Process for coating nylon film with vinylidene chloride copolymers
Assignee: DuPont Canada Inc
•
Filing: 1982-08-16
•
Granted: 1984-03-20
•
Expires: 2002-08-16
Abstract
Abstract A process for coating nylon film with polyvinylidene chloride is disclosed, comprising primer-coating the nylon film with an aqueous dispersion of a vinylidene chloride copolymer having a crystallinity index of less than 1.15 after 30 days' storage at 20° C. and between about 1.05 and 1.20 when stored for 48 hours at 40° C.; drying the primer-coated film; coating the primer-coated film with an aqueous dispersion of a vinylidene chloride copolymer capable of developing crystallinity to a level sufficient that the crystalline vinylidene chloride copolymer so-formed resists attack by an organic solvent, as measured by the Solvent Haze Test; and drying the coated film. During primer-coating and the first drying step, the film is kept under sufficient tension to prevent curling of the film. The coated film may be laminated to polyethylene to provide a laminate useful for packaging of processed food.
Inventors
- 👤 Theodore J. Lang
- 👤 Bernard J. Kershaw
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 23:56
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/02; B05D7/04; C; C08; C08J; C08J7/00; C08J7/04; C08J7/0427; C08J7/043; C08J7/048; C08J7/052; C08J2377/00; C08J2427/00; C08J2427/02; C08J2427/04; C08J2427/08; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31725; Y10T428/31739; Y10T428/31743; Y10T428/31746; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/3192
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
214 words
A nylon film coated with a vinylidene chloride copolymer, said film having been prepared by a process comprising: (a) coating the nylon film with an aqueous dispersion of a vinylidene chloride copolymer while keeping the nylon film under sufficient machine and transverse direction tensions to prevent curling, to form a primer-coated film, said vinyldiene chloride copolymer having a crystallinity index of less than 1.15, when dry, after 30 days' storage at 20° C., and a crystallinity index, when dry, between about 1.05 and 1.20 when stored for 48 hours at 40° C.; (b) drying the primer-coated film to remove substantially all of the water from the dispersion, while maintaining the primer-coated film under said machine and transverse direction tensions and at a drying rate sufficiently high to prevent curling of the primer-coated film; (c) coating the primer-coated film with an aqueous dispersion of a vinylidene chloride copolymer which, when dry, is capable of developing crystallinity to a level sufficient that the crystalline vinylidene chloride copolymer so-formed resists attack by an organic solvent, as measured by the Solvent Haze Test, said organic solvent being capable of dissolving vinylidene chloride copolymers having a crystallinity index of less than 1.05, to form a vinylidene chloride copolymer coated film; and (d) drying the vinylidene chloride copolymer coated film.
Claim 2
Dependent Claim
214 words
A nylon film coated with a vinylidene chloride copolymer, said film having been prepared by a process comprising: (a) coating the nylon film with an aqueous dispersion of a vinylidene chloride copolymer while keeping the nylon film under sufficient machine and transverse direction tensions to prevent curling, to form a primer-coated film, said vinyldiene chloride copolymer having a crystallinity index of less than 1.15, when dry, after 30 days' storage at 20° C., and a crystallinity index, when dry, between about 1.05 and 1.20 when stored for 48 hours at 40° C.; (b) drying the primer-coated film to remove substantially all of the water from the dispersion, while maintaining the primer-coated film under said machine and transverse direction tensions and at a drying rate sufficiently high to prevent curling of the primer-coated film; (c) coating the primer-coated film with an aqueous dispersion of a vinylidene chloride copolymer which, when dry, is capable of developing crystallinity to a level sufficient that the crystalline vinylidene chloride copolymer so-formed resists attack by an organic solvent, as measured by the Solvent Haze Test, said organic solvent being capable of dissolving vinylidene chloride copolymers having a crystallinity index of less than 1.05, to form a vinylidene chloride copolymer coated film; and (d) drying the vinylidene chloride copolymer coated film.
Claim 3
Dependent Claim
54 words
A film according to claim 1 in which the vinylidene chloride copolymer applied in step (a) has a crystallinity index, when dry, of between 1.0 and 1.05 when stored for 30 days at 20° C., and a crystallinity index, when dry, between about 1.05 and 1.20 when stored for 48 hours at 40° C.
