Dental filling materials
Assignee: Bisco Inc
•
Filing: 1983-07-14
•
Granted: 1984-04-10
•
Expires: 2003-07-14
Abstract
Abstract An inorganic filler component for use in resin-based direct dental filling materials comprises fumed or submicron silica which has been silane treated and coated with a thin coating of an active polymerizable monomer of the type used as the binder in making the composition. The use of such a submicron material permits the total filler loading of the composition to be increased substantially, thereby increasing both the compressive and diametrical tensile strength of the cured material as well as improving its polishability and resistance to wear, and reducing its susceptibility to water absorption.
Inventors
- 👤 Byoung I. Suh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 04:46
CPC Classifications
A; A61; A61K; A61K6/00; A61K6/80; A61K6/884; A61K6/887; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2995
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
49 words
A finely divided inorganic filler for use in preparing direct dental filling materials, said filler comprising organo-silane keying agent treated fumed silica having a surface coating comprising about 2-20%, based on the weight of the silica, of an active polyfunctional polymerizable monomer having at least two acrylic end groups.
Claim 2
Dependent Claim
49 words
A finely divided inorganic filler for use in preparing direct dental filling materials, said filler comprising organo-silane keying agent treated fumed silica having a surface coating comprising about 2-20%, based on the weight of the silica, of an active polyfunctional polymerizable monomer having at least two acrylic end groups.
Claim 3
Dependent Claim
42 words
A filler in accordance with claim 1 further including a finely divided organosilane keying agent treated inorganic filler having a particle size of about 1-85 microns in admixture with said fumed silica, said silica comprising about 2-90% by weight of said mixture.
Claim 4
Dependent Claim
16 words
A filler in accordance with claim 2 containing about 10-50% by weight of said fumed silica.
Claim 5
Independent Claim
79 words
A method of treating fumed silica for use as a filler in direct dental filling materials comprising the steps of: treating said silica with an organosilane keying agent; forming on the surface of said silane-treated silica a coating of a polymerizable monomer having at least two acrylic end groups, said coating comprising about 2-20% by weight of the silica; and heat treating said coated silica at a temperature between 90° C. and 130° C. for 1 to 5 hours.
Claim 6
Independent Claim
79 words
A method of treating fumed silica for use as a filler in direct dental filling materials comprising the steps of: treating said silica with an organosilane keying agent; forming on the surface of said silane-treated silica a coating of a polymerizable monomer having at least two acrylic end groups, said coating comprising about 2-20% by weight of the silica; and heat treating said coated silica at a temperature between 90° C. and 130° C. for 1 to 5 hours.
References Cited (Backward Citations)
US3194784A
Cited
US3272772A
Cited
GB1278413A
Cited
US3845009A
Cited
US4362842A
Cited
EP0047971A1
Cited
US4412015A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-10 | 1987-10-10 | 1988-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-10 | 1991-10-10 | 1992-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-10 | 1995-10-10 | 1996-04-10 | $7700.00 | Window Closed / Lapsed |