US4441940A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing toroidal tape cores for fault current safety switches and use of such cores
Assignee: Vacuumschmelze GmbH and Co KG
•
Filing: 1981-08-10
•
Granted: 1984-04-10
•
Expires: 2001-08-10
Abstract
Abstract In order to improve the temperature constancy of induction boost in a standard working temperature range for fault current safety switches, a Ni-Mo-Cu-Fe alloy is provided whose nickel and copper content in a binary nickel-copper system is defined by a quadrangle of points A (80.5 wt. % Ni and 0 wt. % Cu), B (82 wt. % Ni and 0 wt. % Cu), C (70 wt. % Ni and 16.5 wt. % Cu) and D (70 wt. % Ni and 14.4 wt. % Cu) and whose molybdenum content, z, in wt. % satisfies the relation: 11/30 (x-68)≦z≦11/30 (x-63.5) with a given Ni content, x, in wt. % and the remainder of which essentially consists of iron and minor processing impurities. Such an alloy is worked into a 0.05 through 0.3 mm thick tape and wound into a toroidal tape core which is first annealed for about 30 minutes at temperatures between 900° and 1200° C. and is then tempered in accordance with its Mo content at the temperatures between 450° and 550° C. in such a manner that the magnetic anisotropy, K 1 , becomes equal to 0 at temperatures between -5° and +30° C. Such toroidal tape cores are particularly useful as sum current transformer cores or pulse-current-sensitive fault current safety switches, with a trigger current strength of 30 mA.
Inventors
- 👤 Friedrich Pfeifer
- 👤 Willi Kessler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 19:30
CPC Classifications
H; H01; H01F; H01F41/00; H01F41/02; H01F41/0206; H01F41/0213
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
267 words
A method of producing torodial tape cores for fault current safety switches with a relatively high dynamic induction boost, B dyn , at least 0.08 T and, simultaneously, a relatively high temperature constancy of B dyn in the temperature range of about -5° to +80° C. from a toroidal tape core wound out of a 0.05 through 0.3 mm thick tape composed of a Ni-Mo-Cu-Fe alloy such core being subject to thermal treatment in a non-oxidizing atmosphere, said method comprising of: employing as said alloy a composition having an Ni and Cu content in a binary Ni-Cu system which is defined by an area bounded by a quadrangle of points A (80.5 wt. % Ni and 0 wt. % Cu), B (82 wt. % Ni and 0 wt. % Cu), C (70 wt. % Ni and 16.5 wt. % Cu), and D (70 wt. % Ni and 14.4 wt. % Cu), and having a Mo content, z, in wt. % which satisfies the relation: 11/30(x-68)≦z≦11/30(x-63.5) with a given Ni content, x, in wt. %. and the remainder consisting essentially of Fe along with minor amounts of impurities and usual processing-promiting and deoxidizing additives; said thermal treatments in said non-oxidizing atmosphere consisting of annealing said core for at least about 30 minutes at a temperature ranging between 900° and 1200° C., and thereafter tempering said so annealed tape core in accordance with its Mo content at a temperature ranging between 450° and 550° C. in such a manner that the magnetic anisotropy K 1 , thereof becomes equal to 0 at a temperature between -5° and +30° C.
Claim 2
Independent Claim
267 words
A method of producing torodial tape cores for fault current safety switches with a relatively high dynamic induction boost, B dyn , at least 0.08 T and, simultaneously, a relatively high temperature constancy of B dyn in the temperature range of about -5° to +80° C. from a toroidal tape core wound out of a 0.05 through 0.3 mm thick tape composed of a Ni-Mo-Cu-Fe alloy such core being subject to thermal treatment in a non-oxidizing atmosphere, said method comprising of: employing as said alloy a composition having an Ni and Cu content in a binary Ni-Cu system which is defined by an area bounded by a quadrangle of points A (80.5 wt. % Ni and 0 wt. % Cu), B (82 wt. % Ni and 0 wt. % Cu), C (70 wt. % Ni and 16.5 wt. % Cu), and D (70 wt. % Ni and 14.4 wt. % Cu), and having a Mo content, z, in wt. % which satisfies the relation: 11/30(x-68)≦z≦11/30(x-63.5) with a given Ni content, x, in wt. %. and the remainder consisting essentially of Fe along with minor amounts of impurities and usual processing-promiting and deoxidizing additives; said thermal treatments in said non-oxidizing atmosphere consisting of annealing said core for at least about 30 minutes at a temperature ranging between 900° and 1200° C., and thereafter tempering said so annealed tape core in accordance with its Mo content at a temperature ranging between 450° and 550° C. in such a manner that the magnetic anisotropy K 1 , thereof becomes equal to 0 at a temperature between -5° and +30° C.
