Porous ceramic body and a method of manufacturing the same
Assignee: Denso Corp
•
Filing: 1982-06-15
•
Granted: 1984-05-15
•
Expires: 2002-06-15
Abstract
Abstract A method of manufacturing a porous ceramic body useful for a catalyst carrier or a filter which comprises preparing a ceramic honeycomb structure having passages, filling a ceramic slurry mixed with organic solids into the passages and then baking the whole ceramic body to gasify the organic solids thereby producing fine meandering holes in the passages. A porous ceramic body produced by such a method is also proposed.
Inventors
- 👤 Shunzo Yamaguchi
- 👤 Yukihisa Takeuchi
- 👤 Yasunao Miura
- 👤 Naoto Miwa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 12:14
CPC Classifications
B; B01; B01D; B01D46/00; B01D46/24; B01D46/2403; B01D46/2407; B01J; B01J35/00; B01J35/50; B01J35/56; B01J35/57; C; C04; C04B; C04B38/00; C04B38/0006; F; F01; F01N; F01N3/00; F01N3/08; F01N3/10; F01N3/24; F01N3/28; F01N3/2803; F01N3/2825; F01N3/2828; F01N2330/00; F01N2330/06; F02; F02B; F02B1/00; F02B1/02; F02B1/04; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24149; Y10T428/24744
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
106 words
A porous ceramic body which comprises: a ceramic honeycomb structure provided with a large number of passages 0.5 mm to 10 mm in inner diameter; and adhered to the walls of said honeycomb structure a ceramic layer penetrated by fine meandering holes 0.1 mm to 0.5 mm in diameter or width which holes are produced first by filling the passages of the ceramic honeycomb structure with a ceramic slurry formed of a mixture of organic solids 0.05 mm to 0.5 mm in diameter or length, and then firing an integral mass of said ceramic honeycomb structure and ceramic slurry to decompose and scatter the organic solids.
Claim 2
Dependent Claim
106 words
A porous ceramic body which comprises: a ceramic honeycomb structure provided with a large number of passages 0.5 mm to 10 mm in inner diameter; and adhered to the walls of said honeycomb structure a ceramic layer penetrated by fine meandering holes 0.1 mm to 0.5 mm in diameter or width which holes are produced first by filling the passages of the ceramic honeycomb structure with a ceramic slurry formed of a mixture of organic solids 0.05 mm to 0.5 mm in diameter or length, and then firing an integral mass of said ceramic honeycomb structure and ceramic slurry to decompose and scatter the organic solids.
Claim 3
Dependent Claim
29 words
The porous ceramic body according to claim 1, wherein the ceramic slurry further contains lumpy aggregate particles having a diameter ranging from about 0.3 mm to about 3 mm.
Claim 4
Dependent Claim
11 words
A filter made of the porous ceramic body of claim 1.
Claim 5
Dependent Claim
12 words
A catalyst carrier made of the porous ceramic body of claim 1.
Claim 6
Dependent Claim
114 words
A porous ceramic body adapted for the passage of a fluid therethrough which comprises: a honeycomb structure made of a first ceramic material having a plurality of substantially smooth parallel walls defining parallel passages therethrough, each of said passages having an inner diameter of about 0.5 mm to about 10 mm; a layer of second ceramic adhered to and retained in the inside of each of the parallel walls of said honeycomb, said ceramic layer defining in the direction of said parallel walls a tortuous passageway consisting of a multitude of fine meandering holes from about 0.1 mm to about 0.5 mm in diameter or width, said passageway penetrating through the porous ceramic body.
Claim 7
Dependent Claim
114 words
A porous ceramic body adapted for the passage of a fluid therethrough which comprises: a honeycomb structure made of a first ceramic material having a plurality of substantially smooth parallel walls defining parallel passages therethrough, each of said passages having an inner diameter of about 0.5 mm to about 10 mm; a layer of second ceramic adhered to and retained in the inside of each of the parallel walls of said honeycomb, said ceramic layer defining in the direction of said parallel walls a tortuous passageway consisting of a multitude of fine meandering holes from about 0.1 mm to about 0.5 mm in diameter or width, said passageway penetrating through the porous ceramic body.
Claim 8
Dependent Claim
24 words
The porous ceramic body according to claim 5 in which the layer of second ceramic material also includes a plurality of independent air cells.
Claim 9
Dependent Claim
28 words
The porous ceramic body according to claim 5 in which the second ceramic material contains lumpy aggregate particles having a diameter from about 0.3 to about 3 mm.
Claim 10
Dependent Claim
11 words
A filter made of the porous ceramic body of claim 5.
Claim 11
Dependent Claim
12 words
A catalyst carrier made of the porous ceramic body of claim 5.
References Cited (Backward Citations)
US3904551A
Cited
US4253992A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-15 | 1987-11-14 | 1988-05-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-15 | 1991-11-14 | 1992-05-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-15 | 1995-11-14 | 1996-05-15 | $7700.00 | Window Closed / Lapsed |