Electrochemical prediction of corrosion susceptibility of zirconium-base alloys
Assignee: General Electric Co
•
Filing: 1982-03-01
•
Granted: 1984-01-10
•
Expires: 2002-03-01
Abstract
Abstract An electrochemical apparatus and a testing procedure are described for predicting the susceptibility of certain zirconium-base alloys to nodular corrosion in boiling water reactor environments. A chemically polished pre-determined area of the surface of the zirconium-base alloy is made the anode in an electrochemical cell. A constant direct current (d-c) having an alternating current (a-c) superimposed thereon is applied to the cell and the quadrature component of the a-c cell voltage is monitored in order to measure the value of the depth of the minimum occurring in the quadrature component of the a-c cell voltage-versus-time relationship after a d-c cell voltage of at least eight volts has been reached. The application of a-c to the cell is stopped and the constant d-c previously applied is decreased by a a step-change to a constant value providing a reduction of at least one-half in the current density. The d-c cell voltage response to this step-change exhibits a transient decrease and the d-c cell voltage response as a function of time is monitored until the cell voltage again starts to rise in order that the magnitude of this transient can be measured. A constant d-c current is then re-applied to the cell and the degree of non-linearity occurring in the relationship between d-c cell voltage and time is measured. The magnitude of a minimum in the quadrature component of the a-c cell voltage, the magnitude of the transient in the d-c cell voltage response to the step-change in d-c current and the degree of non-linearity displayed in the relationship between d-c cell voltage and time (or some other parameter, which directly relates to time) are compared to standardized values and an assessment, or determination, of the corrosion susceptibility of the sample can be made based upon this comparison.
Inventors
- 👤 Dale F. Taylor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 04:20
CPC Classifications
G; G01; G01N; G01N17/00; G01N17/02
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
172 words
Apparatus for generating and recording specific electrochemical kinetic information in order to characterize the susceptibility of a zirconium-base alloy body to nodular corrosion, comprising in combination: means adapted to releasably cooperate with a predetermined area of said alloy body to define a liquid-tight volume therewith, said defining means having inlet means and outlet means in flow communication with said volume and also including electrically conducting structure disposed to be spaced and electrically insulated from said pre-determined area, means electrically connected to said electrically conducting structure and also adapted to be electrically connected to said pre-determined area for supplying constant d-c current therebetween at pre-selected levels of current with said pre-determined area being at more positive electrical potential than said electrically conducting structure, and means electrically connected to said electrically conducting structure and also adapted to be electrically connected to said pre-determined area for sensing and recording the d-c voltage drop occurring between said electrically conducting structure and said pre-determined area as a function of time, when constant d-c current is applied therebetween.
Claim 2
Dependent Claim
172 words
Apparatus for generating and recording specific electrochemical kinetic information in order to characterize the susceptibility of a zirconium-base alloy body to nodular corrosion, comprising in combination: means adapted to releasably cooperate with a predetermined area of said alloy body to define a liquid-tight volume therewith, said defining means having inlet means and outlet means in flow communication with said volume and also including electrically conducting structure disposed to be spaced and electrically insulated from said pre-determined area, means electrically connected to said electrically conducting structure and also adapted to be electrically connected to said pre-determined area for supplying constant d-c current therebetween at pre-selected levels of current with said pre-determined area being at more positive electrical potential than said electrically conducting structure, and means electrically connected to said electrically conducting structure and also adapted to be electrically connected to said pre-determined area for sensing and recording the d-c voltage drop occurring between said electrically conducting structure and said pre-determined area as a function of time, when constant d-c current is applied therebetween.
Claim 3
Dependent Claim
36 words
The apparatus of claim 1 wherein the defining means comprises wall area and sealing means disposed between said wall area and the alloy body, the electrically conducting structure comprising a metallic portion of said wall area.
Claim 4
Dependent Claim
16 words
The apparatus of claim 2 wherein the metallic portion of the wall area is stainless steel.
Claim 5
Dependent Claim
11 words
The apparatus of claim 2 wherein the sealing means is elastomeric.
Claim 6
Dependent Claim
15 words
The apparatus of claim 4 wherein the elastomeric sealing means is made of hydrophobic material.
