Copper alloy having high electrical conductivity and high mechanical characteristics

Claim 2

A copper alloy consisting essentially of 0.1 to 0.50% by weight of cobalt, 0.04 to 0.25% by weight of phosphorus, the remainder being copper, said cobalt and phosphorus being present in a weight ratio of cobalt to phosphorus of between 2.5 to 5, said alloy having a high electrical conductivity of at least 75% IACS; and said alloy, when subjected to thermal-mechanical treatment having a hardness of at least about 90 HV.

Claim 3

The alloy of claim 1, wherein the amounts of cobalt and phosphorus are as follows: 0.15 to 0.35% by weight of cobalt; 0.05 to 0.12% by weight of phosphorus.

Claim 4

A copper alloy consisting essentially of: 0.10 to 0.4% by weight of cobalt, 0.04 to 0.25% by weight of phosphorus, and up to 0.15% by weight of nickel and/or iron, the nickel content not being higher than 0.05% and the iron content not being higher than 0.01% and the remainder being copper, wherein the weight percentages of Ni, Co, Fe and P are chosen so that the ratio of the weight of Ni+Co+Fe to the weight of phosphorus is between 2.5 and 5, said alloy having a high electrical conductivity of at least 75% IACS, and said alloy, when subjected to thermal-mechanical treatment, having a hardness of at least about 90 HV.

Claim 5

A copper alloy consisting essentially of: 0.10 to 0.4% by weight of cobalt, 0.04 to 0.25% by weight of phosphorus, and up to 0.15% by weight of nickel and/or iron, the nickel content not being higher than 0.05% and the iron content not being higher than 0.01% and the remainder being copper, wherein the weight percentages of Ni, Co, Fe and P are chosen so that the ratio of the weight of Ni+Co+Fe to the weight of phosphorus is between 2.5 and 5, said alloy having a high electrical conductivity of at least 75% IACS, and said alloy, when subjected to thermal-mechanical treatment, having a hardness of at least about 90 HV.

Claim 6

A copper alloy consisting essentially of: 0.10 to 0.50% by weight of cobalt, 0.04 to 0.25% by weight of phosphorus, and at least one element selected from the group consisting of Mg, Cd, Ag, Zn and Sn, the remainder being copper, the weight percentage of said element, when present, being 0.01 to 0.35 Mg, 0.01 to 0.7 Cd, 0.01 to 0.35 Ag, 0.01 to 0.7 Zn and 0.01 to 0.25 Sn the total content of said elements not exceeding 1% by weight, said cobalt and phosphorus being present in a weight ratio of cobalt to phosphorus of between 2.5 to 5, said alloy having a high electrical conductivity of at least 75% IACS; and said alloy, when subjected to thermal-mechanical treatment, having a hardness of at least about 90 HV.

Claim 7

A copper alloy consisting essentially of: 0.10 to 0.50% by weight of cobalt, 0.04 to 0.25% by weight of phosphorus, and at least one element selected from the group consisting of Mg, Cd, Ag, Zn and Sn, the remainder being copper, the weight percentage of said element, when present, being 0.01 to 0.35 Mg, 0.01 to 0.7 Cd, 0.01 to 0.35 Ag, 0.01 to 0.7 Zn and 0.01 to 0.25 Sn the total content of said elements not exceeding 1% by weight, said cobalt and phosphorus being present in a weight ratio of cobalt to phosphorus of between 2.5 to 5, said alloy having a high electrical conductivity of at least 75% IACS; and said alloy, when subjected to thermal-mechanical treatment, having a hardness of at least about 90 HV.

Claim 8

A copper alloy consisting essentially of: 0.10 to 0.4% by weight of cobalt, 0.04 to 0.25% by weight of phosphorus, up to 0.15% by weight of nickel and/or iron, the nickel content not being higher than 0.05% and the iron content not being higher than 0.1% and at least one element selected from the group consisting of Mg, Cd, Ag, Zn and Sn, the remainder being copper, the weight percentage of said element, when present, being 0.01 to 0.35 Mg, 0.01 to 0.7 Cd, 0.01 to 0.35 Ag, 0.01 to 0.7 Zn and 0.01 to 0.25 Sn, the total content of said elements not exceeding 1% by weight, wherein the weight percentage of Ni, Co, Fe and P are chosen so that the ratio of the weight of Ni+Co+Fe to the weight of phosphorus is between 2.5 and 5, said alloy having a high electrical conductivity of at least 75% IACS; and said alloy, when subjected to thermal-mechanical treatment, having a hardness of at least about 90 HV.

Claim 9

A copper alloy consisting essentially of: 0.10 to 0.4% by weight of cobalt, 0.04 to 0.25% by weight of phosphorus, up to 0.15% by weight of nickel and/or iron, the nickel content not being higher than 0.05% and the iron content not being higher than 0.1% and at least one element selected from the group consisting of Mg, Cd, Ag, Zn and Sn, the remainder being copper, the weight percentage of said element, when present, being 0.01 to 0.35 Mg, 0.01 to 0.7 Cd, 0.01 to 0.35 Ag, 0.01 to 0.7 Zn and 0.01 to 0.25 Sn, the total content of said elements not exceeding 1% by weight, wherein the weight percentage of Ni, Co, Fe and P are chosen so that the ratio of the weight of Ni+Co+Fe to the weight of phosphorus is between 2.5 and 5, said alloy having a high electrical conductivity of at least 75% IACS; and said alloy, when subjected to thermal-mechanical treatment, having a hardness of at least about 90 HV.