Process for removing copper and copper oxide encrustations from ferrous surfaces
Assignee: Hydrochem LLC
•
Filing: 1981-11-12
•
Granted: 1984-04-17
•
Expires: 2001-11-12
Abstract
Abstract Aqueous alkaline solutions containing ferric chelates of alkylenepolyamine polycarboxylic acids (e.g. EDTA) have been used to remove plated copper from freshly cleaned ferrous metal surfaces. Normally, an oxidant is added during the copper removal stage to oxidize ferrous ion to the ferric state. This process is improved by adding aqueous hydrogen peroxide to the flowing cleaning solution at a rate such that the solution EMF (platinum or iron versus a saturated calomel electrode), as measured at about 80° F. and at a solution pH of about 9.2, becomes more positive than -250 mV in about one hour.
Inventors
- 👤 Thomas G. Cook
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 07:32
CPC Classifications
C; C23; C23G; C23G1/00; C23G1/14; C23G1/19
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
100 words
In the process for removing copper and copper oxide-containing encrustations from ferrous metal surfaces by contacting the surfaces with an aqueous alkaline cleaning solution containing a ferric chelate(s) of an alkylenepolyamine polyacetic acid and/or soluble chelating aminated or ammoniated salt(s) thereof in amounts and under conditions sufficient to dissolve said copper and copper oxide-containing encrustations, the improvement comprising adding aqueous hydrogen peroxide to said cleaning solution at a rate such that the solution electromotive force, as measured at about 80° F. (platinum vs. a saturated calomel electrode), becomes more positive than about -250 millivolts in less than about one hour.
Claim 2
Dependent Claim
100 words
In the process for removing copper and copper oxide-containing encrustations from ferrous metal surfaces by contacting the surfaces with an aqueous alkaline cleaning solution containing a ferric chelate(s) of an alkylenepolyamine polyacetic acid and/or soluble chelating aminated or ammoniated salt(s) thereof in amounts and under conditions sufficient to dissolve said copper and copper oxide-containing encrustations, the improvement comprising adding aqueous hydrogen peroxide to said cleaning solution at a rate such that the solution electromotive force, as measured at about 80° F. (platinum vs. a saturated calomel electrode), becomes more positive than about -250 millivolts in less than about one hour.
Claim 3
Dependent Claim
24 words
The process defined by claim 1 wherein said aqueous hydrogen peroxide is about 35 weight percent solution of H 2 O 2 in water.
Claim 4
Dependent Claim
22 words
The process defined by claims 1 or 2 wherein said alkylenepolyamine polyacetic acid is ethylenediaminetetraacetic acid (EDTA) and/or an ammoniated salt thereof.
Claim 5
Dependent Claim
20 words
The process defined by claim 1 wherein the pH of said cleaning solution is from about 7 to about 10.
Claim 6
Dependent Claim
20 words
The process defined by claim 4 wherein the pH of said cleaning solution is from about 9.0 to about 9.2.
Claim 7
Dependent Claim
21 words
The process defined by claim 1 wherein the temperature of said cleaning solution is from about 140° to about 180° F.
Claim 8
Dependent Claim
45 words
The process defined by claim 1 wherein said cleaning solution is the "waste" produced by dissolving an iron oxide containing scale from a ferrous metal surface using an aqueous alkaline solution containing an alkylenepolyamine polyacetic acid and/or a soluble chelating aminated or ammoniated salt(s) thereof.
Claim 9
Dependent Claim
135 words
A process for cleaning and passivating a ferrous metal surface comprising the steps of: (a) dissolving iron oxide-containing encrustations from said ferrous metal surface by contacting said surface with an aqueous alkaline cleaning solution containing an alkylenepolyamine polyacetic acid and/or a soluble chelating aminated or ammoniated salt(s) thereof in amounts and under conditions sufficient to dissolve said iron oxide-containing encrustations and thereby produce an aqueous waste solution containing ferric and/or ferrous chelate of said alkylenepolyamine polyacetic acid and/or said salts thereof, and thereafter; (b) dissolving copper from the ferrous metal surface by adding aqueous hydrogen peroxide to said aqueous waste solution at a rate such that the solution electromotive force, as measured at about 80° F. (platinum vs. a saturated calomel electrode), becomes more positive than about -250 millivolts in less than about one hour.
Claim 10
Dependent Claim
135 words
A process for cleaning and passivating a ferrous metal surface comprising the steps of: (a) dissolving iron oxide-containing encrustations from said ferrous metal surface by contacting said surface with an aqueous alkaline cleaning solution containing an alkylenepolyamine polyacetic acid and/or a soluble chelating aminated or ammoniated salt(s) thereof in amounts and under conditions sufficient to dissolve said iron oxide-containing encrustations and thereby produce an aqueous waste solution containing ferric and/or ferrous chelate of said alkylenepolyamine polyacetic acid and/or said salts thereof, and thereafter; (b) dissolving copper from the ferrous metal surface by adding aqueous hydrogen peroxide to said aqueous waste solution at a rate such that the solution electromotive force, as measured at about 80° F. (platinum vs. a saturated calomel electrode), becomes more positive than about -250 millivolts in less than about one hour.
Claim 11
Dependent Claim
19 words
The process defined by claim 8 wherein said alkylenepolyamine polyacetic acid is ethylenediaminetetraacetic acid and/or an ammoniated salt thereof.
Claim 12
Dependent Claim
20 words
The process defined by claim 1 wherein said alkylenepolyamine polyacetic acid is ethylenediaminetetraacetic acid, N-hydroxyethylethylenediaminetriacetic acid, and/or ammoniated salts thereof.
Claim 13
Dependent Claim
20 words
The process defined by claim 7 wherein said alkylenepolyamine polyacetic acid is ethylenediaminetetraacetic acid, N-hydroxyethylethylenediaminetriacetic acid, and/or ammoniated salts thereof.
Claim 14
Dependent Claim
20 words
The process defined by claim 8 wherein said alkylenepolyamine polyacetic acid is ethylenediaminetetraacetic acid, N-hydroxyethylethylenediaminetriacetic acid, and/or ammoniated salts thereof.
References Cited (Backward Citations)
US3438811A
Cited
US3413160A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-17 | 1987-10-17 | 1988-04-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-17 | 1991-10-17 | 1992-04-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-17 | 1995-10-17 | 1996-04-17 | $7700.00 | Window Closed / Lapsed |