Abstract
Abstract Mica reinforced thermoplastic composites, especially polypropylene composites, are prepared by a hot melt mixing process in which the mix contains propylene polymer waxes, in an amount up to about 10 percent by weight based upon the mica. The propylene polymer wax may be degraded, hydrocarbon isotactic polypropylene, or derivatized polypropylene wax such as maleated or sulfonated polypropylene wax. The wax has the effect of increasing the tensile strength and durability of the composite, and providing a smooth, uniform and glossy surface finish.
Inventors
- 👤 Raymond T. Woodhams
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:49
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/10; C08L23/12; C08K; C08K3/00; C08K3/01; C08K3/013; C08L101/00; C08L91/00; C08L91/06
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
79 words
A reinforced thermoplastic resin composite comprising a thermoplastic high molecular weight polymeric matrix material reinforced with inorganic filler material, said filler comprising from about 20 to about 80 volume percent of the total composite, said composite also containing from about 1 to about 10 weight percent, based upon the weight of inorganic filler, of derivatized propylene polymer wax of number average molecular weight from about 500 to about 10,000, said derivatized propylene polymer wax having functional reactive end groups.
Claim 2
Dependent Claim
79 words
A reinforced thermoplastic resin composite comprising a thermoplastic high molecular weight polymeric matrix material reinforced with inorganic filler material, said filler comprising from about 20 to about 80 volume percent of the total composite, said composite also containing from about 1 to about 10 weight percent, based upon the weight of inorganic filler, of derivatized propylene polymer wax of number average molecular weight from about 500 to about 10,000, said derivatized propylene polymer wax having functional reactive end groups.
Claim 3
Dependent Claim
21 words
The composite of claim 1 wherein the thermoplastic polymeric matrix material is selected from polypropylene, ethylene-propylene copolymers, and other propylene-α-olefin copolymers.
Claim 4
Dependent Claim
24 words
The composite of claim 2 wherein the inorganic filler material is selected from mica, talc, calcium carbonate, silica, glass fibres, graphite, asbestos and wollastonite.
Claim 5
Dependent Claim
12 words
The composite of claim 3 wherein the filler material is mica flakes.
Claim 6
Dependent Claim
21 words
The composite of claim 4 wherein the mica flakes are high aspect ratio mica flakes, of aspect ratio at least 30.
Claim 7
Dependent Claim
12 words
The composite of claim 5 wherein the polymeric matrix material is polypropylene.
Claim 8
Dependent Claim
14 words
The composite of claim 4 wherein the propylene polymer wax is hydrocarbon polypropylene wax.
Claim 9
Dependent Claim
21 words
The composite of claim 4 wherein the propylene polymer wax is derivatized polypropylene wax having acidic functional reactive end groups thereon.
Claim 10
Dependent Claim
20 words
The composite of claim 4 wherein the mica is surface treated with silylating agents prior to incorporation into the composite.
Claim 11
Dependent Claim
92 words
A process for preparing thermoplastic resin composites reinforced with inorganic filler material, which comprises intimately dispersing in a molten, high molecular weight thermoplastic polymeric matrix material an inorganic filler material, in the amount of about 20 to about 80 volume percent of the total composite, in the presence of from about 1 to about 10 weight percent, based on the weight of inorganic filler, of derivatized propylene polymer wax having a number average molecular weight of from about 500 to about 10,000, said derivatized propylene polymer wax having functional reactive end groups.
Claim 12
Dependent Claim
92 words
A process for preparing thermoplastic resin composites reinforced with inorganic filler material, which comprises intimately dispersing in a molten, high molecular weight thermoplastic polymeric matrix material an inorganic filler material, in the amount of about 20 to about 80 volume percent of the total composite, in the presence of from about 1 to about 10 weight percent, based on the weight of inorganic filler, of derivatized propylene polymer wax having a number average molecular weight of from about 500 to about 10,000, said derivatized propylene polymer wax having functional reactive end groups.
Claim 13
Dependent Claim
19 words
The process of claim 10 wherein the thermoplastic resin is selected from polypropylene, ethylene-propylene copolymers and other propylene-α-olefin copolymers.
Claim 14
Dependent Claim
24 words
The process of claim 11 wherein the inorganic filler material is selected from mica, talc, calcium carbonate, silica, glass fibres, graphite, asbestos and wollastonite.
Claim 15
Dependent Claim
18 words
The process of claim 12 wherein the thermoplastic resin is polypropylene and the filler material is mica flakes.
Claim 16
Dependent Claim
34 words
The process of claim 13 wherein intimate dispersion is achieved by mixing the molten thermoplastic polypropylene and the mica flakes, in the presence of said propylene polymer wax, under conditions of high shear agitation.
Claim 17
Dependent Claim
23 words
The process of claim 13 including the step of pretreating the mica with silylating agent prior to dispersing it in the molten polypropylene.
Claim 18
Dependent Claim
15 words
The process of claim 13 wherein the propylene polymer wax is hydrocarbon isotactic polypropylene wax.
Claim 19
Dependent Claim
21 words
The process of claim 13 wherein the propylene polymer wax is derivatized polypropylene wax having acidic functional reactive end groups thereon.
Claim 20
Dependent Claim
39 words
The process of claim 17 including preliminary steps of emulsifying the derivatized polypropylene wax to form an aqueous emulsion thereof, and treating the mica flakes with the aqueous wax emulsion, prior to said dispersion in molten polypropylene matrix material.
Claim 21
Dependent Claim
102 words
A reinforced thermoplastic resin composite consisting essentially of high molecular weight, crystalline, isotactic polypropylene, a mica reinforcing material, and a functionalized propylene polymer wax of number average molecular weight from about 500 to about 10,000, said functionalized propylene polymer wax having an isotactic structure and having terminal carboxyl functions resulting from reaction of terminally unsaturated isotactic polypropylene wax with maleic or succinic anhydride, the mica content being from about 20 to about 80 volume percent of the total composite, and the functionalized propylene polymer wax content being from about 1 to about 10 percent by weight based upon the weight of mica.
Claim 22
Dependent Claim
102 words
A reinforced thermoplastic resin composite consisting essentially of high molecular weight, crystalline, isotactic polypropylene, a mica reinforcing material, and a functionalized propylene polymer wax of number average molecular weight from about 500 to about 10,000, said functionalized propylene polymer wax having an isotactic structure and having terminal carboxyl functions resulting from reaction of terminally unsaturated isotactic polypropylene wax with maleic or succinic anhydride, the mica content being from about 20 to about 80 volume percent of the total composite, and the functionalized propylene polymer wax content being from about 1 to about 10 percent by weight based upon the weight of mica.
Claim 23
Dependent Claim
22 words
The composite of claim 19, wherein the mica is mica flakes surface treated with silylating agents prior to incorporation into the composite.
References Cited (Backward Citations)
US3243395A
Cited
US3271340A
Cited
US3775359A
Cited
US4317765A
Cited
US3580882A
Cited
US4040997A
Cited
JPS5365346A
Cited
US4165302A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-10 | 1987-10-10 | 1988-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-10 | 1991-10-10 | 1992-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-10 | 1995-10-10 | 1996-04-10 | $7700.00 | Window Closed / Lapsed |