Rapid setting accelerators for cementitious compositions
Assignee: PROCHEMTECHNOLOGY Inc
•
Filing: 1983-02-02
•
Granted: 1984-04-24
•
Expires: 2003-02-02
Abstract
Abstract A mixture comprised of an alkali metal carbonate and an inorganic salt of ferric iron, other than ferric phosphate, is an accelerator for cementitious compositions and is particularly useful for shotcrete and hand-applied mortar. The preferred alkali metal carbonates are sodium carbonate and potassium carbonate and the preferred ferric iron salts are ferric sulfate, ferric chloride and ferric nitrate. The mixture achieves initial set times of at most about 3 minutes and final set times of at most about 10 minutes. Both initial and final set times are shorter than predicted by simply averaging the corresponding set times of both components when used alone.
Inventors
- 👤 Raymond J. Schutz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:03
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
82 words
An improved process for shotcreting comprising: (1) hydrating a dry mixture consisting essentially of (a) cement and (b) set accelerators comprising an alkali metal carbonate and an inorganic salt of ferric iron other than ferric phosphate, said set accelerators being sufficiently dispersed in the cement mixture to sustantially prevent them from reacting with each other by causing them to react with components of the cement; (2) within at most 10 minutes after said hydration, affixing the hydrated mixture into the desired conformation.
Claim 2
Dependent Claim
82 words
An improved process for shotcreting comprising: (1) hydrating a dry mixture consisting essentially of (a) cement and (b) set accelerators comprising an alkali metal carbonate and an inorganic salt of ferric iron other than ferric phosphate, said set accelerators being sufficiently dispersed in the cement mixture to sustantially prevent them from reacting with each other by causing them to react with components of the cement; (2) within at most 10 minutes after said hydration, affixing the hydrated mixture into the desired conformation.
Claim 3
Dependent Claim
23 words
The process of claim 1 in which the alkali metal carbonate is selected from the group consisting of sodium carbonate and potassium carbonate.
Claim 4
Dependent Claim
24 words
The process of claim 1 in which the inorganic ferric iron salt is selected from the group consisting of ferric chloride and ferric nitrate.
Claim 5
Dependent Claim
15 words
The process of claim 1 in which the inorganic ferric iron salt is ferric sulfate.
Claim 6
Dependent Claim
25 words
The process of claim 1 in which the set accelerators are present in an amount of about 0.5 weight percent to about 10 weight percent.
Claim 7
Dependent Claim
25 words
The process of claim 1 in which the accelerator components are present in an amount from about 0.5 weight percent to about 5 weight percent.
References Cited (Backward Citations)
SU196592A1
Cited
US4209335A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-24 | 1987-10-24 | 1988-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-24 | 1991-10-24 | 1992-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-24 | 1995-10-24 | 1996-04-24 | $7700.00 | Window Closed / Lapsed |