Carboxylated nitrile rubber/PVC/nylon flux blends

Claim 2

A vulcanizable polymer composition comprising a polymer blend and a curative system, said polymer blend being a flux blend of (i) from about 5 to about 50 parts by weight of polyvinyl chloride, (ii) from about 35 to about 75 parts by weight of a carboxylated nitrile rubber, (iii) from about 5 to about 50 parts by weight of a nylon having a melting point of less than about 210° C., the total of (i), (ii) and (iii) being 100 parts by weight, (iv) from about 1.5 to about 4 parts by total weight of one or more stabilizers for (i), and (v) from about 0.25 to about 3 parts by total weight of one or more antioxidants for (ii), said parts of (iv) and (v) being per 100 parts total of (i), (ii) and (iii).

Claim 3

The composition according to claim 1 wherein (ii) is a copolymer of butadiene, acrylonitrile and one or more α,β-unsaturated carboxylic acids selected from acrylic, methacrylic, fumaric, maleic and itaconic acids, and (iii) is selected from nylon-11 and nylon-12.

Claim 4

The composition according to claim 2 wherein the acrylonitrile content of (ii) is from about 25 to about 35 percent by weight and the carboxylic acid content of (ii) is from about 4 to about 8 percent by weight based on said copolymer, the amount of (i) is from about 5 to about 35 parts by weight and the amount of (iii) is from about 15 to about 35 parts by weight.

Claim 5

The composition according to claim 2 wherein the acrylonitrile content of (ii) is from about 25 to about 35 percent by weight and the carboxylic acid content of (ii) is from about 0.5 to about 2 percent by weight based on the copolymer, the amount of (i) is from about 20 to about 35 parts by weight, the amount of (ii) is from about 35 to about 50 parts by weight, and the amount of (iii) is from about 20 to about 35 parts by weight.

Claim 6

The composition according to claim 2 wherein (iv) is from about 2 to about 3 parts by weight of a mixed metal salt of barium/cadmium and (v) is a mixture of from about 0.4 to about 1 part by weight of tris(nonylated phenyl) phosphite and from about 0.5 to about 1 part by weight of thiodiethylene bis(3,5-di-t-butyl-4-hydroxy)hydrocinnamate.

Claim 7

The vulcanizate obtained by heating the composition according to claim 2.

Claim 8

The vulcanizate obtained by heating the composition according to claim 3.

Claim 9

The vulcanizate obtained by heating the composition according to claim 4.

Claim 10

A process for preparing a vulcanizable polymer composition comprising admixing (i) from about 5 to about 50 parts by weight of polyvinyl chloride, (ii) from about 35 to about 75 parts by weight of a carboxylated nitrile rubber, (iii) from about 5 to about 50 parts by weight of a nylon having a melting point of less than about 210° C., the total of (i), (ii) and (iii) being 100 parts by weight, (iv) from about 1.5 to about 4 parts by total weight of one or more stabilizers for (i), and (v) from about 0.25 to about 3 parts by total weight of one or more antioxidants for (ii), said parts of (iv) and (v) being per 100 parts total of (i), (ii) and (iii), said admixing being at a temperature sufficient to cause fluxing of (i) and (iii) and mixing of all the components and for a length of time sufficient to cause such mixing but not to cause significant thermal degradation of the components, recovering and cooling the polymer blend so formed, and admixing said polymer blend with a curative system to form said polymer composition.

Claim 11

A process for preparing a vulcanizable polymer composition comprising admixing (i) from about 5 to about 50 parts by weight of polyvinyl chloride, (ii) from about 35 to about 75 parts by weight of a carboxylated nitrile rubber, (iii) from about 5 to about 50 parts by weight of a nylon having a melting point of less than about 210° C., the total of (i), (ii) and (iii) being 100 parts by weight, (iv) from about 1.5 to about 4 parts by total weight of one or more stabilizers for (i), and (v) from about 0.25 to about 3 parts by total weight of one or more antioxidants for (ii), said parts of (iv) and (v) being per 100 parts total of (i), (ii) and (iii), said admixing being at a temperature sufficient to cause fluxing of (i) and (iii) and mixing of all the components and for a length of time sufficient to cause such mixing but not to cause significant thermal degradation of the components, recovering and cooling the polymer blend so formed, and admixing said polymer blend with a curative system to form said polymer composition.

Claim 12

The process according to claim 9 wherein (ii) is a copolymer of butadiene, acrylonitrile and one or more α,β-unsaturated carboxylic acids selected from acrylic, methacrylic, fumaric, maleic and itaconic acids, and (iii) is selected from nylon-11 and nylon-12.

Claim 13

The process according to claim 10 wherein the acrylonitrile content of (ii) is from about 25 to about 35 percent by weight and the carboxylic acid content of (ii) is from about 4 to about 8 percent by weight based on said copolymer, the amount of (i) is from about 5 to about 35 parts by weight and the amount of (iii) is from about 15 to about 35 parts by weight.

Claim 14

The process according to claim 10 wherein the acrylonitrile content of (ii) is from about 25 to about 35 percent by weight and the carboxylic acid content of (ii) is from about 0.5 to about 2 percent by weight based on the copolymer, the amount of (i) is from about 20 to about 35 parts by weight, the amount of (ii) is from about 35 to about 50 parts by weight, and the amount of (iii) is from about 20 to about 35 parts by weight.

Claim 15

The process according to claim 10 wherein (iv) is from about 2 to about 3 parts by weight of a mixed metal salt of barium/cadmium and (v) is a mixture of from about 0.4 to about 1 part by weight of tris(nonylated phenyl) phosphite and from about 0.5 to about 1 part by weight of thiodiethylene bis(3,5-di-t-butyl-4-hydroxy)hydrocinnamate.

Claim 16

The process according to claim 10 wherein said curative system comprises an organic peroxide.

Claim 17

The process according to claim 14 wherein said curative system additionally comprises one or more sulfur-containing accelerators.

Claim 18

The process according to claim 10 wherein said curative system comprises elemental sulfur and one or more sulfur-containing accelerators.

Claim 19

The process according to claim 16 wherein said curative system additionally comprises a masterbatch of about equal parts by weight of zinc peroxide and a butadiene-acrylonitrile rubber.

Claim 20

The process according to claim 10 which further comprises heating said polymer composition to provide a vulcanizate.

Claim 21

The process according to claim 11 which further comprises heating said polymer composition to provide a vulcanizate.

Claim 22

The process according to claim 12 which further comprises heating said polymer composition to provide a vulcanizate.

Claim 23

The process according to claim 17 which further comprises heating said polymer composition to provide a vulcanizate.