Abstract
Abstract Directed to an overaging heat treatment applied to age-hardenable nickel-cobalt-iron controlled expansion alloys so as to contribute high notch strength at temperatures on the order of about 1000 DEG F. thereto.
Inventors
- 👤 Darrell F. Smith, Jr.
- 👤 Edward F. Clatworthy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 20:40
CPC Classifications
C; C22; C22F; C22F1/00; C22F1/10; C21; C21D; C21D6/00; C21D6/001; C22C; C22C19/00; C22C19/03; C22C38/00; C22C38/10; C22C38/105
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
208 words
The method for providing elevated temperature notch strength in wrought products made of an alloy consisting essentially of about 34% to about 55% nickel, about 5% to about 25% cobalt, about 1.5% to about 5.5% columbium, about 1% to about 2% titanium, no more than 0.2% aluminum, up to about 0.1% carbon and the balance essentially iron, said columbium being replaceable by tantalum on the basis of two parts of tantalum for each part of columbium by weight, which comprises annealing said product at a temperature of about 1650° F. to about 1925° F. and then heating said annealed product in an intermediate temperature range of about 1375° F. to about 1550° F. for a time sufficient to overage said product, with the proviso that said intermediate temperature and time are upwardly graduated as the annealing temperature is increased, said temperature and time relationship being equivalent to at least 8 hours at the intermediate temperature of 1425° F. when the annealing temperature is 1900° F., and then heat treating said product in a lower temperature range of about 1100° F. to 1400° F. for at least 8 hours to provide in said product a notch strength of at least about 100 hours at 1000° F. and 100 ksi.
Claim 2
Independent Claim
208 words
The method for providing elevated temperature notch strength in wrought products made of an alloy consisting essentially of about 34% to about 55% nickel, about 5% to about 25% cobalt, about 1.5% to about 5.5% columbium, about 1% to about 2% titanium, no more than 0.2% aluminum, up to about 0.1% carbon and the balance essentially iron, said columbium being replaceable by tantalum on the basis of two parts of tantalum for each part of columbium by weight, which comprises annealing said product at a temperature of about 1650° F. to about 1925° F. and then heating said annealed product in an intermediate temperature range of about 1375° F. to about 1550° F. for a time sufficient to overage said product, with the proviso that said intermediate temperature and time are upwardly graduated as the annealing temperature is increased, said temperature and time relationship being equivalent to at least 8 hours at the intermediate temperature of 1425° F. when the annealing temperature is 1900° F., and then heat treating said product in a lower temperature range of about 1100° F. to 1400° F. for at least 8 hours to provide in said product a notch strength of at least about 100 hours at 1000° F. and 100 ksi.
Claim 3
Dependent Claim
43 words
The method in accordance with claim 1 wherein said intermediate temperature treatment is conducted at a temperature of at least about 1425° F. and for more than 8 hours when said annealing treatment is conducted at a temperature of at least 1800° F.
Claim 4
Dependent Claim
25 words
The method in accordance with claim 1 wherein the product is slowly cooled from the intermediate temperature to a temperature within the lower temperature range.
Claim 5
Dependent Claim
22 words
The method in accordance with claim 3 wherein the cooling rate is about 20° F. per hour to 200° F. per hour.
Claim 6
Dependent Claim
35 words
The method in accordance with claim 1 wherein the annealed product is heated isothermally in the intermediate temperature range, is slowly cooled to a temperature in the lower temperature range and is then isothermally treated.
Claim 7
Dependent Claim
52 words
The method in accordance with claim 1 wherein the product is air cooled from the intermediate temperature and is thereafter subjected to two-step aging treatment in the lower aging temperature range wherein the temperature of the first step is at least about 100° F. higher than the temperature of the second step.
Claim 8
Dependent Claim
134 words
A controlled expansion age hardened alloy consisting essentially of about 34% to about 45% nickel, about 5% to about 25% cobalt, about 1.5% to about 5.5% columbium, about 1% to about 2% titanium, not over about 0.2% aluminum, not over about 0.1% carbon, up to about 1% vanadium, up to about 2% hafnium, up to about 0.03% boron and the balance essentially iron, with the proviso that tantalum may be substituted for columbium on the basis of two parts of tantalum for each part of columbium by weight, said alloy being in the heat treated condition which includes an overaging treatment at a temperature in the range of about 1375° F. to about 1550° F. and being characterized by a notch strength of at least about 100 hours at 1000° F. and 100 ksi.
