Cobalt base alloy
Assignee: Hitachi Ltd
•
Filing: 1981-07-24
•
Granted: 1984-03-20
•
Expires: 2001-07-24
Abstract
Abstract A cobalt base alloy having a superior high-temperature strength and high-temperature ductility, containing, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% zirconium, less than 110% iron, less than 1% tantalum, less than 1% hafnium and remainder cobalt. At least one of 0.01 to 1 wt% titanium and 0.01 to 1 wt% (combined amount) rare earth elements is added to the alloy. The alloy is used as a casting and contains eutectic carbides and secondary carbides precipitated substantially uniformly in the grains. If the secondary carbides are formed by an age-treatment conducted at a higher temperature than that at which the alloy is actually used, the high-temperature strength and the high-temperature ductility of the alloy are remarkably improved. The cobalt base alloy is formed into gas turbine nozzles by a precision casting.
Inventors
- 👤 Yutaka Fukui
- 👤 Tetsuo Kashimura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:55
CPC Classifications
C; C22; C22C; C22C19/00; C22C19/07
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
158 words
A cobalt base cast alloy consisting essentially of, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, less than 10% iron, less than 1% tantalum, less than 1% hafnium and the remainder substantially cobalt, wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU2## and wherein there exist eutectic carbides and secondary carbides precipitated by an age-treatment in uniformly dispersed form in the vicinity of grain boundaries whereby growth of the secondary carbides is suppressed; said alloy having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 2
Dependent Claim
158 words
A cobalt base cast alloy consisting essentially of, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, less than 10% iron, less than 1% tantalum, less than 1% hafnium and the remainder substantially cobalt, wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU2## and wherein there exist eutectic carbides and secondary carbides precipitated by an age-treatment in uniformly dispersed form in the vicinity of grain boundaries whereby growth of the secondary carbides is suppressed; said alloy having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 3
Dependent Claim
22 words
A cobalt base cast alloy as claimed in claim 1, wherein the value determined by said equation is between 0.03 and 0.08.
Claim 4
Dependent Claim
166 words
A cobalt base cast alloy consisting essentially of by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, 0.01 to 1% (combined amount) rare earth elements, less than 10% iron, less than 1% tantalum, less than 1% hafnium and remainder substantially cobalt wherein there exist eutectic carbides and secondary carbides precipitated by an age-treatment in uniformly dispersed form in the vicinity of grain boundaries whereby growth of the secondary carbides is suppressed and wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected so as to satisfy the following equation: ##EQU3## said alloy having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 5
Dependent Claim
166 words
A cobalt base cast alloy consisting essentially of by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, 0.01 to 1% (combined amount) rare earth elements, less than 10% iron, less than 1% tantalum, less than 1% hafnium and remainder substantially cobalt wherein there exist eutectic carbides and secondary carbides precipitated by an age-treatment in uniformly dispersed form in the vicinity of grain boundaries whereby growth of the secondary carbides is suppressed and wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected so as to satisfy the following equation: ##EQU3## said alloy having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 6
Dependent Claim
32 words
A cobalt base cast alloy as claimed in claim 3, wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU4##
Claim 7
Dependent Claim
22 words
A cobalt base cast alloy as claimed in claim 1, wherein the value determined by said equation is between 0.03 and 0.08.
