Process for producing epoxy resins
Assignee: Dow Chemical Co
•
Filing: 1983-02-28
•
Granted: 1984-03-20
•
Expires: 2003-02-28
Abstract
Abstract An improved process for reacting vicinal epoxides with phenols or thiophenols is described. This process is conducted at essentially anhydrous conditions and temperatures less than 175° C. The resulting resins are generally more linear and less colored than advanced resins produced via prior art processes. Also the phosphonium catalyst remains active to promote subsequent advancement or curing reactions. The catalyst can be deactivated in a separate step to produce a resin of exceptional purity.
Inventors
- 👤 George A. Doorakian
- 👤 Marsha A. Paul
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 11:13
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/62; C08G59/02; C08G59/04; C08G59/06; C08G59/066; C08G59/68
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
66 words
In a process for preparing an advanced epoxy resin by reacting (a) a compound bearing an average of more than one vicinal epoxide group per molecule with (b) a polyhydric phenol or thiophenol, in the presence of a catalytic amount of a tetrahydrocarbyl phosphonium salt, the improvement wherein the reaction is conducted at a temperature less than about 175° C. and in an essentially anhydrous medium.
Claim 2
Dependent Claim
66 words
In a process for preparing an advanced epoxy resin by reacting (a) a compound bearing an average of more than one vicinal epoxide group per molecule with (b) a polyhydric phenol or thiophenol, in the presence of a catalytic amount of a tetrahydrocarbyl phosphonium salt, the improvement wherein the reaction is conducted at a temperature less than about 175° C. and in an essentially anhydrous medium.
Claim 3
Dependent Claim
36 words
The process as described in claim 1, wherein at least about 50 percent of the tetrahydrocarbyl phosphonium cation salt employed as a catalyst is present as a phosphonium salt at the conclusion of the advancement reaction.
Claim 4
Dependent Claim
24 words
The process as described in claim 1 which further comprises the curing of the advanced resin with a conventional amine or anhydride curing reagent.
Claim 5
Dependent Claim
56 words
The process as described in claim 1 wherein the epoxy resin produced contains at least 20 percent more of the tetrahydrocarbyl phosphonium cation than in a similar advancement reaction where 0.01 weight percent water based on the reactants is present in the reaction medium and the maximum reaction or exotherm temperature is at least 180° C.
Claim 6
Dependent Claim
50 words
The process as described in claim 1 wherein the tetrahydrocarbyl phosphonium salt corresponds to the formulae I, II, III or IV ##STR14## wherein R at each occurrence is independently a hydrocarbyl or inertly substituted hydrocarbyl group, n is an integer from 1 to 20 and X is a compatible anion.
Claim 7
Dependent Claim
21 words
The process as described in claim 5 wherein at least one R borne by each phosphonium cation is an aryl moiety.
Claim 8
Dependent Claim
24 words
The process as described in claim 6 wherein one R is alkyl and the other R groups are aryl moieties for each phosphonium cation.
Claim 9
Dependent Claim
15 words
The process as described in claim 5 wherein the phosphonium salt corresponds to formula II.
Claim 10
Dependent Claim
19 words
The process as described in claim 8, wherein X.sup.⊖ is a halide, carboxylate, bicarbonate, biphosphate tetrafluoroborate, phenate or bisphenate.
Claim 11
Dependent Claim
24 words
The process as described in claim 9 wherein three of the R groups are phenyl and one is a C 1 -C 4 alkyl.
Claim 12
Dependent Claim
17 words
The process as described in claim 1 wherein the phosphonium salt is a phosphonium hydroxide inner salt.
Claim 13
Dependent Claim
37 words
The process as described in claim 6 further comprising the step of adding a sufficient quantity of a phosphonium ylid quenching reagent to selectively deactivate the tetrahydrocarbyl phosphonium catalyst without substantial reaction with the advanced epoxy resin.
Claim 14
Dependent Claim
15 words
The process as described in claim 12 wherein the phosphonium ylid quenching agent is water.
Claim 15
Dependent Claim
18 words
The process as described in claim 12 wherein the phosphonium ylid quenching agent is an aldehyde or ketone.
Claim 16
Dependent Claim
15 words
The advanced epoxy resin containing a tetrahydrocarbyl phosphonium salt produced as described in claim 2.
Claim 17
Dependent Claim
14 words
The advanced epoxy resin containing active phosphonium cations produced as described in claim 7.
Claim 18
Dependent Claim
14 words
The advanced epoxy resin containing active phosphonium cations produced as described in claim 10.
Claim 19
Dependent Claim
13 words
The advanced epoxy resin and deactivated catalyst produced as described in claim 12.
Claim 20
Dependent Claim
13 words
The advanced epoxy resin and deactivated catalyst produced as described in claim 13.
Claim 21
Dependent Claim
40 words
The advanced epoxy resin and deactivated catalyst as described in claim 19 wherein the phosphonium catalyst used to advance the resin corresponds to formula II where three R groups are phenyl and one is a C 1 -C 4 alkyl.
References Cited (Backward Citations)
US3547881A
Cited
US3477990A
Cited
US3547885A
Cited
US3694407A
Cited
US3948855A
Cited
US3738862A
Cited
US4171420A
Cited
US4048141A
Cited
US4352918A
Cited
US4389520A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-20 | 1987-09-19 | 1988-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-20 | 1991-09-19 | 1992-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-20 | 1995-09-19 | 1996-03-20 | $7700.00 | Window Closed / Lapsed |