Claim 4
Dependent Claim
38 words
A film according to claims 1 or 2 in which the vinylidene chloride copolymer applied in step (c) has sufficient crystallinity to be unaffected by acetone, ethyl acetate, methyl ethyl ketone or toluene in the Solvent Haze Test.
Claim 5
Dependent Claim
212 words
A process for coating nylon film with a vinylidene chloride copolymer, comprising: (a) coating the nylon film with an aqueous dispersion of vinylidene chloride copolymer while keeping the nylon film under sufficient machine and transverse direction tensions to prevent curling of the nylon film, to form a primer-coated film, said vinylidene chloride copolymer having a crystallinity index of less than 1.15, when dry, after 30 days' storage at 20° C., and a crystallinity index, when dry, of between about 1.05 and 1.20 when stored for 48 hours at 40° C.; (b) drying the primer-coated film to remove substantially all of the water from the dispersion, while maintaining the primer-coated film under said machine and transverse direction tensions and at a drying rate sufficiently high to prevent curling of the primer-coated film; (c) coating the primer-coated film with an aqueous dispersion of a vinylidene chloride copolymer which, when dry, is capable of developing crystallinity to a level sufficient that the crystalline vinylidene chloride copolymer so-formed resists attack by an organic solvent, as measured by the Solvent Haze Test, said organic solvent being capable of dissolving vinylidene chloride copolymers having a crystallinity index of less than 1.05, to form a vinylidene chloride copolymer coated film; and (d) drying the vinylidene chloride copolymer coated film.
Claim 6
Dependent Claim
212 words
A process for coating nylon film with a vinylidene chloride copolymer, comprising: (a) coating the nylon film with an aqueous dispersion of vinylidene chloride copolymer while keeping the nylon film under sufficient machine and transverse direction tensions to prevent curling of the nylon film, to form a primer-coated film, said vinylidene chloride copolymer having a crystallinity index of less than 1.15, when dry, after 30 days' storage at 20° C., and a crystallinity index, when dry, of between about 1.05 and 1.20 when stored for 48 hours at 40° C.; (b) drying the primer-coated film to remove substantially all of the water from the dispersion, while maintaining the primer-coated film under said machine and transverse direction tensions and at a drying rate sufficiently high to prevent curling of the primer-coated film; (c) coating the primer-coated film with an aqueous dispersion of a vinylidene chloride copolymer which, when dry, is capable of developing crystallinity to a level sufficient that the crystalline vinylidene chloride copolymer so-formed resists attack by an organic solvent, as measured by the Solvent Haze Test, said organic solvent being capable of dissolving vinylidene chloride copolymers having a crystallinity index of less than 1.05, to form a vinylidene chloride copolymer coated film; and (d) drying the vinylidene chloride copolymer coated film.
Claim 7
Dependent Claim
46 words
A process according to claim 1 in which the vinylidene chloride copolymer applied in step (a) has an amount of a low boiling alcohol sufficient to prevent foaming of the dispersion upon coating of the film, and to aid in the quick drying of step (b).
Claim 8
Dependent Claim
54 words
A process according to claim 1 in which the vinylidene chloride copolymer applied in step (a) has a crystallinity index, when dry, of between 1.0 and 1.05 when stored for 30 days at 20° C., and a crystallinity index, when dry, between about 1.05 and 1.20 when stored for 48 hours at 40° C.
Claim 9
Dependent Claim
40 words
A process according to claim 4 in which the vinylidene chloride copolymer applied during step (c) is capable of crystallizing to a crystallinity index, when dry, of 1.20 or higher, after storage of up to 24 days at 20° C.
Claim 10
Dependent Claim
26 words
A process according to claim 4 in which the vinylidene chloride copolymer dispersion applied during step (c) is applied using a low shear method of application.
Claim 11
Dependent Claim
26 words
A process according to claim 6 in which the vinylidene chloride copolymer dispersion applied during step (c) is applied using a low shear method of application.
Claim 12
Dependent Claim
28 words
A process according to claims 7, 8 or 9 in which the low shear method is selected from smooth roll, Meyer™ rod, offset gravure and reverse gravure methods.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-20 | 1987-09-19 | 1988-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-20 | 1991-09-19 | 1992-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-20 | 1995-09-19 | 1996-03-20 | $7700.00 | Window Closed / Lapsed |