US4448738A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing foamed plastic articles
Assignee: Geon Co
•
Filing: 1982-03-15
•
Granted: 1984-05-15
•
Expires: 2002-03-15
Abstract
Abstract An improvement is disclosed in a process for producing foamed articles of thermo-plastic or thermo-setting compounds. The improvement reduces the number of steps normally followed to make a foamed product and cuts down on the time. The improvement comprises the steps of intensively mixing and thermokinetically heating a batch of the compounds with a foaming agent having a preselected trigger temperature to initiate gas evolution, the mixing and heating occurring in an enclosed mixing chamber with a plurality of blades attached to arms rotating about an axis, with a blade tip speed of at least about 18 meters per second, mixing until the compounds and the foaming agent are heated above the trigger temperature of the foaming agent to a mixture having a predetermined discharge temperature representing a state of flux of the compounds suitable for forming and the mixture having a viscosity sufficient to contain gas evolved from the foaming agent, discharging the batch from the chamber when the batch reaches the predetermined temperature, and feeding the mixture from the discharged batch to a forming unit while foaming is still occurring.
Inventors
- 👤 Zenas Crocker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 05:14
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/34; B29C44/36; B29C44/46; B29C44/461; B01; B01F; B01F35/00; B01F35/20; B01F35/22; B01F35/221; B01F35/2214; B01F35/22142; B01F35/221421; B01F35/2215; B29B; B29B7/00; B29B7/002; B29B7/005; B29B7/02; B29B7/06; B29B7/10; B29B7/12; B29B7/16; B29B7/74; B29B7/7404; B29B7/7409; B29B7/7414; B29B7/80; B29B7/82; C; C08; C08J; C08J9/00; C08J9/04; C08J9/06; C08J9/10; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2023/0608; B29K2023/0633; B29K2027/00; B29K2027/06; B29K2105/00; B29K2105/04; C08J2323/00; C08J2323/02; C08J2323/04; C08J2323/06; C08J2327/00; C08J2327/02; C08J2327/04; C08J2327/06; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10S264/60
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
215 words
A method of making a molded foamed thermoplastic article from a particulate thermoplastic resin comprising: intensively mixing and thermokenetically heating a particulate composition comprising thermoplastic resin particles and a foaming agent, said foaming agent having a trigger temperature at which a gas is evolved therefrom to effect foaming, said mixing and heating being effected by mixing said particulate composition in an enclosed mixing chamber with a plurality of blades attached to arms rotating within said chamber with a blade tip speed of at least about 18 meters per second; continuing said mixing of said particulate composition in said enclosed chamber until said particulate composition is heated to a mixing temperature at or above said trigger temperature of said foaming agent, said mixing temperature being sufficient to effect fluxing of said particulate composition to an extent such that the fluxed composition has a viscosity sufficient to contain gas evolved from said foaming agent; discharging the fluxed composition from said mixing chamber when the fluxed composition is at said mixing temperature and when said foaming agent is just beginning to foam; and feeding the discharged fluxed composition to a mold and confining the composition within said mold to mold the composition while foaming of said composition continues, to form a molded foamed plastic article in said mold.
Claim 2
Independent Claim
215 words
A method of making a molded foamed thermoplastic article from a particulate thermoplastic resin comprising: intensively mixing and thermokenetically heating a particulate composition comprising thermoplastic resin particles and a foaming agent, said foaming agent having a trigger temperature at which a gas is evolved therefrom to effect foaming, said mixing and heating being effected by mixing said particulate composition in an enclosed mixing chamber with a plurality of blades attached to arms rotating within said chamber with a blade tip speed of at least about 18 meters per second; continuing said mixing of said particulate composition in said enclosed chamber until said particulate composition is heated to a mixing temperature at or above said trigger temperature of said foaming agent, said mixing temperature being sufficient to effect fluxing of said particulate composition to an extent such that the fluxed composition has a viscosity sufficient to contain gas evolved from said foaming agent; discharging the fluxed composition from said mixing chamber when the fluxed composition is at said mixing temperature and when said foaming agent is just beginning to foam; and feeding the discharged fluxed composition to a mold and confining the composition within said mold to mold the composition while foaming of said composition continues, to form a molded foamed plastic article in said mold.
Claim 3
Dependent Claim
24 words
A method according to claim 1 wherein said foaming agent and said resin particles are introduced into said mixing chamber at the same time.
Claim 4
Dependent Claim
25 words
A method according to claim 1 wherein said foaming agent is present in an amount of about 0.5 to 1.2% by weight of the composition.
Claim 5
Dependent Claim
25 words
A method according to claim 1 wherein said resin particles comprise a resin selected from the group consisting of polyvinyl chloride and low density polyethylene.
Claim 6
Dependent Claim
17 words
A method according to claim 4 wherein said blade tip speed is about 31-38 meters per second.
Claim 7
Dependent Claim
21 words
A method according to claim 4 wherein said foaming agent is selected from the group consisting of azodicarbonamide and para-oxybis (benzenesulfonylhydrazide).
Claim 8
Dependent Claim
16 words
A method according to claim 5 wherein said mixing temperature is about 190° to 240° C.
Claim 9
Dependent Claim
19 words
A method according to claim 7 wherein said mixing and heating is effected for about 7 to 20 seconds.
Claim 10
Dependent Claim
25 words
A method according to claim 1 wherein said composition is confined within said mold under a pressure of 80 to 320 lbs. per square inch.
Claim 11
Dependent Claim
23 words
A method according to claim 9 wherein said composition is confined within said mold under said pressure for not more than 5 minutes.
Claim 12
Dependent Claim
23 words
A method according to claim 1 wherein said foaming agent is introduced into said mixing chamber after said resin particles are introduced therein.
References Cited (Backward Citations)
US2525965A
Cited
US2654913A
Cited
US2806255A
Cited
US3037474A
Cited
US3266738A
Cited
US3564602A
Cited
GB1320982A
Cited
GB1241409A
Cited
US4059661A
Cited
US4142804A
Cited
US4230615A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-15 | 1987-11-14 | 1988-05-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-15 | 1991-11-14 | 1992-05-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-15 | 1995-11-14 | 1996-05-15 | $7700.00 | Window Closed / Lapsed |