Abstract
Abstract An electrolyte for solid-state electrochemical cell comprising in solid state, a combination of lithium, phosphate and iodide and either calcium or aluminum moieties, the non-metallic moieties being in stoichiometric relationship with the metallic moieties. An advantageous electrolyte is prepared by reacting calcium iodide and lithium orthophosphate.
Inventors
- 👤 Ashok V. Joshi
- 👤 Arun D. Jatkar
- 👤 William P. Sholette
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 06:47
CPC Classifications
H; H01; H01M; H01M6/00; H01M6/14; H01M6/18
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
101 words
A solid state electrolyte for use in a solid-state electrochemical cell having a lithium anode comprised in mole percent of about 10 to about 50% iodine moiety, about 8 to about 47% lithium moiety, about 3% to about 16% phosphate moiety, up to about 38% oxygen moiety not inclusive of oxygen contained in the phosphate radical and about 5 to about 30% of at least one moiety selected from the group of calcium and aluminum moieties, said electrolyte being in the form of an interdiffused body of sources of said moieties and said moieties being in stoichiometric relationship metallic to non-metallic.
Claim 2
Dependent Claim
101 words
A solid state electrolyte for use in a solid-state electrochemical cell having a lithium anode comprised in mole percent of about 10 to about 50% iodine moiety, about 8 to about 47% lithium moiety, about 3% to about 16% phosphate moiety, up to about 38% oxygen moiety not inclusive of oxygen contained in the phosphate radical and about 5 to about 30% of at least one moiety selected from the group of calcium and aluminum moieties, said electrolyte being in the form of an interdiffused body of sources of said moieties and said moieties being in stoichiometric relationship metallic to non-metallic.
Claim 3
Dependent Claim
28 words
A solid-state electrolyte as in claim 1 which the moiety from the group of calcium and aluminum is calcium and the source of said moiety is calcium iodide.
Claim 4
Dependent Claim
30 words
A solid-state electrolyte as in claim 1 in which the moiety from the group of calcium and aluminum is aluminum and the source of said moiety is lithium aluminum iodide.
Claim 5
Dependent Claim
39 words
A solid-state electrolyte as in claim 1 which consists of, in mole percentages, about 25% to 43% lithium moiety, about 8% to 14.5% phosphate moiety, about 14% to 23% calcium moiety and about 28% to about 45% iodine moiety.
Claim 6
Dependent Claim
30 words
A solid-state electrolyte as in claim 4 which consists, in mole percent, of about 31.3% lithium moiety, about 10.4% phosphate moiety, about 19.4% calcium moiety and about 38.8% iodine moiety.
Claim 7
Dependent Claim
27 words
A solid state electrolyte as in claim 4 containing some in situ produced calcium orthophosphate formed in accordance with the relationship 2Li.sub.3 PO.sub.4 +3CaI.sub.2 ⃡Ca.sub.3 (PO.sub.4).sub.2 +6LiI.
Claim 8
Dependent Claim
18 words
A solid-state electrochemical cell having a lithium anode, a cathode and an electrolyte as defined in claim 1.
Claim 9
Dependent Claim
107 words
A process for producing a novel electrolyte for use in solid-state electrochemical cells comprising interdiffusing quantities of lithium orthophosphate, one or both of the group of calcium iodide and aluminum iodide and, optionally, one or more of aluminum oxide and lithium iodide to provide an interdiffused composition containing, in mole percent, about 10% to about 50% iodine moiety, about 8 to about 47% lithium moiety, about 3% to about 16% phosphate moiety, up to about 38% oxygen moiety not inclusive of oxygen contained in the phosphate radical and about 5 to about 30% of at least one moiety selected from the group of calcium and aluminum moieties.
Claim 10
Dependent Claim
107 words
A process for producing a novel electrolyte for use in solid-state electrochemical cells comprising interdiffusing quantities of lithium orthophosphate, one or both of the group of calcium iodide and aluminum iodide and, optionally, one or more of aluminum oxide and lithium iodide to provide an interdiffused composition containing, in mole percent, about 10% to about 50% iodine moiety, about 8 to about 47% lithium moiety, about 3% to about 16% phosphate moiety, up to about 38% oxygen moiety not inclusive of oxygen contained in the phosphate radical and about 5 to about 30% of at least one moiety selected from the group of calcium and aluminum moieties.
Claim 11
Dependent Claim
14 words
A process as in claim 8 wherein calcium iodide and lithium orthophosphate are interdiffused.
Claim 12
Dependent Claim
41 words
A process as in claim 9 wherein the resultant interdiffused composition contains, in mole percent, about 25% to 43% lithium moiety, about 8% to 14.5% phosphate moiety, about 14% to 23% calcium moiety and about 28% to about 45% iodine moiety.
Claim 13
Dependent Claim
16 words
A process as in claim 8 wherein lithium orthophosphate lithium iodide and aluminum iodide are interdiffused.
Claim 14
Dependent Claim
40 words
A process as in claim 8 wherein the interdiffusion takes place at a temperature in excess of the melting point of the lowest melting ingredient but below that temperature at which all ingredients melt for up to about 2 hours.
Claim 15
Dependent Claim
31 words
A process as in claim 10 wherein the interdiffused composition contains, in mole percent, about 31.3% lithium moiety, about 10.4% phosphate moiety, about 19.4% calcium moiety and about 38.8% iodine moiety.
References Cited (Backward Citations)
US3837920A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-27 | 1987-08-29 | 1988-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-27 | 1991-08-29 | 1992-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-27 | 1995-08-29 | 1996-02-28 | $7700.00 | Window Closed / Lapsed |