Preparation of cord for bonding to rubber

Claim 2

A one-step dip for coating a cord or fabric made from adhesive-activated polyester, or aramid, comprising, an aqueous dispersion containing (a) an adhesive latex of a diene polymer, (b) an acrylic resin selected from the group consisting of poly[(meth)acrylic acids], poly[N-methylol (meth)acrylamides], and a copolymer of one or more monomers of the foregoing homopolymers with a lower (meth)acrylic acid ester, having the structure ##STR3## wherein, R represents H, methyl, ethyl, Cl or CN, and, X represents hydroxyl (OH), hydroxymethylamino (NHCH 2 OH), or alkoxy (O-alkyl) having from 1 to 4 carbon atoms, and, (c) a reversibly blocked polyisocyanate formed by reversibly blocking a polyisocyanate with a blocking agent capable of an addition reaction with it, wherein resorcinol formaldehyde solids in said adhesive latex and said acrylic resin are present in a ratio in the range from about 0.5:1 to about 5:1, and the ratio of resorcinol formaldehyde solids to reversibly blocked polyisocyanate is in the range from about 9:1 to about 1:3.

Claim 3

The one-step dip of claim 1 wherein, said latex is in substantial part a dispersion of a polymer made predominantly from butadiene and to a minor extent, from styrene and vinyl pyridine, said acrylic resin is at least partially soluble in water, said resin having a molecular weight in the range from about 3,000 to about 300,000, and, said reversibly blocked polyisocyanate is an aromatic polyisocyanate which is unblocked at a temperature above about 300° F. but below that which is deleterious to the tensile stength of said cord or fabric.

Claim 4

The one-step dip of claim 2 wherein said acrylic resin is selected from the group consisting of a a homopolymer selected from the group consisting of polyacrylic acid, polymethacrylic acid, poly(N-methylol acrylamide), poly(N-methylol methacrylamide), and a copolymer made from methyl methacrylate, acrylic or methacrylic acid, and N-methylol acrylamide.

Claim 5

The one-step dip of claim 2 wherein said blocking agent is a phenol or amide.

Claim 6

The one-step dip of claim 3 wherein said acrylic resin is a copolymer made predominantly from methyl methacrylate, to a minor extent from acrylic or methacrylic acid, and to an extent at least equivalent to that of the acid, from N-methylol acrylamide.

Claim 7

The one-step dip of claim 4 wherein, said aromatic polyisocyanate is selected from the group consisting of triphenyl methane-triisocyanate, 2,4-toluene-diisocyanate, and methylene-bis-(4-phenylisocyanate, said phenol blocking agent is a monohydroxy benzene selected from the group consisting of o-chlorophenol, p-chlorophenol, o-bromophenol, p-bromophenol, o-cresol, p-cresol, 3,4-dichlorophenol, p-tertiary butyl phenol, and 2,5-dimethyl phenol, and, said amide is a lactam selected from the group consisting of 2-pyrrolidone, 2-piperidone, and caprolactam.

Claim 8

A one-step process for dipping cord or fabric to coat it with an adhesive from a bath prior to drying and heat-setting the adhesive, comprising, (a) a one-step process for dipping the cord or fabric made from adhesive-activated polyester or aramid in said bath comprising an aqueous dispersion containing an adhesive latex of a diene polymer, an acrylic resin selected from the group consisting of poly[(meth)acrylic acids], poly[N-methylol (meth)acrylamides], and a copolymer of one or more monomers of the foregoing homopolymers with a lower (meth)acrylic acid ester, having the structure ##STR4## wherein, R represents H, methyl, ethyl, Cl or CN, and, X represents hydroxyl (OH), hydroxymethylamino (NHCH 2 OH), or alkoxy (O-alkyl) having from 1 to 4 carbon atoms, and, a reversibly blocked polyisocyanate formed by reversibly blocking a polyisocyanate with a blocking agent capable of an addition reaction with said polyisocyanate, wherein resorcinol formaldehyde solids in said adhesive latex and said acrylic resin are present in a ratio in the range from about 0.5:1 to about 5:1, and the ratio of resorcinol formaldehyde solids to reversibly blocked polyisocyanate is in the range from about 9:1 to about 1:3, (b) drying the cord at a temperature in the range from about 200° F. to about 350° F. under tension, and thereafter (c) heat-setting the coated cord or fabric at a temperature in the range from about 350° F. but below that which is deleterious to the tensile strength of the cord or fabric.

