US4443306A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process and cell for the preparation of polyvalent metals such as Zr or Hf by electrolysis of molten halides
Assignee: Pechiney SA
•
Filing: 1981-11-16
•
Granted: 1984-04-17
•
Expires: 2001-11-16
Abstract
Abstract The electrolysis cell according to the invention is concerned with the preparation of Zr or Hf by electrolysis, from a molten mixture of alkali metal or alkaline earth chlorides and fluorides. It comprises a graphite collector which defines the anodic space and which is extended at the lower end below the level of the electrolyte by a metal wall made of metal to be deposited or coated with said metal. The wall may advantageously be made in the form of a porous diaphragm.
Inventors
- 👤 Marcel Armand
- 👤 Philippe Moinard
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 19:25
CPC Classifications
C; C25; C25C; C25C7/00; C25C7/005; C25C3/00; C25C3/26
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
143 words
A process to electrolytically produce zirconium or hafnium from chlorides thereof in a bath of molten alkali metal or alkaline earth halides in an electrolytic cell consisting of: (a) providing above the electrolyte an anodic space defined by a graphite collector; (b) extending the lower end of the collector below the surface of the electrolyte to form a seal wherein the lower end of the collector is extended by an annular porous wall or diaphragm of polyvalent metal; (c) directing a negative current to said collector such that the electrical resistance of the electrolyte impregnating the collector is maintained at a constant value; and (d) maintaining the value of the electrical resistance of the electrolyte by adjusting the strength of the current directed to the collector as a function of the difference between the potential difference through the electrolyte and a reference potential.
Claim 2
Dependent Claim
143 words
A process to electrolytically produce zirconium or hafnium from chlorides thereof in a bath of molten alkali metal or alkaline earth halides in an electrolytic cell consisting of: (a) providing above the electrolyte an anodic space defined by a graphite collector; (b) extending the lower end of the collector below the surface of the electrolyte to form a seal wherein the lower end of the collector is extended by an annular porous wall or diaphragm of polyvalent metal; (c) directing a negative current to said collector such that the electrical resistance of the electrolyte impregnating the collector is maintained at a constant value; and (d) maintaining the value of the electrical resistance of the electrolyte by adjusting the strength of the current directed to the collector as a function of the difference between the potential difference through the electrolyte and a reference potential.
Claim 3
Dependent Claim
17 words
A process according to claim 1, wherein the annular wall of polyvalent metal is zirconium or hafnium.
Claim 4
Dependent Claim
34 words
A process according to claim 1, wherein the annular wall of polyvalent metal is a diaphragm of metal that cannot be attacked by the electrolyte and is coated with the metal to be deposited.
Claim 5
Dependent Claim
38 words
A process according to claim 1, wherein the annular wall is connected by way of the collector to the negative terminal of a current source, the positive terminal of which is connected to the anode of the cell.
Claim 6
Dependent Claim
29 words
A process according to claim 1, wherein two reference electrodes are disposed on respective sides of said wall and are connected to a means for measuring their potential difference.
Claim 7
Dependent Claim
36 words
A process according to claim 1, wherein the value of the electrical resistance of the electrolyte is expressed by the following equation: ##EQU4## in which R D represents the resistance of the electrolyte impregnating the diaphragm.
Claim 8
Dependent Claim
53 words
A cell according to claim 1, which includes means for maintaining the electrical resistance of the electrolyte which impregnates the diaphragm at a constant value by diverting into the diaphragm a current, the strength of which is dependent on the difference between the potential difference through the electrolyte and a reference potential difference.
Claim 9
Dependent Claim
133 words
A novel cell for the preparation of Zr or Hf by electrolysis of chlorides thereof in a bath of molten alkali metal and/or alkaline earth halides, which comprises a collector which defines an anodic space above the electrolyte, said collector comprising graphite or coated with graphite, the lower end of which collector penetrates a little below the surface of the electrolyte to form a hydraulic seal and is extended by a porous metal wall, which metal wall is a diaphragm made of a metal that cannot be attacked by the electrolyte and which is coated, prior to electrolysis, with the metal to be deposited during electrolysis, and which cell further comprises two reference electrodes disposed on opposite sides of the diaphragm and which are connected to a means for measuring their potential difference.
Claim 10
Dependent Claim
133 words
A novel cell for the preparation of Zr or Hf by electrolysis of chlorides thereof in a bath of molten alkali metal and/or alkaline earth halides, which comprises a collector which defines an anodic space above the electrolyte, said collector comprising graphite or coated with graphite, the lower end of which collector penetrates a little below the surface of the electrolyte to form a hydraulic seal and is extended by a porous metal wall, which metal wall is a diaphragm made of a metal that cannot be attacked by the electrolyte and which is coated, prior to electrolysis, with the metal to be deposited during electrolysis, and which cell further comprises two reference electrodes disposed on opposite sides of the diaphragm and which are connected to a means for measuring their potential difference.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-17 | 1987-10-17 | 1988-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-17 | 1991-10-17 | 1992-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-17 | 1995-10-17 | 1996-04-17 | $7700.00 | Window Closed / Lapsed |