Claim 8
Dependent Claim
185 words
A cobalt base cast alloy in the form of a nozzle for a gas turbine, said gas turbine being produced by precision casting and made of a cobalt base alloy consisting essentially of, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, less than 1% tantalum, less than 1% hafnium, less than 10% iron and remainder substantially cobalt, wherein said cast alloy contains eutectic carbides and secondary carbides precipitated by an age-treatment and dispersed uniformly in the vicinity of the grain boundaries whereby growth of the secondary carbides is suppressed and wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU5## said alloy material having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 9
Dependent Claim
185 words
A cobalt base cast alloy in the form of a nozzle for a gas turbine, said gas turbine being produced by precision casting and made of a cobalt base alloy consisting essentially of, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, less than 1% tantalum, less than 1% hafnium, less than 10% iron and remainder substantially cobalt, wherein said cast alloy contains eutectic carbides and secondary carbides precipitated by an age-treatment and dispersed uniformly in the vicinity of the grain boundaries whereby growth of the secondary carbides is suppressed and wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU5## said alloy material having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 10
Dependent Claim
193 words
A cobalt base cast alloy in the form of a nozzle for a gas turbine, said gas turbine being produced by precision casting and made of a cobalt base alloy consisting essentially of, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, 0.01 to 1% (combined amount) rare earth elements, less than 10% iron, less than 1% tantalum, less than 1% hafnium and remainder substantially cobalt, wherein said cast alloy contains eutectic carbides and secondary carbides precipitated by an age-treatment and dispersed uniformly in the vicinity of the grain boundaries whereby growth of the secondary carbides is suppressed and wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU6## said alloy material having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 11
Dependent Claim
193 words
A cobalt base cast alloy in the form of a nozzle for a gas turbine, said gas turbine being produced by precision casting and made of a cobalt base alloy consisting essentially of, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, 0.01 to 1% (combined amount) rare earth elements, less than 10% iron, less than 1% tantalum, less than 1% hafnium and remainder substantially cobalt, wherein said cast alloy contains eutectic carbides and secondary carbides precipitated by an age-treatment and dispersed uniformly in the vicinity of the grain boundaries whereby growth of the secondary carbides is suppressed and wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU6## said alloy material having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 12
Dependent Claim
185 words
A cobalt base cast alloy consisting essentially of, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, less than 10% iron, less than 1% tantalum, less than 1% hafnium and the remainder substantially cobalt, wherein said cast alloy has been subjected to a solution heat treatment and then to an age-treatment conducted at a temperature higher than the temperature at which said alloy is actually used, and contains eutectic carbides and secondary carbides uniformly dispersed in the vicinity of the grain boundaries whereby growth of the secondary carbides is suppressed and wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU7## and alloy material having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 13
Dependent Claim
185 words
A cobalt base cast alloy consisting essentially of, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, less than 10% iron, less than 1% tantalum, less than 1% hafnium and the remainder substantially cobalt, wherein said cast alloy has been subjected to a solution heat treatment and then to an age-treatment conducted at a temperature higher than the temperature at which said alloy is actually used, and contains eutectic carbides and secondary carbides uniformly dispersed in the vicinity of the grain boundaries whereby growth of the secondary carbides is suppressed and wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU7## and alloy material having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 14
Dependent Claim
190 words
A cobalt base cast alloy consisting essentially of, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, 0.01 to 1% (combined amount) rare earth elements, less than 10% iron, less than 1% tantalum, less than 1% hafnium and remainder substantially cobalt, wherein said alloy has been subjected to a solution heat treatment and then to an age-treatment conducted at a higher temperature than that at which said alloy is actually used, and contains eutectic carbides and secondary carbides uniformly dispersed in the vicinity of the grain boundaries whereby growth of the secondary carbides is suppressed and wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU8## said alloy material having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 15
Dependent Claim
190 words
A cobalt base cast alloy consisting essentially of, by weight, 0.15 to 2% carbon, less than 2% silicon, less than 2% manganese, 5 to 15% nickel, 18 to 35% chromium, 3 to 15% tungsten, 0.003 to 0.1% boron, 0.01 to 1% niobium, 0.01 to 1% titanium, 0.01 to 1% zirconium, 0.01 to 1% (combined amount) rare earth elements, less than 10% iron, less than 1% tantalum, less than 1% hafnium and remainder substantially cobalt, wherein said alloy has been subjected to a solution heat treatment and then to an age-treatment conducted at a higher temperature than that at which said alloy is actually used, and contains eutectic carbides and secondary carbides uniformly dispersed in the vicinity of the grain boundaries whereby growth of the secondary carbides is suppressed and wherein the carbon (C), niobium (Nb), titanium (Ti) and zirconium (Zr) contents are so selected as to satisfy the following equation: ##EQU8## said alloy material having a creep rupture strength of higher than 4.3 Kg/mm 2 in 1,000 hours creep rupture at 982° C. and a reduction of area of at least 34% in 100 hours creep rupture at 982° C.
Claim 16
Dependent Claim
25 words
A cobalt base cast alloy as claimed in claim 8, wherein said cast alloy is formed into a gas turbine nozzle by a precision casting.
References Cited (Backward Citations)
US3582320A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-20 | 1987-09-19 | 1988-03-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-20 | 1991-09-19 | 1992-03-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-20 | 1995-09-19 | 1996-03-20 | $7700.00 | Window Closed / Lapsed |