Fiber reinforced composite article using modified polyimide adhesive
Assignee: IMI-TECH Corp ELK GROVE ILL A CORP OF
•
Filing: 1983-06-10
•
Granted: 1984-04-24
•
Expires: 2003-06-10
Abstract
Abstract Modified polyimide adhesives useful for high efficiency bonding at moderate temperatures. Basically, the adhesives are prepared by reacting suitable quantities of an oxime, an aromatic tetracarboxylic acid dianhydride and an aliphatic tetracarboxylic acid dianhydride, esterifying the resulting bisimide with a reactive solvent esterifying agent and mixing therewith a suitable diamine. This copolyimide adhesive may be dried to a selected viscosity before or after coating onto one or both surfaces to be bonded together. When the surfaces are pressed together under moderate pressure and heated for a suitable period at a temperature in the range of about 230° to 320° C. an excellent, flexible bond is obtained, having high peel strength and excellent resistance to high temperatures.
Inventors
- 👤 John Gagliani
- 👤 John V. Long
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 12:35
CPC Classifications
C; C08; C08G; C08G73/00; C08G73/06; C08G73/10; C08G73/1003; C08G73/1007; C08G73/1028; C08G73/1032; C08G73/1042; C09; C09J; C09J179/00; C09J179/04; C09J179/08; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24058; Y10T428/24124; Y10T428/31504; Y10T428/31721; Y10T442/00; Y10T442/30; Y10T442/3472; Y10T442/3504; Y10T442/3602; Y10T442/3667; Y10T442/3683; Y10T442/3691; Y10T442/60; Y10T442/659; Y10T442/67
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
157 words
A high strength fiber reinforced composite article produced from the method which comprises the steps of: preparing an adhesive mixture by mixing an aromatic tetracarboxylic acid dianhydride with an oxime in a mole ratio of oxime to tetracarboxylic acid dianhydride between about 0.01:1 and 1:1 to produce an N-substituted aliphatic imide, dissolving said imide in a solvent, adding thereto a diamine and adding to the mixture an aliphatic tetracarboxylic acid dianhydride either before or after the mixture is dissolved in said solvent, said solvent is a reactive solvent esterifying agent; soaking at least two woven fabric or mat sheets in said adhesive mixture; drying the soaked sheets of woven fabric or mat sheets at a temperature range of 100° to 150° f. to remove said solvent; and stacking said sheets in a mold and applying a pressure of about 5 to 100 psi at a temperature in the range of 300°-450° f. for 30 to 120 minutes.
Claim 2
Dependent Claim
157 words
A high strength fiber reinforced composite article produced from the method which comprises the steps of: preparing an adhesive mixture by mixing an aromatic tetracarboxylic acid dianhydride with an oxime in a mole ratio of oxime to tetracarboxylic acid dianhydride between about 0.01:1 and 1:1 to produce an N-substituted aliphatic imide, dissolving said imide in a solvent, adding thereto a diamine and adding to the mixture an aliphatic tetracarboxylic acid dianhydride either before or after the mixture is dissolved in said solvent, said solvent is a reactive solvent esterifying agent; soaking at least two woven fabric or mat sheets in said adhesive mixture; drying the soaked sheets of woven fabric or mat sheets at a temperature range of 100° to 150° f. to remove said solvent; and stacking said sheets in a mold and applying a pressure of about 5 to 100 psi at a temperature in the range of 300°-450° f. for 30 to 120 minutes.
Claim 3
Dependent Claim
18 words
The article of claim 1 wherein said at least two woven fabric sheets are constructed of glass fibers.
Claim 4
Dependent Claim
17 words
The article of claim 1 wherein said at least two woven fabric sheets are constructed graphite fibers.
Claim 5
Dependent Claim
18 words
The article of claim 1 wherein said at least two woven fabric sheets are constructed of carbon fibers.
Claim 6
Dependent Claim
32 words
The article of claim 1 wherein said at least two woven fabric sheets are constructed from one or more of a class of materials consisting of glass, graphite, carbon or Kevlar fiber.
Claim 7
Dependent Claim
14 words
The article of claim 1 wherein the fibers are positioned in a unidirectional relationship.
Claim 8
Dependent Claim
14 words
The article of claim 1 wherein the fibers are positioned in a cross-ply relationship.
Claim 9
Dependent Claim
14 words
The article of claim 1 wherein the fibers are positioned in a tandom direction.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-24 | 1987-10-24 | 1988-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-24 | 1991-10-24 | 1992-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-24 | 1995-10-24 | 1996-04-24 | $7700.00 | Window Closed / Lapsed |