Claim 3
Dependent Claim
27 words
The method as defined in claim 1 wherein said toroidal tape core produced from such alloy is annealed at a temperature ranging between 900° and 1050° C.
Claim 4
Dependent Claim
57 words
The method as defined in claim 2 wherein said annealed tape core is tempered at a temperature ranging between 470° and 520° C. as a function of the Mo content of the alloy forming said tape core in such a manner that K 1 thereof becomes equal to 0 at a temperature between 0° and 20° C.
Claim 5
Dependent Claim
57 words
The method as defined in claim 1 wherein said annealed tape core is tempered at a temperature ranging between 470° and 520° C. as a function of the Mo content of the alloy forming said tape core in such a manner that K 1 thereof becomes equal to 0 at a temperature between 0° and 20° C.
Claim 6
Dependent Claim
262 words
A toroidal tape core for an electronic safety switch, and for fault current-sensitive safety switches, with a relatively high dynamic induction boost, B dyn , at least 0.08 T and, simultaneously, a relatively high temperature constancy of B dyn in the temperature range of about -5° to +80° C.; said core having been wound out of a 0.05 through 0.3 mm thick tape composed of Ni-Mo-Cu-Fe alloy, such core having been subjected to thermal treatment in a non-oxidizing atmosphere, said alloy having a Ni and Cu content in a binary Ni-Cu system which is defined by an area bounded by a quadrangle of points A (80.5 wt. % Ni and 0 wt. % Cu), B (82 wt. % Ni and 0 wt. % Cu), C (70 wt. % Ni and 16.5 wt. % Cu), and D (70 wt. % Ni and 14.4 wt. % Cu), and having a Mo content, z, in wt. % which satisfies the relation: 11/30(x-68)≦z≦11/30(x-63.5) with a given Ni content, x, in wt. %, and the remainder consisting essentially of Fe along with minor amounts of impurities and usual processing-promoting and deoxidizing additives; said thermal treatment in said non-oxidizing atmosphere consisting of first annealing said core for at least about 30 minutes at a temperature ranging between 900° and 1200° C., and thereafter tempering said so annealed tape core in accordance with its Mo content at a temperature ranging between 450° and 550° C. in such a manner that the magnetic anisotropy K 1 , thereof becomes equal to 0 at a temperature between -5° and +30° C.
Claim 7
Dependent Claim
262 words
A toroidal tape core for an electronic safety switch, and for fault current-sensitive safety switches, with a relatively high dynamic induction boost, B dyn , at least 0.08 T and, simultaneously, a relatively high temperature constancy of B dyn in the temperature range of about -5° to +80° C.; said core having been wound out of a 0.05 through 0.3 mm thick tape composed of Ni-Mo-Cu-Fe alloy, such core having been subjected to thermal treatment in a non-oxidizing atmosphere, said alloy having a Ni and Cu content in a binary Ni-Cu system which is defined by an area bounded by a quadrangle of points A (80.5 wt. % Ni and 0 wt. % Cu), B (82 wt. % Ni and 0 wt. % Cu), C (70 wt. % Ni and 16.5 wt. % Cu), and D (70 wt. % Ni and 14.4 wt. % Cu), and having a Mo content, z, in wt. % which satisfies the relation: 11/30(x-68)≦z≦11/30(x-63.5) with a given Ni content, x, in wt. %, and the remainder consisting essentially of Fe along with minor amounts of impurities and usual processing-promoting and deoxidizing additives; said thermal treatment in said non-oxidizing atmosphere consisting of first annealing said core for at least about 30 minutes at a temperature ranging between 900° and 1200° C., and thereafter tempering said so annealed tape core in accordance with its Mo content at a temperature ranging between 450° and 550° C. in such a manner that the magnetic anisotropy K 1 , thereof becomes equal to 0 at a temperature between -5° and +30° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-10 | 1987-10-10 | 1988-04-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-10 | 1991-10-10 | 1992-04-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-10 | 1995-10-10 | 1996-04-10 | $7700.00 | Window Closed / Lapsed |