Para-selective alkylation catalysts and processes

Claim 3

A method according to claim 1 wherein said contacting of base catalyst composite occurs in a single stage operation without intermediate calcination of said composite.

Claim 4

A method according to claim 1 wherein said siliceous crystalline zeolite is selected from the group consisting of ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35, ZSM-38 and ZSM-48.

Claim 5

A method according to claim 3 wherein said zeolite crystal major dimension ranges from about 2 to 4 microns and said zeolite crystal minor dimension ranges from about 0.5 to 2 microns.

Claim 6

A method according to claim 3 wherein said aqueous solution of magnesium nitrate used to contact said base catalyst composite comprises Mg(NO 3 ) 2 .6H 2 O present to the extent of from about 40% to 65% by weight of solution.

Claim 7

A method according to claim 5 wherein contact of magnesium nitrate solution with base catalyst composite occurs for a period of at least about 0.5 hour at a temperature of from about 10° C. to 65° C.

Claim 8

A method according to claim 5 wherein said crystalline zeolite is ZSM-5.

Claim 9

A method according to claim 3 wherein calcination occurs at a temperature of from about 510° C. to 540° C. for a period of from about 1 to 6 hours.

Claim 10

A method according to claim 3 wherein: (a) the magnesium nitrate content of said magnesium nitrate solution ranges from about 60% to 65% by weight of solution; (b) the calcined aromatics alkylation catalyst composition comprises from about 6% to 7% by weight of magnesium.

Claim 11

A substantially phosphorus-free, magnesium-containing, zeolite-based, aromatics alkylation catalyst composition prepared in accordance with the method of claim 1.

Claim 12

A substantially phosphorus-free, magnesium-containing, zeolite-based, aromatics alkylation catalyst composition prepared in accordance with the method of claim 7.

Claim 13

A process for the alkylation of monoalkyl substituted compounds to produce a dialkyl-substituted benzene compound mixture enriched in the para-dialkylbenzene isomer, said process comprising contacting a monoalkyl substituted aromatic compound with an alkylating agent under aromatic alkylation conditions in the presence of a substantially phosphorus-free, magnesium-containing, zeolite-based alkylation catalyst composition made by (a) preparing a base catalyst composite comprising from about 25% to 80% by weight of a siliceous crystalline zeolite material characterized by a silica to alumina mole ratio of at least about 12, a Constraint Index within the approximate range of from about 1 to 12, a zeolite crystal major dimension of from about 1 to 10 microns, and a zeolite crystal minor dimension of from about 0.2 to 4 microns; said composite further comprising from about 20% to 75% by weight of an inorganic oxide binder; (b) contacting said base catalyst composite with an aqueous solution of magnesium nitrate under contacting conditions, and for a period of time, sufficient to incorporate magnesium nitrate onto said base catalyst composite; said contact of catalyst composite with said magnesium nitrate solution occurring without either prior or subsequent contact of said composite with solutions of phosphorus compounds; and (c) calcining said magnesium nitrate-treated catalyst composite in a nitrogen-containing or oxygen-containing atmosphere at a temperature of from about 200° C. to 565° C. for a period of time sufficient to form said aromatics alkylation catalyst composition which contains from about 4% to 8% by weight of magnesium present at least in part as magnesium oxide.

Claim 14

A process for the alkylation of monoalkyl substituted compounds to produce a dialkyl-substituted benzene compound mixture enriched in the para-dialkylbenzene isomer, said process comprising contacting a monoalkyl substituted aromatic compound with an alkylating agent under aromatic alkylation conditions in the presence of a substantially phosphorus-free, magnesium-containing, zeolite-based alkylation catalyst composition made by (a) preparing a base catalyst composite comprising from about 25% to 80% by weight of a siliceous crystalline zeolite material characterized by a silica to alumina mole ratio of at least about 12, a Constraint Index within the approximate range of from about 1 to 12, a zeolite crystal major dimension of from about 1 to 10 microns, and a zeolite crystal minor dimension of from about 0.2 to 4 microns; said composite further comprising from about 20% to 75% by weight of an inorganic oxide binder; (b) contacting said base catalyst composite with an aqueous solution of magnesium nitrate under contacting conditions, and for a period of time, sufficient to incorporate magnesium nitrate onto said base catalyst composite; said contact of catalyst composite with said magnesium nitrate solution occurring without either prior or subsequent contact of said composite with solutions of phosphorus compounds; and (c) calcining said magnesium nitrate-treated catalyst composite in a nitrogen-containing or oxygen-containing atmosphere at a temperature of from about 200° C. to 565° C. for a period of time sufficient to form said aromatics alkylation catalyst composition which contains from about 4% to 8% by weight of magnesium present at least in part as magnesium oxide.

Claim 15

An alkylation process according to claim 12 wherein said alkylation conditions include a reaction temperature of between about 300° C. and 650° C., a molar ratio of alkylating agent to aromatic compound of from about 0.05 to 2 and a weight hourly space velocity of reactant feed of from about 1 to 50.

Claim 16

An alkylation process according to claim 13 wherein said aromatic compound is selected from toluene and ethylbenzene and said alkylating agent contains from 1 to about 16 carbon atoms and is selected from olefins, alkyl halides and alkanols.

Claim 17

An alkylation process according to claim 14 wherein said aromatic compound is toluene and said alkylating agent is ethylene.

Claim 18

An alkylation process according to claim 15 wherein said siliceous crystalline zeolite material is ZSM-5.