Claim 7
Dependent Claim
17 words
The apparatus of claim 5 wherein the hydrophobic material is a fluoroelastomer containing polytetrafluoroethylene as an additive.
Claim 8
Dependent Claim
24 words
The apparatus of claim 1 wherein the defining means is in a generally cylindrical configuration adapted to releasably cooperate with a cylindrical alloy body.
Claim 9
Dependent Claim
285 words
Apparatus for generating and recording specific electrochemical kinetic information in order to characterize the susceptibility of a zirconium-base alloy body to nodular corrosion, comprising in combination: means adapted to releasably cooperate with a predetermined area of said alloy body to define a liquid-tight volume therewith, said defining means having inlet means and outlet means in flow communication with said volume and also including electrically conducting structure disposed to be spaced and electrically insulated from said pre-determined area, means electrically connected to said electrically conducting structure and also adapted to be electrically connected to said pre-determined area for supplying constant d-c current therebetween at pre-selected levels of current with said pre-determined area being at a more positive electrical potential than said electrically conducting structure, means electrically connected to said electrically conducting structure and also adapted to be electrically connected to said pre-determined area for sensing and recording the d-c voltage drop occurring as a function of time between said electrically conducting structure and said pre-determined area, when d-c current is applied therebetween, means for selectively applying an a-c current to said means for supplying constant d-c current whereby an a-c current is superimposed on the d-c current supplied thereby and means electrically connected to said electrically conducting structure and also adapted to be electrically connected to said pre-determined area for sensing and recording the a-c quadrature component of the a-c voltage occurring as a function of time between said electrically conducting structure and said pre-determined area, when d-c current with superimposed a-c current is applied therebetween, said means for sensing and recording the a-c quadrature component of the a-c voltage being electrically connected to said a-c current applying means to receive a reference a-c signal therefrom.
Claim 10
Dependent Claim
285 words
Apparatus for generating and recording specific electrochemical kinetic information in order to characterize the susceptibility of a zirconium-base alloy body to nodular corrosion, comprising in combination: means adapted to releasably cooperate with a predetermined area of said alloy body to define a liquid-tight volume therewith, said defining means having inlet means and outlet means in flow communication with said volume and also including electrically conducting structure disposed to be spaced and electrically insulated from said pre-determined area, means electrically connected to said electrically conducting structure and also adapted to be electrically connected to said pre-determined area for supplying constant d-c current therebetween at pre-selected levels of current with said pre-determined area being at a more positive electrical potential than said electrically conducting structure, means electrically connected to said electrically conducting structure and also adapted to be electrically connected to said pre-determined area for sensing and recording the d-c voltage drop occurring as a function of time between said electrically conducting structure and said pre-determined area, when d-c current is applied therebetween, means for selectively applying an a-c current to said means for supplying constant d-c current whereby an a-c current is superimposed on the d-c current supplied thereby and means electrically connected to said electrically conducting structure and also adapted to be electrically connected to said pre-determined area for sensing and recording the a-c quadrature component of the a-c voltage occurring as a function of time between said electrically conducting structure and said pre-determined area, when d-c current with superimposed a-c current is applied therebetween, said means for sensing and recording the a-c quadrature component of the a-c voltage being electrically connected to said a-c current applying means to receive a reference a-c signal therefrom.
Claim 11
Dependent Claim
30 words
The apparatus of claim 8 wherein the means for sensing and recording the a-c quadrature component comprises a phase-sensitive detector, a voltmeter and a data acquisition system electrically connected thereto.
Claim 12
Dependent Claim
36 words
The apparatus of claim 8 wherein the defining means comprises wall area and sealing means disposed between said wall area and the alloy body, the electrically conducting structure comprising a metallic portion of said wall area.
Claim 13
Dependent Claim
16 words
The apparatus of claim 10 wherein the metallic portion of the wall area is stainless steel.
Claim 14
Dependent Claim
11 words
The apparatus of claim 10 wherein the sealing means is elastomeric.
Claim 15
Dependent Claim
15 words
The apparatus of claim 12 wherein the elastomeric sealing means is made of hydrophobic material.
Claim 16
Dependent Claim
17 words
The apparatus of claim 13 wherein the hydrophobic material is a fluoroelastomer containing polytetrafluoroethylene as an additive.
