Method and apparatus for forming electrically conductive transparent oxide
Assignee: Balzers und Leybold Deutschland Holding AG
•
Filing: 1982-03-26
•
Granted: 1984-01-31
•
Expires: 2002-03-26
Abstract
Abstract The invention concerns a method of and apparatus for forming electrically conductive transparent oxide coatings on water-containing substrates by magnetic-field reinforced cathodic atomization of a target hot-pressed from powdered oxide ceramic materials. The coatings formed have electrical conductivity. When the atomization process is carried out using direct-current voltages of between 150 and 600 volts and a power density of 3 to 15 and preferably 5 to 10 watts/cm 2 , the degree of pressing of the target is at least 75% of the density of the solid material and the atomization atmosphere is maintained at between 1×10 -3 and 5×10 -2 mbars with a composition of 2 to 20% oxygen, 40 to 70% hydrogen, and the remainder argon. Based upon the speed of travel of the web, a thickness of coating of between 10 and 100 mm and a specific resistance of between 100 and 10,000 μΩcm are achieved.
Inventors
- 👤 Klaus J. Heimbach
- 👤 Wolf-Dieter Munz
- 👤 Rolf Adam
- 👤 Heinz Wenzl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:46
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C23C14/35; C23C14/0021; C23C14/0036; C23C14/0068
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
150 words
A method of producing electrically-conductive, transparent oxide coatings on a water-containing substrate by magnetic-field reinforced cathodic atomization thereonto of a targer hot-pressed from powdered oxide ceramic material selected from the group consisting of indium oxide/tin oxide mixtures, cadmium oxide/tin oxide mixtures and tin oxide, comprising: (a) atomizing the target with a direct-current voltage of between 150 and 600 volts, (b) adjusting the power density of the target atomization to from 3 to 15 watt/cm 2 of the target surface, (c) providing the target with a degree of pressing providing at least 75% of the density of solid material the same as the target powder, and (d) providing an atomization atmosphere at a pressure of from 1×10 -3 to 5×10 -2 mbars, by the controlled introduction of argon, hydrogen and oxygen in a composition which comprises from 2 to 20% of oxygen, 40 to 70% of hydrogen and the rest argon.
Claim 2
Independent Claim
150 words
A method of producing electrically-conductive, transparent oxide coatings on a water-containing substrate by magnetic-field reinforced cathodic atomization thereonto of a targer hot-pressed from powdered oxide ceramic material selected from the group consisting of indium oxide/tin oxide mixtures, cadmium oxide/tin oxide mixtures and tin oxide, comprising: (a) atomizing the target with a direct-current voltage of between 150 and 600 volts, (b) adjusting the power density of the target atomization to from 3 to 15 watt/cm 2 of the target surface, (c) providing the target with a degree of pressing providing at least 75% of the density of solid material the same as the target powder, and (d) providing an atomization atmosphere at a pressure of from 1×10 -3 to 5×10 -2 mbars, by the controlled introduction of argon, hydrogen and oxygen in a composition which comprises from 2 to 20% of oxygen, 40 to 70% of hydrogen and the rest argon.
Claim 3
Dependent Claim
50 words
The method of claim 1, wherein the substrate is web moving past the target, and further comprising: controlling the speed of movement of the web past the target to provide an atomization coating thereon of from 10 to 100 nm thickness and of from 100 to 10,000 μΩ cm resistance.
Claim 4
Dependent Claim
26 words
The method according to claim 2, wherein providing the atomization atmosphere comprises providing the oxygen in a concentration just sufficient to prevent visible deposition of metal.
Claim 5
Dependent Claim
55 words
The method according to claim 2, wherein providing the atomization atmosphere comprises providing the hydrogen in a concentration sufficient relative to the rate of travel of the web that an increase in the pressure of the atomization atmosphere by the release of water vapor from the substrate under the affect of the atomization is prevented.
Claim 6
Dependent Claim
60 words
The method of claim 2 wherein the atomization of the target onto the substrate defines a coating zone, and further comprising providing a plate-like screen (5) between the web (1) and the target (3) having an opening (6) which is appreciably smaller than the extent of the coating zone (7) in directions parallel with the surface (4) of the target.
References Cited (Backward Citations)
US3884787A
Cited
US4113599A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-30 | 1987-08-01 | 1988-01-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-30 | 1991-08-01 | 1992-01-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-30 | 1995-08-01 | 1996-01-31 | $7700.00 | Window Closed / Lapsed |