Assignee: Teijin Ltd
•
Filing: 1983-04-26
•
Granted: 1984-05-01
•
Expires: 2003-04-26
Abstract
Abstract A process for the preparation of a woven fabric of low air permeability which comprises preparing a woven fabric by use of a composite fiber of a splitting and severing type, which consists of polyester and polyamide and produces extremely fine fibers of 0.001 to 0.8 denier size, as a warp and/or a weft; treating thus obtained woven fabric by use of an aqueous emulsion of a swelling agent for polyester and nylon under the conditions where nylon is mainly allowed to swell and then shrink; scouring and dyeing the woven fabric; and after calendering the woven fabric with the use of heated rollers rotated under pressure.
Inventors
- 👤 Norihiro Minemura
- 👤 Shigenobu Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 14:02
CPC Classifications
D; D06; D06P; D06P3/00; D06P3/82; D06P3/8204; D06P3/8214
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
114 words
A process for the preparation of a woven fabric of low air permeability comprising preparing a woven fabric by use of a composite fiber of a splitting and severing type consisting of polyester components and polyamide components, each of which is to be splitted and severed to form an extra fine fiber of 0.001 to 0.8 denier size, as a warp and/or a weft; treating said woven fabric with an aqueous emulsion of a swelling agent for polyester and nylon under the conditions where nylon is mainly allowed to swell and then shrink; scouring and dyeing the woven fabric; and after calendering the woven fabric with the use of heated rollers rotated under pressure.
Claim 2
Dependent Claim
114 words
A process for the preparation of a woven fabric of low air permeability comprising preparing a woven fabric by use of a composite fiber of a splitting and severing type consisting of polyester components and polyamide components, each of which is to be splitted and severed to form an extra fine fiber of 0.001 to 0.8 denier size, as a warp and/or a weft; treating said woven fabric with an aqueous emulsion of a swelling agent for polyester and nylon under the conditions where nylon is mainly allowed to swell and then shrink; scouring and dyeing the woven fabric; and after calendering the woven fabric with the use of heated rollers rotated under pressure.
Claim 3
Dependent Claim
87 words
The process for the preparation of a woven fabric of low air permeability according to claim 1, wherein the process involves the treatment of the woven fabric with phenylphenols expressed by the following formula (I) used as a swelling agent for polyester and nylon, ##STR5## wherein R 1 indicates a phenyl group or a lower alkyl substituted phenyl group, in which the woven fabric is treated in an aqueous emulsion of 0.1 to 5% by weight of said phenylphenol at a temperature of 40° C. or lower.
Claim 4
Dependent Claim
150 words
The process for the preparation of a woven fabric of low air permeability according to claim 1, wherein the process involves the treatment of the woven fabric with at least one compound selected from a group consisting of chlorobenzenes expressed by the following formula (II), naphthalenes expressed by formula (III), and diphenyls expressed by formula (IV) used as a swelling agent for polyester and nylon, in which the woven fabric is treated in an aqueous emulsion of 0.1 to 5% by weight of said compound at a temperature of 60° C. or lower: ##STR6## wherein m is an integer 1 to 3, ##STR7## wherein R 2 is hydrogen or an alkyl group having 1 to 4 carbon atoms and n is an integer 1 to 2, ##STR8## wherein R 3 is hydrogen or an alkyl group having 1 to 4 carbon atoms and n' is an integer 1 to 2.
Claim 5
Dependent Claim
44 words
The process for the preparation of a woven fabric of low air permeability according to claim 1, wherein the process involves a water repellent treatment of the woven fabric after the scouring and dyeing and before a after the calendering of the woven fabric.
Claim 6
Dependent Claim
33 words
The process for the preparation of a woven fabric of low air permeability according to claim 1, wherein the process involves the water proof finish treatment of the woven fabric after the calendering.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-05-01 | 1987-10-31 | 1988-05-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-05-01 | 1991-10-31 | 1992-05-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-05-01 | 1995-10-31 | 1996-05-01 | $7700.00 | Window Closed / Lapsed |