Method of preparing crystalline zeolite

Claim 1

A method for preparing a synthetic crystalline zeolite material consisting essentially of ZSM-5 and an unidentified crystalline material having the X-ray diffraction pattern of Table II and having a constraint index between 1 and 12 and a SiO 2 /Al 2 O 3 ratio greater than 5 which comprises preparing a reaction mixture containing a source of an alkali metal oxide, an oxide of silicon, optionally an oxide of aluminum, R 2 O, and water, and having a composition, in terms of mole ratios of oxides, falling within the following ranges: SiO 2 /Al 2 O 3 =10 to ∞ M 2 O/SiO 2 =0.01 to 3.0 R 2 O/M 2 O=0.01 to 2.0 OH/SiO 2 =0 to 1.0 wherein M is an alkali or alkaline earth metal and R 2 O is an organic nitrogen-N-oxide selected from the group consisting of 4-picoline-N-oxide and a trialkyl-amine-N-oxide wherein the alkyl group comprises C 2 -C 5 hydrocarbons and maintaining said mixture under crystallization conditions until crystals of said zeolite material are formed.

Claim 2

A method for preparing a synthetic crystalline zeolite material consisting essentially of ZSM-5 and an unidentified crystalline material having the X-ray diffraction pattern of Table II and having a constraint index between 1 and 12 and a SiO 2 /Al 2 O 3 ratio greater than 5 which comprises preparing a reaction mixture containing a source of an alkali metal oxide, an oxide of silicon, optionally an oxide of aluminum, R 2 O, and water, and having a composition, in terms of mole ratios of oxides, falling within the following ranges: SiO 2 /Al 2 O 3 =10 to ∞ M 2 O/SiO 2 =0.01 to 3.0 R 2 O/M 2 O=0.01 to 2.0 OH/SiO 2 =0 to 1.0 wherein M is an alkali or alkaline earth metal and R 2 O is an organic nitrogen-N-oxide selected from the group consisting of 4-picoline-N-oxide and a trialkyl-amine-N-oxide wherein the alkyl group comprises C 2 -C 5 hydrocarbons and maintaining said mixture under crystallization conditions until crystals of said zeolite material are formed.

Claim 4

A method of preparing in situ a catalyst composition consisting essentially of a ZSM-5 zeolite in an inorganic oxide binder which comprises: (a) preparing a reaction mixture containing a source of an alkali metal oxide, an oxide of silicon, optionally an oxide of aluminum, R 2 O, and water, and having a composition, in terms of mole ratios of oxides, falling within the following ranges: SiO 2 /Al 2 O 3 =10 to ∞ M 2 O/SiO 2 =0.01 to 3.0 R 2 O/M 2 O=0.01 to 2.0 OH/SiO 2 =0 to 1.0 wherein M is an alkali or alkaline earth metal and R 2 O is an organic nitrogen-n-oxide selected from the group consisting of 4-picoline-N-oxide and a trialkyl-amine-N-oxide wherein the alkyl group comprises C 2 -C 5 hydrocarbons, (b) maintaining said mixture under crystallization conditions until crystals consisting essentially of ZSM-5 and an unidentified crystalline material having the X-ray diffraction pattern of Table II are formed, and (c) subjecting said crystals to thermal treatment effective to cause the unidentified crystalline material to collapse forming an inorganic oxide binder for the ZSM-5.

Claim 5

A method of preparing in situ a catalyst composition consisting essentially of a ZSM-5 zeolite in an inorganic oxide binder which comprises: (a) preparing a reaction mixture containing a source of an alkali metal oxide, an oxide of silicon, optionally an oxide of aluminum, R 2 O, and water, and having a composition, in terms of mole ratios of oxides, falling within the following ranges: SiO 2 /Al 2 O 3 =10 to ∞ M 2 O/SiO 2 =0.01 to 3.0 R 2 O/M 2 O=0.01 to 2.0 OH/SiO 2 =0 to 1.0 wherein M is an alkali or alkaline earth metal and R 2 O is an organic nitrogen-n-oxide selected from the group consisting of 4-picoline-N-oxide and a trialkyl-amine-N-oxide wherein the alkyl group comprises C 2 -C 5 hydrocarbons, (b) maintaining said mixture under crystallization conditions until crystals consisting essentially of ZSM-5 and an unidentified crystalline material having the X-ray diffraction pattern of Table II are formed, and (c) subjecting said crystals to thermal treatment effective to cause the unidentified crystalline material to collapse forming an inorganic oxide binder for the ZSM-5.