Production of closed-cell polyurethane moldings having a densified surface zone
Assignee: BASF Polyurethanes GmbH
•
Filing: 1982-03-30
•
Granted: 1984-03-13
•
Expires: 2002-03-30
Abstract
Abstract A process for the preparation of moldings, in particular resilient elements, which by virtue of a densified surface zone with substantially closed cells, have only a low water absorption, wherein a mixture comprising: (a) 100 parts by weight of an NCO-containing prepolymer, having an NCO content of from 3 to 6% by weight and based on organic diisocyanates and substantially linear polyester-polyols or polytetramethylene ether glycol, (b) from 0.5 to 1.6 parts by weight of water, (c) one or more catalysts, preferably a tertiary amine, in an amount of from 0.01 to 2.0 parts by weight and (d) assistants, with or without additives, is reacted in a closed mold, while undergoing densification, the surface temperature of the inner wall of the mold being from 50° to 70° C.
Inventors
- 👤 Otmar Zipp
- 👤 Heinz Bollmann
- 👤 Herbert Stutz
- 👤 Wolfgang Scholz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:42
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/34; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/42; C08G18/4236; C08G18/4238; C08G18/48; C08G18/4854; C08G18/70; C08G18/72; C08G18/74; C08G18/76; C08G18/7657; C08G18/7678; C08J9/02; F; F16; F16F; F16F1/00; F16F1/36; F16F1/37; C08G2110/00; C08G2110/0033; C08G2110/0041; C08G2110/0066; C08G2110/0083; C08J2375/00; C08J2375/04; C08J2375/06
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
140 words
A process for the production of polyurethane moldings which have a densified surface zone and substantially closed cells by reacting organic polyisocyanates, polyols and water, wherein (a) 100 parts by weight of an NCO-containing prepolymer, having an NCO content from 3 to 6% by weight, said polymer being prepared by reacting organic diisocyanates and substantially linear polyester-polyols or polytetramethylene ether glycol and (b) 0.5 to 1.6 parts by weight of water are mixed thoroughly in the presence of (c) one or more catalysts (d) one or more surfactants, cell regulators, flameproofing agents, stabilizers, dyes, pigments, and fillers as assistants and/or additives, the resulting reaction mixture is introduced into a mold of which the inner wall has a surface temperature of from 50° C. to 70° C., the mold is closed and the mixture is allowed to harden whilst undergoing densification.
Claim 2
Dependent Claim
140 words
A process for the production of polyurethane moldings which have a densified surface zone and substantially closed cells by reacting organic polyisocyanates, polyols and water, wherein (a) 100 parts by weight of an NCO-containing prepolymer, having an NCO content from 3 to 6% by weight, said polymer being prepared by reacting organic diisocyanates and substantially linear polyester-polyols or polytetramethylene ether glycol and (b) 0.5 to 1.6 parts by weight of water are mixed thoroughly in the presence of (c) one or more catalysts (d) one or more surfactants, cell regulators, flameproofing agents, stabilizers, dyes, pigments, and fillers as assistants and/or additives, the resulting reaction mixture is introduced into a mold of which the inner wall has a surface temperature of from 50° C. to 70° C., the mold is closed and the mixture is allowed to harden whilst undergoing densification.
Claim 3
Dependent Claim
22 words
The process of claim 1, wherein a polyester-diol having an OH number from 20 to 225 is used to prepare the prepolymer.
Claim 4
Dependent Claim
13 words
The process of claim 1, wherein the organic diisocyanate used is 1,5-naphthylene diisocyanate.
Claim 5
Dependent Claim
13 words
The process of claim 1, wherein the catalyst used is a tertiary amine.
Claim 6
Dependent Claim
31 words
The process of claim 4, wherein the tertiary amine is used in an amount of from 0.01 to 2 parts by weight per 100 parts by weight of the NCO-containing prepolymer.
Claim 7
Dependent Claim
18 words
The process of claim 1, wherein the polyurethane molding has a density of from 250 to 800 g/liter.
Claim 8
Dependent Claim
13 words
The process of claim 1, wherein the polyurethane molding is a resilient element.
References Cited (Backward Citations)
US3042631A
Cited
FR1388551A
Cited
GB1120425A
Cited
GB1209243A
Cited
FR1599325A
Cited
FR2031632A5
Cited
US3632707A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-13 | 1987-09-12 | 1988-03-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-13 | 1991-09-12 | 1992-03-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-13 | 1995-09-12 | 1996-03-13 | $7700.00 | Window Closed / Lapsed |