US4427716A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for predetermining peel strength at copper/aluminum interface
Assignee: General Electric Co
•
Filing: 1983-01-21
•
Granted: 1984-01-24
•
Expires: 2003-01-21
Abstract
Abstract A method is disclosed for predetermining the magnitude of the average release peel strength at the interface between a vapor deposited copper film and a flexible aluminum carrier sheet to which the copper has been previously directly applied. The resulting copper-to-aluminum adherence is due to the formation of a preferential diffusion bond.
Inventors
- 👤 Erwin G. Siwek
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 12:42
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/06; C23C14/14; C23C14/16; C23C14/58; C23C14/5806; C23C14/5893; H; H05; H05K; H05K3/00; H05K3/02; H05K3/022; H05K3/025
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
195 words
A method for developing a bond between contiguous metallic laminae having a predetermined average unit magnitude, said method comprising the steps of: (a) forming a copper film on a flexible aluminum carrier sheet to produce a laminate by applying copper directly on a major surface of said aluminum sheet by vapor deposition with the crystals of said copper film being predominately columnar in configuration, the yield strength of said aluminum sheet being significantly in excess of 10,000 psi and said surface being free from hydrocarbon contamination to an extent at least comparable to being in "chemically clean" condition at the time of such vapor deposition; (b) heating said laminate in a protective atmosphere at a temperature in excess of about 150° C. for a preset time sufficient to develop a diffusion bond between said copper film and said aluminum sheet requiring a force of between about 0.2 and 2.0 pounds per lineal inch to peel said aluminum sheet from said copper film, the maximum heating exposure being such as not to reduce the yield strength of said aluminum sheet below about 10,000 psi and (c) cooling said laminate to room temperature in a protective atmosphere.
Claim 2
Independent Claim
195 words
A method for developing a bond between contiguous metallic laminae having a predetermined average unit magnitude, said method comprising the steps of: (a) forming a copper film on a flexible aluminum carrier sheet to produce a laminate by applying copper directly on a major surface of said aluminum sheet by vapor deposition with the crystals of said copper film being predominately columnar in configuration, the yield strength of said aluminum sheet being significantly in excess of 10,000 psi and said surface being free from hydrocarbon contamination to an extent at least comparable to being in "chemically clean" condition at the time of such vapor deposition; (b) heating said laminate in a protective atmosphere at a temperature in excess of about 150° C. for a preset time sufficient to develop a diffusion bond between said copper film and said aluminum sheet requiring a force of between about 0.2 and 2.0 pounds per lineal inch to peel said aluminum sheet from said copper film, the maximum heating exposure being such as not to reduce the yield strength of said aluminum sheet below about 10,000 psi and (c) cooling said laminate to room temperature in a protective atmosphere.
Claim 3
Dependent Claim
27 words
The method of claim 1 wherein the protective atmosphere used is selected from the group consisting of vacuum, helium gas, argon gas, hydrogen gas and nitrogen gas.
Claim 4
Dependent Claim
22 words
The method of claim 2 wherein an oxygen content of less than 1 percent by volume prevails in the protective atmosphere employed.
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein the peel strength of the laminate is between about 0.4 and 1.0 pounds per lineal inch.
Claim 6
Dependent Claim
48 words
The method of claim 1 including, after the step of forming the copper film on the aluminum sheet, the step of depositing a layer of an oxide of a second metal over said copper film under conditions of temperature and pressure substantially precluding the formation of copper oxide.
Claim 7
Dependent Claim
34 words
The method of claim 5 wherein the heating is conducted in a protective atmosphere selected from the group consisting of (a) vacuum of less than about 2 inches of mercury and (b) reducing gas.
Claim 8
Dependent Claim
11 words
The method of claim 6 wherein the protective atmosphere is hydrogen.
Claim 9
Dependent Claim
21 words
The method of claim 1 wherein the temperature during the heating step is in the range of 200° to 300° C.
Claim 10
Dependent Claim
18 words
The method of claim 1 wherein the heating and cooling steps are conducted in the same protective atmosphere.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-23 | 1987-07-25 | 1988-01-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-23 | 1991-07-25 | 1992-01-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-23 | 1995-07-25 | 1996-01-24 | $7700.00 | Window Closed / Lapsed |