Synthetic rubber dispersions containing carboxyl groups, a process for their preparation and their use
Assignee: Bayer AG
•
Filing: 1981-12-04
•
Granted: 1984-04-03
•
Expires: 2001-12-04
Abstract
Abstract Synthetic rubber dispersions containing carboxyl groups, free from specks and with little tendency to foaming, with advantages for their technical application contain a copolymer of 0.3 to 1.0 parts by weight of itaconic acid and 99.0 to 99.7 parts by weight of a mixture of 10 to 90 parts by weight of one or more acyclic conjugated dienes having 4 to 9 carbon atoms and 10 to 90 parts by weight of one or more aryl vinyl monomers having 8 to 12 carbon atoms and/or (meth)acrylonitrile, in which the quantity of (meth)acrylonitrile is at most 50 parts by weight and wherein up to 25 parts by weight of the non-dissociating monomers may optionally be replaced by one or more other non-dissociating copolymerizable monomers, which dispersions are stabilized with 0.05 to 0.5% by weight, based on the copolymer, of an anionic emulsifier.
Inventors
- 👤 Ferdinand Heins
- 👤 Martin Matner
- 👤 Hellmut Striegler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:24
CPC Classifications
C; C08; C08F; C08F236/00; C08F236/02; C08F236/04; C08F236/10
Claims Analysis
Total Claims: 2
Claim 1
Independent Claim
212 words
Process for the preparation of aqueous synthetic rubber dispersions by emulsion polymerization of from 0.3 to 1.0% by weight of itaconic acid and 99.0 to 99.7% by weight of a mixture of from 10 to 90% by weight of butadiene, 10 to 90% by weight of styrene, 0 to 50% by weight of (meth)acrylonitrile and 0 to 25% by weight of N-methylol-(meth)-acrylamide and N-methoxymethyl-(meth)acrylamide in the presence of from 0.05 to 0.5% by weight, based on the copolymer, of an emulsifier consisting of the sulphate or sulphonate type comprising introducing part of the water, part or all of the itaconic acid, all or part of the emulsifier and part of the other monomers into a reactor equipped with a stirrer, adjusting the pH to 3.5 to 6 by addition of a base, initiating the polymerization at a temperature of at least 70° C. by addition of part of 0.5 to 1.5% by weight, based on the total quantity of monomers, of an ammonium peroxodisulphate and/or an alkali metal peroxodisulphate and adding at least one non-aqueous stream of the remaining monomers, and at least one aqueous stream containing the remainder of the peroxodisulphate while maintaining a temperature of the reactor of 75° to 150° C. until the monomers have undergone almost complete conversion.
Claim 2
Dependent Claim
212 words
Process for the preparation of aqueous synthetic rubber dispersions by emulsion polymerization of from 0.3 to 1.0% by weight of itaconic acid and 99.0 to 99.7% by weight of a mixture of from 10 to 90% by weight of butadiene, 10 to 90% by weight of styrene, 0 to 50% by weight of (meth)acrylonitrile and 0 to 25% by weight of N-methylol-(meth)-acrylamide and N-methoxymethyl-(meth)acrylamide in the presence of from 0.05 to 0.5% by weight, based on the copolymer, of an emulsifier consisting of the sulphate or sulphonate type comprising introducing part of the water, part or all of the itaconic acid, all or part of the emulsifier and part of the other monomers into a reactor equipped with a stirrer, adjusting the pH to 3.5 to 6 by addition of a base, initiating the polymerization at a temperature of at least 70° C. by addition of part of 0.5 to 1.5% by weight, based on the total quantity of monomers, of an ammonium peroxodisulphate and/or an alkali metal peroxodisulphate and adding at least one non-aqueous stream of the remaining monomers, and at least one aqueous stream containing the remainder of the peroxodisulphate while maintaining a temperature of the reactor of 75° to 150° C. until the monomers have undergone almost complete conversion.
References Cited (Backward Citations)
US3711437A
Cited
US3781236A
Cited
US3795647A
Cited
US3793244A
Cited
US4130691A
Cited
US4064081A
Cited
US4359543A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-03 | 1987-10-03 | 1988-04-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-03 | 1991-10-03 | 1992-04-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-03 | 1995-10-03 | 1996-04-03 | $7700.00 | Window Closed / Lapsed |