Claim 9
Dependent Claim
134 words
A controlled expansion age hardened alloy consisting essentially of about 34% to about 45% nickel, about 5% to about 25% cobalt, about 1.5% to about 5.5% columbium, about 1% to about 2% titanium, not over about 0.2% aluminum, not over about 0.1% carbon, up to about 1% vanadium, up to about 2% hafnium, up to about 0.03% boron and the balance essentially iron, with the proviso that tantalum may be substituted for columbium on the basis of two parts of tantalum for each part of columbium by weight, said alloy being in the heat treated condition which includes an overaging treatment at a temperature in the range of about 1375° F. to about 1550° F. and being characterized by a notch strength of at least about 100 hours at 1000° F. and 100 ksi.
Claim 10
Dependent Claim
134 words
A wrought product made of a controlled expansion age hardened alloy consisting essentially of about 34% to about 45% nickel, about 5% up to about 25% cobalt, about 1.5% to about 5.5% columbium, about 1% to about 2% titanium, not over about 0.2% aluminum, not over about 0.1% carbon, up to about 1% vanadium, up to 2% hafnium and the balance essentially iron, with the proviso that tantalum may be substituted for columbium on the basis of two parts of tantalum for each part of columbium by weight, said product being in the heat treated condition which includes an overaging treatment at a temperature in the range of about 1375° F. to about 1550° F. and being characterized by a notch strength of at least about 100 hours at 1000° F. and 100 ksi.
Claim 11
Dependent Claim
134 words
A wrought product made of a controlled expansion age hardened alloy consisting essentially of about 34% to about 45% nickel, about 5% up to about 25% cobalt, about 1.5% to about 5.5% columbium, about 1% to about 2% titanium, not over about 0.2% aluminum, not over about 0.1% carbon, up to about 1% vanadium, up to 2% hafnium and the balance essentially iron, with the proviso that tantalum may be substituted for columbium on the basis of two parts of tantalum for each part of columbium by weight, said product being in the heat treated condition which includes an overaging treatment at a temperature in the range of about 1375° F. to about 1550° F. and being characterized by a notch strength of at least about 100 hours at 1000° F. and 100 ksi.
Claim 12
Dependent Claim
19 words
A wrought product in accordance with claim 8, wherein the cobalt content of the alloy is at least 10%.
Claim 13
Dependent Claim
20 words
A wrought product in accordance with claim 8, wherein the cobalt content of the alloy is about 12% to 16%.
Claim 14
Dependent Claim
20 words
A wrought product in accordance with claim 8, wherein the boron level of the alloy is up to about 0.03%.
Claim 15
Dependent Claim
21 words
A wrought product in accordance with claim 8, wherein the iron content of the alloy is about 20% to about 55%.
Claim 16
Dependent Claim
19 words
A wrought product in accordance with claim 8, wherein the ##EQU1## level in the alloy does not exceed 4.5.
Claim 17
Dependent Claim
21 words
A brazed wrought product in accordance with claim 8, wherein the article is annealed at a temperature of about 1900° F.
Claim 18
Dependent Claim
24 words
An article of manufacture designed for use at temperatures in the order of 1000° F. made from the heat treated alloy of claim 7.
Claim 19
Dependent Claim
16 words
The method in accordance with claim 1, wherein the alloy contains up to about 45% nickel.
Claim 20
Dependent Claim
16 words
The method in accordance with claim 1, wherein the alloy contains up to about 0.03% boron.
Claim 21
Dependent Claim
121 words
A wrought product made of a controlled expansion age hardened alloy consisting essentially of about 34% to about 55% nickel, about 5% to about 25% cobalt, about 1.5% to about 5.5% columbium, about 1% to about 2% titanium, not over about 0.2% aluminum, not over about 0.1% carbon and the balance essentially iron, with the proviso that tantalum may be substituted for columbium on the basis of two parts of tantalum for each part of columbium by weight, said product being in the heat treated condition which includes an overaging treatment and being characterized by a notch strength of at least about 100 hours at 1000° F. and 100 ksi, and said product being made by the method of claim 1.
References Cited (Backward Citations)
US4200459A
Cited
US4200459B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-01 | 1987-10-31 | 1988-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-01 | 1991-10-31 | 1992-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-01 | 1995-10-31 | 1996-05-01 | $7700.00 | Window Closed / Lapsed |