US4434215A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Battery separator
Assignee: WR Grace and Co Conn
•
Filing: 1982-09-02
•
Granted: 1984-02-28
•
Expires: 2002-09-02
Abstract
Abstract A composition suitable for use as a battery separator comprising a substantially homogeneous mixture of a copolymer of ethylene and acrylic acid having from 10 to 23 mole percent acrylic acid therein and a melt index of from about 0.1 to 5 in combination with a copolymer of ethylene and acrylic acid having at least 25 mole percent acrylic acid therein and having a melt index of at least about 10. The present invention is further directed to a process of forming a sheet product from the subject composition and the use of the formed product as a battery separator.
Inventors
- 👤 Walter R. Wszolek
- 👤 Joseph T. Lundquist, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:21
CPC Classifications
H; H01; H01M; H01M50/00; H01M50/40; H01M50/46; C; C08; C08L; C08L23/00; C08L23/02; C08L23/04; C08L23/08; C08L23/0846; C08L23/0869; C08L23/0876; H01M50/409; H01M50/411; H01M50/414; H01M50/417; H01M50/489; C08L2205/00; C08L2205/02; H01M2300/00; H01M2300/0002; H01M2300/0014; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
126 words
A composition suitable for forming a battery separator sheet product comprising a mixture of (a) a copolymer of ethylene and acrylic acid or methacrylic acid, said acid substantially neutralized with an alkali or alkaline earth metal cation and said copolymer having from 10 to 23 mole percent of said acid therein and having a standard load melt index of from 0 to 5; and (b) a copolymer of ethylene and acrylic acid or methacrylic acid, said acid substantially neutralized with an alkali or alkaline earth metal cation and said copolymer having at least about 25 mole percent of acrylic acid therein and having a standard load melt index of from about 10 to 100; the weight ratio of (a) to (b) being from 0.3 to 2.
Claim 2
Dependent Claim
126 words
A composition suitable for forming a battery separator sheet product comprising a mixture of (a) a copolymer of ethylene and acrylic acid or methacrylic acid, said acid substantially neutralized with an alkali or alkaline earth metal cation and said copolymer having from 10 to 23 mole percent of said acid therein and having a standard load melt index of from 0 to 5; and (b) a copolymer of ethylene and acrylic acid or methacrylic acid, said acid substantially neutralized with an alkali or alkaline earth metal cation and said copolymer having at least about 25 mole percent of acrylic acid therein and having a standard load melt index of from about 10 to 100; the weight ratio of (a) to (b) being from 0.3 to 2.
Claim 3
Dependent Claim
15 words
The composition of claim 1 wherein the copolymers are each substantially neutralized with potassium cation.
Claim 4
Dependent Claim
63 words
The composition of claim 1 wherein copolymer (a) contains from 15 to 23 mole percent of acrylic acid based on said copolymer and has a standard load melt index of from 0.1 to 1 and copolymer (b) contains from 25 to 35 mole percent of acrylic acid based on said copolymer and has a standard load melt index of from 10 to 20.
Claim 5
Dependent Claim
20 words
A sheet product of from 0.5 to 10 mils thickness formed from the composition of claims 1, 2 or 3.
Claim 6
Dependent Claim
47 words
In a battery having an electrolyte, at least one pair of a positive and a negative electrodes and a separator membrane between each adjacent positive and negative electrodes, the improvement comprising having said separator membrane formed from at least one sheet of the product of claim 4.
Claim 7
Dependent Claim
135 words
In a battery having an electrolyte, at least one pair of a positive and a negative electrodes and a separator membrane positioned between adjacent positive and negative electrodes, wherein the improvement comprises having each said separator membranes of less than 10 mils thick and being a laminate product of (1) a sheet formed from an admixture of from 7 to 30 weight percent polyolefin having an average molecular weight of at least 100,000; from 0 to 15 weight percent plasticizer; and from 50 to 93 weight percent of a filler selected from titania, alumina, magnesium hydroxide or calcium hydroxide, said filler having a surface area of from 100 to 385 m 2 /cc and a pore volume of at least 0.075 cc/gm and (2) at least one sheet material of claim 1, 2, or 3.
Claim 8
Dependent Claim
37 words
The battery of claim 6 wherein filler of sheet (1) of the laminate is titania having a surface area of from 125 to 385 m 2 /cc and a pore volume of from 0.08 to 0.8 cc/gm.
Claim 9
Dependent Claim
35 words
The battery of claim 6 wherein the sheet (1) of the laminate further contains up to 10 weight percent of a conductive carbon black having a surface area of at least 100 m 2 /cc.
References Cited (Backward Citations)
US3427206A
Cited
US3615865A
Cited
US3892594A
Cited
US3928497A
Cited
US4230549A
Cited
US4287276A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-27 | 1987-08-29 | 1988-02-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-27 | 1991-08-29 | 1992-02-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-27 | 1995-08-29 | 1996-02-28 | $7700.00 | Window Closed / Lapsed |