Method of producing open-cell foamed articles of cross-linked polyolefins
Assignee: Sanwa Kako Co Ltd
•
Filing: 1982-03-12
•
Granted: 1984-03-06
•
Expires: 2002-03-12
Abstract
Abstract An open-cell foamed article of a cross-linked polyolefin having a high open-cell ratio and a high degree of expansion is produced by a method which comprises the steps of preparing a foamable and cross-linkable polyolefin composition, forming the composition into a desired shape maintaining its gel percent at zero, decomposing the cross-linking agent and blowing agent concurrently by heating the composition under atmospheric pressure in such conditions that the peak of the ratio of the degree of cross-linking to the degree of decomposition of the blowing agent is not more than 20 and exerting a mechanical deformation to the resulting polyolefin foam to rupture the cell membranes.
Inventors
- 👤 Hiroo Ito
- 👤 Takeo Kasanami
- 👤 Shuji Miura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:26
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/34; B29C44/3484; B29C44/56; B29C44/5627; B29C44/5636; C; C08; C08J; C08J9/00; C08J9/04; C08J9/06; C08J9/10; C08J9/36; C08J9/38; B29K; B29K2023/00; B29K2023/04; B29K2023/08; B29K2023/083; B29K2105/00; B29K2105/24; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10S264/13; Y10S264/18
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
262 words
A method for the production of open-cell foamed articles of cross-linked polyolefins comprising the steps of: blending with heating a polyolefin, a chemical blowing agent and a cross-linking agent to obtain a foamable and cross-linkable composition, forming the foamable and cross-linkable composition into a desired shape under pressure and at a temperature of from 115° to 155° C. and which is lower than the foaming temperature of said composition while maintaining its gel percent at zero, heating the shaped composition at a suitable foaming temperature under atmospheric pressure to decompose the cross-linking agent and the blowing agent concurrently, the peak of the ratio of the degree of cross-linking to the degree of decomposition of the blowing agent being not more than 20, thereby giving rise to a foamed product of cross-linked polyolefin having cells enclosed with very thin membranes capable of being easily ruptured by the action of mechanical force, and mechanically deforming said foamed product to cause the membranes of the cells to rupture; wherein the gel percent is the ratio of the foamable and cross-linkable composition after extraction to that before extraction, the extraction being carried out under reflux of trichloroethylene as a solvent for 24 hours by means of a soxhlet extractor using a glass filter of from 40 to 50μ; the degree of cross-linking is the gel percent of the composition at a given heating time and the degree of decompositon of the blowing agent is the ratio of the degree of expansion at said given heating time to the final degree of expansion of the foamed composition.
Claim 2
Independent Claim
262 words
A method for the production of open-cell foamed articles of cross-linked polyolefins comprising the steps of: blending with heating a polyolefin, a chemical blowing agent and a cross-linking agent to obtain a foamable and cross-linkable composition, forming the foamable and cross-linkable composition into a desired shape under pressure and at a temperature of from 115° to 155° C. and which is lower than the foaming temperature of said composition while maintaining its gel percent at zero, heating the shaped composition at a suitable foaming temperature under atmospheric pressure to decompose the cross-linking agent and the blowing agent concurrently, the peak of the ratio of the degree of cross-linking to the degree of decomposition of the blowing agent being not more than 20, thereby giving rise to a foamed product of cross-linked polyolefin having cells enclosed with very thin membranes capable of being easily ruptured by the action of mechanical force, and mechanically deforming said foamed product to cause the membranes of the cells to rupture; wherein the gel percent is the ratio of the foamable and cross-linkable composition after extraction to that before extraction, the extraction being carried out under reflux of trichloroethylene as a solvent for 24 hours by means of a soxhlet extractor using a glass filter of from 40 to 50μ; the degree of cross-linking is the gel percent of the composition at a given heating time and the degree of decompositon of the blowing agent is the ratio of the degree of expansion at said given heating time to the final degree of expansion of the foamed composition.
Claim 3
Dependent Claim
80 words
The method according to claim 1, wherein the decomposition of the cross-linking agent and blowing agent in the shaped composition is effected more concurrently by the two step heating; in the primary heating from 5 to 70% by weight of the blowing agent originally present in said composition being decomposed, and in the secondary heating the undecomposed blowing agent and cross-linking agent remaining in the primary foamed product being decomposed at a higher temperature than that in the primary heating.
Claim 4
Dependent Claim
52 words
The method according to claim 1 or 2, wherein the decomposition of the cross-linking agent and blowing agent in the shaped composition is effected by heating the composition in a bath selected from the group consisting of metal bath, oil bath and molten salt bath or in an atmosphere of nitrogen gas.
Claim 5
Dependent Claim
62 words
The method according to claim 1, wherein the shaped composition is placed in an openable mold which is not airtight and provided with a heater or a jacket through which a heating medium is circulated, and the decomposition of the cross-linking agent and blowing agent in the shaped composition is effected by the indirect heating with the heater or the heating medium.
Claim 6
Dependent Claim
24 words
The method according to claim 1, wherein the foaming temperature of the shaped composition falls within the range of from 145° to 210° C.
Claim 7
Dependent Claim
42 words
The method according to claim 2, wherein the foaming temperature of the shaped composition falls within the range of from 145° to 180° C. in the primary heating and within the range of from 170° to 210° C. in the secondary heating.
Claim 8
Dependent Claim
26 words
The method according to claim 1, wherein the shaping of the foamable and cross-linkable composition is effected by use of an extruder or a calendering roll.
Claim 9
Dependent Claim
25 words
The method according to claim 1, wherein the mechanical deformation is effected by means of compression exerted with two rolls rotated at an equal speed.
Claim 10
Dependent Claim
16 words
The method according to claim 1, wherein the foamable and cross-linkable composition contains a foaming aid.
Claim 11
Dependent Claim
34 words
The method according to claim 1, wherein the foamable and cross-linkable composition contains a compounding agent or filler, such as metal oxides, carbonates, fibrous filler materials, dyes, pigments, fluorescent materials and rubber compounding ingredients.
Claim 12
Dependent Claim
83 words
The method according to claim 1, wherein the polyolefin is selected from the group of high-density polyethylene, medium-density polyethylene, low-density polyethylene, poly-1,2-butadiene, ethylene-propylene copolymer, ethylene-butene copolymer, ethylene-vinyl acetate copolymer, copolymers of ethylene with up to 45% of methyl-, ethyl-, propyl- or butyl-acrylates or methacrylates, chlorinated products of the above homopolymers or copolymers having chlorine content of up to 60% by weight, mixtures of two or more of the above mentioned polymers, and mixtures of the above mentioned polymers with atactic or isotactic polypropylene.
Claim 13
Dependent Claim
25 words
The method according to claim 1, wherein the cross-linking agent is an organic peroxide having a decomposition temperature higher than the flow temperature of polyolefin.
Claim 14
Dependent Claim
39 words
The method according to claim 1, wherein the blowing agent is selected from the group of azo type compounds, nitroso type compounds, hydrazide type compounds and sulfonyl semicarbazide type compounds possessed decomposition temperatures exceeding the melting temperature of polyolefin.
References Cited (Backward Citations)
US3394214A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-03-06 | 1987-09-05 | 1988-03-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-03-06 | 1991-09-05 | 1992-03-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-03-06 | 1995-09-05 | 1996-03-06 | $7700.00 | Window Closed / Lapsed |