Claim 9

A one-step process for dipping cord or fabric to coat it with an adhesive from a bath prior to drying and heat-setting the adhesive, comprising, (a) a one-step process for dipping the cord or fabric made from adhesive-activated polyester or aramid in said bath comprising an aqueous dispersion containing an adhesive latex of a diene polymer, an acrylic resin selected from the group consisting of poly[(meth)acrylic acids], poly[N-methylol (meth)acrylamides], and a copolymer of one or more monomers of the foregoing homopolymers with a lower (meth)acrylic acid ester, having the structure ##STR4## wherein, R represents H, methyl, ethyl, Cl or CN, and, X represents hydroxyl (OH), hydroxymethylamino (NHCH 2 OH), or alkoxy (O-alkyl) having from 1 to 4 carbon atoms, and, a reversibly blocked polyisocyanate formed by reversibly blocking a polyisocyanate with a blocking agent capable of an addition reaction with said polyisocyanate, wherein resorcinol formaldehyde solids in said adhesive latex and said acrylic resin are present in a ratio in the range from about 0.5:1 to about 5:1, and the ratio of resorcinol formaldehyde solids to reversibly blocked polyisocyanate is in the range from about 9:1 to about 1:3, (b) drying the cord at a temperature in the range from about 200° F. to about 350° F. under tension, and thereafter (c) heat-setting the coated cord or fabric at a temperature in the range from about 350° F. but below that which is deleterious to the tensile strength of the cord or fabric.

Claim 10

The one-step process of claim 7 wherein, said latex is in substantial part a dispersion of a polymer made predominantly from butadiene and to a minor extent, from styrene and vinyl pyridine, said acrylic resin is at least partially soluble in water, said resin having a molecular weight in the range from about 3,000 to about 300,000, and, said reversibly blocked polyisocyanate is an aromatic polyisocyanate which is unblocked at a temperature above about 300° F. but below that which is deleterious to the tensile strength of said cord or fabric.

Claim 11

The one-step process of claim 7 wherein said acrylic resin is selected from the group consisting of a a homopolymer selected from the group consisting of polyacrylic acid, polymethacrylic acid, poly(N-methylol acrylamide), poly(N-methylol methacrylamide), and a copolymer made from methyl methacrylate, acrylic or methacrylic acid, and N-methylol acrylamide.

Claim 12

The one-step process of claim 9 wherein said blocking agent is a phenol or amide.

Claim 13

The one-step process of claim 9 wherein said acrylic resin is a copolymer made predominantly from methyl methacrylate, to a minor extent from acrylic or methacrylic acid, and to an extent at least equivalent to that of the acid, from N-methylol acrylamide.

Claim 14

The one-step process of claim 10 wherein, said aromatic polyisocyanate is selected from the group consisting of triphenyl methane-triisocyanate, 2,4-toluene-diisocyanate, and methylene-bis-(4-phenylisocyanate), said phenol blocking agent is a monohydroxy benzene selected from the group consisting of o-chlorophenol, p-chlorophenol, o-bromophenol, p-bromophenol, o-cresol, p-cresol, 3,4-dichlorophenol, p-tertiary butyl phenol, and 2,5-dimethyl phenol, and, said amide is a lactam selected from the group consisting of 2-pyrrolidone, 2-piperidone, and caprolactam.

Claim 15

The process of claim 11 wherein the pick-up of resorcinol formaldehyde latex together with reversibly blocked polyisocyanate is in the range from about 0.5 to about 20% by weight on a solids basis.