelectric response therefrom.
Claim 2
Independent Claim
184 words
A method of fabricating a composite ink jet drive member comprising the steps of: forming a planar base layer of polymeric material; applying a first, substantially uniformly thick layer of discrete particles of piezoelectric ceramic material to said base layer; covering said first layer of ceramic particles with a second planar layer of polymeric material to form a sandwich of ceramic particles between layers of polymeric material; exerting a pressure on said sandwich of ceramic particles at an elevated temperature to form a composite drive member having two outer surfaces, so that said layers of polymeric material are squeezed towards each other to fill interstices between said ceramic particles while concurrently causing the ceramic particles to be continuously connected throughout the thickness of the composite drive member in the direction that the pressure is applied, said ceramic particles adjacent the outer surfaces of the composite drive member having surface portions which extend through the polymeric material for electrical contact at the outer surfaces of the composite drive member; and poling said composite drive member with an electric field to cause a piezoelectric response therefrom.
Claim 3
Dependent Claim
43 words
The method of claim 1, which further comprises the steps of: bonding by hot pressing the composite drive member directly to a back mounting plate of an ink droplet generator, so that the need for an adhesive or other attaching means is avoided.
Claim 4
Dependent Claim
71 words
The method of claim 1 which further comprises the steps of: applying a second, substantially uniformly thick layer of said ceramic particles to said second planar layer of polymeric material; and covering said second layer of ceramic particles with a third planar layer of polymeric material to from a sandwich having two layers ceramic particles between three layers of polymeric material prior to exerting the pressure step at an elevated temperature.
Claim 5
Dependent Claim
96 words
The method of claim 3, wherein the ceramic particles are PZT and have an average diameter of 7 mils; wherein the planar layer of polymeric material are 3.6 mil thick polyethylene sheets; wherein the pressure exerted is about 1500 pounds per square inch and the elevated temperature is 170° celsius; wherein the portion of ceramic particles in the composite drive member is greater than 35% by volume; and wherein the method further comprises the step of: abrading the outer surfaces of the composite drive member, so that the thickness thereof is between 10 and 12 mils.
Claim 6
Dependent Claim
87 words
The method of claim 1, wherein the ceramic particles are PZT and have an average diameter greater than the desired thickness of the composite drive member; wherein the planar layer of polymeric material is 3.6 mil thick polyethylene sheets; and wherein the method further comprises the steps of: abrading the composite drive member to the desired thickness, so that the PZT particles extend across the entire thickness dimension of the composite drive member which enables the use of smaller electric poling fields to achieve piezoelectric response therefrom.
Claim 7
Independent Claim
116 words
A method for fabricating a composite ink jet droplet drive member comprising the steps of: mixing particles of a ceramic piezoelectric material with a polymeric powder to form a combination having a range of percentage by volume of ceramic material of between 30 and 50 percent; pressing the combination at an elevated temperature to melt the powder and to form a composite film, so that the ceramic particles are continuously connected across the entire thickness of the film and surface portions of the ceramic particles are exposed at the surfaces of the composite film; and poling said film to cause said film to respond as a piezoelectric composite drive member when energized with an electric field.
Claim 8
Independent Claim
116 words
A method for fabricating a composite ink jet droplet drive member comprising the steps of: mixing particles of a ceramic piezoelectric material with a polymeric powder to form a combination having a range of percentage by volume of ceramic material of between 30 and 50 percent; pressing the combination at an elevated temperature to melt the powder and to form a composite film, so that the ceramic particles are continuously connected across the entire thickness of the film and surface portions of the ceramic particles are exposed at the surfaces of the composite film; and poling said film to cause said film to respond as a piezoelectric composite drive member when energized with an electric field.
Claim 9
Dependent Claim
41 words
The method of claim 6, wherein the ceramic particles are PZT and have an average diameter of 1.5 microns; wherein the polymeric powder is polyethylene; wherein the film thickness is 10 mils; and wherein the film contains 45% PZT by volume.
Claim 10
Dependent Claim
35 words
The method of claim 6, wherein the ceramic particles are PZT and have an average diameter of 7 mils; wherein the polymeric powder is polyethylene; and wherein film thickness is between 10 and 12 mils.
References Cited (Backward Citations)
US2420864A
Cited
US3940637A
Cited
US4227111A
Cited
US4282532A
Cited
US4296417A
Cited
US4405402A
Cited
US4407054A
Cited
US4330593A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-15 | 1987-11-14 | 1988-05-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-15 | 1991-11-14 | 1992-05-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-15 | 1995-11-14 | 1996-05-15 | $7700.00 | Window Closed / Lapsed |