Pigments and their preparation by coating with oxides of Zr-Si-Al

Claim 2

Titanium dioxide pigments comprising particulate titanium dioxide having (i) an inner coating on a core of rutile titanium dioxide of an oxide or hydrous oxide of zirconium in an amount of from about 1% to about 4% by weight, expressed as ZrO 2 by weight of TiO 2 ; (ii) a coating of dense, amorphous silica in an amount of from about 2% to about 12% by weight, expressed as SiO 2 by weight of TiO 2 carried on the inner coating; and (iii) an outer coating of a hydrous oxide of alumina in an amount of from about 1% to about 6% by weight, expressed as Al 2 O 3 by weight of TiO 2 .

Claim 3

Titanium dioxide pigment according to claim 1 in which the amount of dense amorphous silica is from 4% to 8% by weight expressed as SiO 2 on weight of TiO 2 .

Claim 4

Titanium dioxide pigment according to claim 1 in which the optional outer coating of hydrous alumina is present in an amount of from 1% to 3% expressed as Al 2 O 3 on weight of TiO 2 .

Claim 5

A process for the manufacture of titanium dioxide pigment that comprises (i) depositing on a particulate core material comprising rutile titanium dioxide an inner coating of an oxide or hydrous oxide of zirconium in an amount of from about 1% to about 4% by weight, expressed as ZrO 2 by weight of TiO 2 ; (ii) forming an aqueous dispersion of said coated particles in admixture with a water-soluble silicate and depositing at a pH greater than 8 a dense, amorphous coating of silica on the inner coating on the core particles with the amount of the dense, amorphous silica being deposited in an amount of from about 2% to about 12% by weight, expressed as SiO 2 by weight of TiO 2 ; and (iii) depositing from a water-soluble aluminium compound a hydrous oxide of alumina as an outer coating on said pigment after the deposition of said dense, amorphous silica with the amount of the hydrous oxide of alumina being deposited in an amount of from about 1% to about 6% by weight, expressed as Al 2 O 3 by weight of TiO 2 .

Claim 6

A process for the manufacture of titanium dioxide pigment that comprises (i) depositing on a particulate core material comprising rutile titanium dioxide an inner coating of an oxide or hydrous oxide of zirconium in an amount of from about 1% to about 4% by weight, expressed as ZrO 2 by weight of TiO 2 ; (ii) forming an aqueous dispersion of said coated particles in admixture with a water-soluble silicate and depositing at a pH greater than 8 a dense, amorphous coating of silica on the inner coating on the core particles with the amount of the dense, amorphous silica being deposited in an amount of from about 2% to about 12% by weight, expressed as SiO 2 by weight of TiO 2 ; and (iii) depositing from a water-soluble aluminium compound a hydrous oxide of alumina as an outer coating on said pigment after the deposition of said dense, amorphous silica with the amount of the hydrous oxide of alumina being deposited in an amount of from about 1% to about 6% by weight, expressed as Al 2 O 3 by weight of TiO 2 .

Claim 7

A process according to claim 4 in which the rutile titanium dioxide particulate core material is obtained by the vapour phase oxidation of titanium tetrachloride.

Claim 8

A process according to claim 4 in which the rutile titanium dioxide core material is a calcined pigment obtained by the "sulphate" process.

Claim 9

A process according to claim 5 in which the inner coating is deposited in the vapour phase by oxidising an oxidisable zirconium compound with an oxygen-containing gas.

Claim 10

A process according to claim 4 in which the core material is milled prior to coating with a hydrous oxide of zirconium or prior to coating with the dense amorphous coating of silica.

Claim 11

A process according to claim 8 in which the milling is carried out by sand milling.

Claim 12

A process according to claim 4 in which the core material having said inner coating in the form of an aqueous dispersion is mixed with an alkaline solution of a silicate and to which is then added a mineral acid to deposit the said dense amorphous coating while maintaining the pH at a value greater than 8.

Claim 13

A process according to claim 4 in which the core material carrying said inner coating in the form of an aqueous dispersion is mixed simultaneously with an aqueous alkaline solution of a silicate and a mineral acid in amounts such that the pH is maintained at a value greater than 8 to deposit said dense amorphous silica.

Claim 14

A process according to claim 4 in which the temperature is maintained at a value of from 70° C. to 90° C. and the pH at a value of from 9 to 10.5 during deposition of said dense amorphous silica.