US4430150A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Production of single crystal semiconductors
Assignee: Spheral Solar Power Inc
•
Filing: 1981-08-07
•
Granted: 1984-02-07
•
Expires: 2001-08-07
Abstract
Abstract Polycrystalline semiconductor material is treated to form a skin of a thermally stable substance and melted with the molten material retained by the film. Upon cooling, the material solidifies as single crystal and the skin is removed.
Inventors
- 👤 Jules D. Levine
- 👤 William R. McKee
- 👤 Kent R. Carson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 04:40
CPC Classifications
C; C30; C30B; C30B11/00; C30B11/002; C30B29/00; C30B29/60
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
60 words
The method comprising: (a) treating a polycrystalline semiconductor material in a reactive gaseous environment to form a skin thereon of a thermally stable compound; (b) thereafter melting the material within said skin while in said gaseous environment with the molten material retained within said skin; and (c) cooling the material to form a solid single crystal body within said skin.
Claim 2
Independent Claim
60 words
The method comprising: (a) treating a polycrystalline semiconductor material in a reactive gaseous environment to form a skin thereon of a thermally stable compound; (b) thereafter melting the material within said skin while in said gaseous environment with the molten material retained within said skin; and (c) cooling the material to form a solid single crystal body within said skin.
Claim 3
Dependent Claim
19 words
The method of claim 1 wherein said material is one of the class comprising silicon, germanium and gallium arsenide.
Claim 4
Dependent Claim
17 words
The method of claim 1 wherein said material is silicon and said environment is an oxidizing gas.
Claim 5
Dependent Claim
21 words
The method of claim 1 wherein said material is germanium and said environment is a gaseous atmosphere of silane and ammonia.
Claim 6
Dependent Claim
20 words
The method of claim 1 wherein said material is gallium arsenide and the skin is formed by chemical vapor deposition.
Claim 7
Independent Claim
106 words
A method for producing particles of single crystal semiconductor material from irregular particles of polycrystalline material, comprising the steps of: (a) heating said polycrystalline particles to a temperature below the melting point thereof in an environment containing a reactive gas capable of growth of a coating over the surface of each particle; (b) heating said polycrystalline materials inside each said coating to a temperature above the melting point of said crystalline material in the presence of a reactive gas which maintains the integrity of said coating; and (c) cooling the particles to allow the molten material to solidify in a single crystal structure within said coating.
Claim 8
Independent Claim
106 words
A method for producing particles of single crystal semiconductor material from irregular particles of polycrystalline material, comprising the steps of: (a) heating said polycrystalline particles to a temperature below the melting point thereof in an environment containing a reactive gas capable of growth of a coating over the surface of each particle; (b) heating said polycrystalline materials inside each said coating to a temperature above the melting point of said crystalline material in the presence of a reactive gas which maintains the integrity of said coating; and (c) cooling the particles to allow the molten material to solidify in a single crystal structure within said coating.
Claim 9
Dependent Claim
24 words
The method set forth in claim 6, wherein polycrystalline particles of silicon are heated in an oxygen environment, to grow a silicon dioxide skin.
Claim 10
Dependent Claim
26 words
The method set forth in claim 6, wherein polycrystalline particles of silicon are heated in a nitrogen containing gas environment, to grow a silicon nitride skin.
Claim 11
Dependent Claim
27 words
The method set forth in claim 6, wherein polycrystalline particles of silicon are heated in a carbon containing gas environment to grow a skin of silicon carbide.
Claim 12
Independent Claim
116 words
The method of producing particles of single crystal silicon from the particles of polycrystalline silicon, comprising the steps of: (a) heating said polycrystalline silicon particles to a temperature below 1410° C. in an environment containing a reactive gas for growth of a silicon compound coating over the surface of each particle; (b) heating the materials inside said coatings to a temperature above 1410° C. to melt said materials in the presence of a reactive gas to maintain the integrity of said coating; (c) cooling the particles to allow the molten silicon to solidify in a single crystal structure within said coating; and (d) annealing said particles for removal of contaminants in the material inside said skin.
