Room temperature vulcanizable polyorganosiloxane compositions which are paintable following curing
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1983-06-07
•
Granted: 1984-05-08
•
Expires: 2003-06-07
Abstract
Abstract Paintable, cured polyorganosiloxane sealants are prepared at room temperature from room temperature curable compositions containing a hydroxyl-terminated polyorganosiloxane, an organosilicon compound containing at least two amido groups, aminoxy groups or combinations thereof, per molecule and a substituted alcohol where the substituent is acyloxy, alkoxycarbonyl, cyano, <IMAGE> mercapto, or the combination of a carbon-to-carbon triple bond and an ether-type oxygen atom, where each Y and Z are individually selected from the group consisting of hydrogen, hydrocarbyl and halohydrocarbyl.
Inventors
- 👤 Miyoji Fukayama
- 👤 Chikara Ichiijo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 07:36
CPC Classifications
C; C08; C08K; C08K5/00; C08K5/04; C08K5/10; C08K5/101; C08K5/0008; C08K5/05; C08K5/06; C08K5/16; C08K5/17; C08K5/20; C08K5/36; C08K5/37; C08K5/54
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
116 words
A room temperature vulcanizable polyorganosiloxane composition comprising (A) 100 parts by weight of a hydroxyl-terminated polyorganosiloxane exhibiting a viscosity of from 0.02 to 1000 Pa.s at 25° C.; (B) from 0.5 to 30 parts by weight of at least one organosilicon compound containing at least two functional groups selected from the group consisting of amido and aminoxy; and (C) from 0.01 to 15 parts by weight of an alcohol containing a substituent selected from the group consisting of acyloxy, alkoxycarbonyl, carboxy, cyano, ##STR37## mercapto, and the combination of a carbon-to-carbon triple bond and at least one ether-type oxygen atom, where each Y and Z are individually selected from the group consisting of hydrogen, hydrocarbyl, and halohydrocarbyl.
Claim 2
Dependent Claim
116 words
A room temperature vulcanizable polyorganosiloxane composition comprising (A) 100 parts by weight of a hydroxyl-terminated polyorganosiloxane exhibiting a viscosity of from 0.02 to 1000 Pa.s at 25° C.; (B) from 0.5 to 30 parts by weight of at least one organosilicon compound containing at least two functional groups selected from the group consisting of amido and aminoxy; and (C) from 0.01 to 15 parts by weight of an alcohol containing a substituent selected from the group consisting of acyloxy, alkoxycarbonyl, carboxy, cyano, ##STR37## mercapto, and the combination of a carbon-to-carbon triple bond and at least one ether-type oxygen atom, where each Y and Z are individually selected from the group consisting of hydrogen, hydrocarbyl, and halohydrocarbyl.
Claim 3
Dependent Claim
12 words
The composition of claim 1 where said alcohol is monohydric or dihydric.
Claim 4
Dependent Claim
82 words
The composition of claim 2 where said alcohol contains a ##STR38## radical or a ##STR39## radical and an ether-type oxygen atom, where R 1 represents methyl, ethyl or isobutyl, R 2 represents methyl or ethyl and said oxygen atom is bonded to the ##STR40## radical and either a hydroxyalkyl radical or a hydroxyl-terminated polyoxyalkylene radical, where the alkylene portion of said polyoxyalkylene radical is ethylene, propylene or a combination thereof and the alkyl portion of said hydroxyalkyl radical is ethyl or propyl.
Claim 5
Dependent Claim
76 words
The composition of claim 1 where said alcohol is represented by a general formula selected from the group consisting of ##STR41## where R 3 represents a monovalent hydrocarbon radical or a monovalent halohydrocarbon radical where the halogen is chlorine, bromine, or fluorine, R 4 represents a bivalent hydrocarbon radical or a bivalent halohydrocarbon radical, R 5 and R 6 are individually selected from the group consisting of hydrogen atoms, monovalent hydrocarbon radicals, and monovalent halohydrocarbon radicals.
Claim 6
Dependent Claim
16 words
The composition of claim 1 wherein said alcohol is selected from the group consisting of ##STR42##
Claim 7
Dependent Claim
26 words
The composition of claim 1 where the concentration of said alcohol is from 0.05 to 5 parts by weight per 100 parts of said hydroxyl-terminated polyorganosiloxane.
Claim 8
Dependent Claim
49 words
The composition of claim 1 where component (B) is a silane, a linear siloxane or a cyclosiloxane and contains at least two amido or aminoxy groups per molecule that are bonded to silicon through the nitrogen atom of the amido group or the oxygen atom of the aminoxy group.
Claim 9
Dependent Claim
27 words
The composition of claim 1 where component (B) is a mixture of organosilicon compounds containing an average of more than two amido or aminoxy groups per molecule.
Claim 10
Dependent Claim
22 words
The composition of claim 8 where component (B) is a mixture of ##STR43## a mixture of ##STR44## or a mixture of ##STR45##
Claim 11
Dependent Claim
26 words
The composition of claim 1 where the concentration of component (B) is from 1 to 20 parts by weight per 100 parts of hydroxyl-terminated polyorganosiloxane (A).
Claim 12
Dependent Claim
68 words
The composition of claim 1 where the hydroxyl-terminated polyorganosiloxane is a α,ω-dihydroxypolydiorganosiloxane of the general formula HO--R 2 7 SiO-- n H where each R 7 is individually selected from the group consisting of hydrocarbyl, halohydrocarbyl and cyanohydrocarbyl radicals and substituted monovalent hydrocarbon radicals and the value of n represents an average degree of polymerization equivalent to a viscosity of from 0.02 to 1000 Pa.s at 25° C.
Claim 13
Dependent Claim
27 words
The composition of claim 11 where R 7 is selected from the group consisting of methyl, ethyl, propyl, octyl, vinyl, allyl, phenyl, tolyl, chloromethyl, 3,3,3-trifluoropropyl, and cyanoethyl.
Claim 14
Dependent Claim
18 words
The composition of claim 11 where at least 70% of the radicals represented by R 7 are methyl.
Claim 15
Dependent Claim
12 words
The composition of claim 1 wherein the hydroxyl-terminated polyorganosiloxane is an α,ω-dihydroxypolydimethylsiloxane.
Claim 16
Dependent Claim
20 words
The composition of claim 1 where the polydiorganosiloxane exhibits a viscosity of from 0.2 to 200 Pa.s at 25° C.
Claim 17
Dependent Claim
45 words
The composition of claim 1 where said composition contains from 5 to 500 parts by weight of a finely divided filler selected from the group consisting of fume silica, calcined silica, precipitated silica, powdered quartz, calcium carbonate, titanium dioxide, diatomaceous earth, aluminum hydroxide and alumina.
Claim 18
Dependent Claim
11 words
The composition of claim 16 where the filler is calcium carbonate.
Claim 19
Dependent Claim
17 words
The composition of claim 16 wherein the filler concentration is from 20 to 300 parts by weight.
References Cited (Backward Citations)
US4358558A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-08 | 1987-11-07 | 1988-05-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-08 | 1991-11-07 | 1992-05-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-08 | 1995-11-07 | 1996-05-08 | $7700.00 | Window Closed / Lapsed |