Claim 13
Independent Claim
116 words
The method of producing particles of single crystal silicon from the particles of polycrystalline silicon, comprising the steps of: (a) heating said polycrystalline silicon particles to a temperature below 1410° C. in an environment containing a reactive gas for growth of a silicon compound coating over the surface of each particle; (b) heating the materials inside said coatings to a temperature above 1410° C. to melt said materials in the presence of a reactive gas to maintain the integrity of said coating; (c) cooling the particles to allow the molten silicon to solidify in a single crystal structure within said coating; and (d) annealing said particles for removal of contaminants in the material inside said skin.
Claim 14
Dependent Claim
22 words
The method as recited in claim 10, wherein the particles are heated in an oxygen environment to grow a silicon dioxide skin.
Claim 15
Independent Claim
134 words
A method of producing particles of single crystal silicon from particles of polycrystalline silicon, comprising the steps of: (a) exposing said particles to a mixture of a carrier gas and hydrogen chloride gas at an elevated temperature below the melting point of silicon to clean the surfaces of said particles; (b) elevating the temperature of the cleaned particles to slightly below 1410° C. in a gaseous environment containing oxygen which will react to grow a continuous silicon dioxide coating over the surface of each said particle; (c) thereafter further elevating the temperature of said particles in the presence of a reactive gas to melt the polysilicon material inside the coating of each said particle; and (d) cooling the particles to allow the molten silicon to solidify in a single crystal structure within said coating.
Claim 16
Independent Claim
134 words
A method of producing particles of single crystal silicon from particles of polycrystalline silicon, comprising the steps of: (a) exposing said particles to a mixture of a carrier gas and hydrogen chloride gas at an elevated temperature below the melting point of silicon to clean the surfaces of said particles; (b) elevating the temperature of the cleaned particles to slightly below 1410° C. in a gaseous environment containing oxygen which will react to grow a continuous silicon dioxide coating over the surface of each said particle; (c) thereafter further elevating the temperature of said particles in the presence of a reactive gas to melt the polysilicon material inside the coating of each said particle; and (d) cooling the particles to allow the molten silicon to solidify in a single crystal structure within said coating.
Claim 17
Dependent Claim
23 words
The method set forth in claim 12, wherein the polycrystalline particles are heated in an oxygen environment, to grow a silicon dioxide skin.
Claim 18
Dependent Claim
24 words
The method set forth in claim 12, wherein the polycrystalline particles are heated in a nitrogen containing environment, to grow a silicon nitride skin.
Claim 19
Dependent Claim
25 words
The method set forth in claim 12, wherein the polycrystalline particles are heated in a carbon containing gas environment to grow a silicon carbide skin.
Claim 20
Independent Claim
107 words
A method of producing particles of single crystal silicon from particles of polycrystalline silicon, comprising the steps of: (a) oxidizing the polysilicon particles by heating at about 1380° C. in an environment containing oxygen for about 3 minutes to grow a continuous silicon dioxide coating over the surface of each particle; (b) elevating the temperature of the polycrystalline materials inside the coating of each said particle to about 1430° C. for about 2 minutes while in said oxygen environment; and (c) cooling the particles to about 1380° C. for about 10 minutes to allow the molten silicon to solidify in a single crystal structure within said coating.
Claim 21
Independent Claim
107 words
A method of producing particles of single crystal silicon from particles of polycrystalline silicon, comprising the steps of: (a) oxidizing the polysilicon particles by heating at about 1380° C. in an environment containing oxygen for about 3 minutes to grow a continuous silicon dioxide coating over the surface of each particle; (b) elevating the temperature of the polycrystalline materials inside the coating of each said particle to about 1430° C. for about 2 minutes while in said oxygen environment; and (c) cooling the particles to about 1380° C. for about 10 minutes to allow the molten silicon to solidify in a single crystal structure within said coating.
Claim 22
Dependent Claim
35 words
The method set forth in claim 16, wherein the particles are thereafter annealed at a temperature of about 1250° C. for a period of several hours to remove dissolved oxygen from the single crystal particles.
References Cited (Backward Citations)
US3998659A
Cited
US4033792A
Cited
US4040849A
Cited
US4298423A
Cited
US4188177A
Cited
US4377605A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-02-06 | 1987-08-08 | 1988-02-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-02-06 | 1991-08-08 | 1992-02-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-02-06 | 1995-08-08 | 1996-02-07 | $7700.00 | Window Closed / Lapsed |