Claim 17
Dependent Claim
24 words
The apparatus of claim 8 wherein the defining means is in a generally cylindrical configuration adapted to releasably cooperate with a cylindrical alloy body.
Claim 18
Dependent Claim
233 words
An electrochemical process for predicting the ability of a zirconium-base alloy body to resist nodular corrosion in a boiling water nuclear reactor during normal operation, comprising the steps of: (1) chemically polishing a pre-determined area of a surface of said alloy body, (2) making said pre-determined area the anode in an electrochemical cell, (3) applying to said cell constant direct current providing a current density at the anode in the range of from about 0.1 mA/cm 2 d-c to about 10 mA/cm 2 d-c, (4) decreasing the constant direct current previously applied to said cell by a step-change to a constant value providing a current density of less than one-half the direct current density utilized in step (3) and monitoring the d-c cell voltage response, which exhibits a transient, as a function of time until the cell voltage again starts to increase in value, (5) re-applying to said cell a value of constant direct current providing a current density in the range of from 0.1 mA/cm 2 d-c to about 10 mA/cm 2 d-c and measuring the degree of non-linearity occurring in the relationship between d-c voltage and time, (6) measuring the value of the transient voltage, the depth of the minimum occurring as the d-c cell voltage varies with time, (7) comparing the values obtained in steps (5) and (6) to standardized values to determine the corrosion susceptibility of said alloy body.
Claim 19
Dependent Claim
233 words
An electrochemical process for predicting the ability of a zirconium-base alloy body to resist nodular corrosion in a boiling water nuclear reactor during normal operation, comprising the steps of: (1) chemically polishing a pre-determined area of a surface of said alloy body, (2) making said pre-determined area the anode in an electrochemical cell, (3) applying to said cell constant direct current providing a current density at the anode in the range of from about 0.1 mA/cm 2 d-c to about 10 mA/cm 2 d-c, (4) decreasing the constant direct current previously applied to said cell by a step-change to a constant value providing a current density of less than one-half the direct current density utilized in step (3) and monitoring the d-c cell voltage response, which exhibits a transient, as a function of time until the cell voltage again starts to increase in value, (5) re-applying to said cell a value of constant direct current providing a current density in the range of from 0.1 mA/cm 2 d-c to about 10 mA/cm 2 d-c and measuring the degree of non-linearity occurring in the relationship between d-c voltage and time, (6) measuring the value of the transient voltage, the depth of the minimum occurring as the d-c cell voltage varies with time, (7) comparing the values obtained in steps (5) and (6) to standardized values to determine the corrosion susceptibility of said alloy body.
Claim 20
Dependent Claim
27 words
The process recited in claim 16 wherein the ratio of the initial constant direct current to the constant direct current applied after the step-change is about 5:1.
Claim 21
Dependent Claim
11 words
The process of claim 16 wherein the zirconium-base alloy is Zircaloy-2.
Claim 22
Dependent Claim
20 words
The process of claim 16 wherein the initial direct current density at the anode is about 0.5 mA/cm 2 .
Claim 23
Dependent Claim
320 words
An electrochemical process for predicting the ability of a zirconium-base alloy body to resist nodular corrosion in a boiling water nuclear reactor during normal operation, comprising the steps of: (1) chemically polishing a pre-determined area of a surface of said alloy body, (2) making said pre-determined area the anode in an electrochemical cell, (3) applying to said cell constant direct current providing a current density at the anode in the range of from about 0.1 mA/cm 2 d-c to about 10 mA/cm 2 d-c and simultaneously applying to said cell alternating current providing a current density at the anode having a workable signal-to-noise ratio and monitoring the quadrature component of the a-c cell voltage response thereto as a function of time, (4) measuring the value of the depth of the minimum occurring in the quadrature component of the a-c cell voltage-versus-time relationship after a d-c cell voltage of at least 8 volts has been reached, (5) ceasing the application of alternating current to said cell, (6) decreasing the constant direct current previously applied to said cell by a step-change to a constant value providing a current density of less than one-half the direct current density utilized in step (3) and monitoring the d-c cell voltage response, which exhibits a transient, as a function of time until the cell voltage again starts to increase in value, (7) re-applying to said cell a value of constant direct current providing a current density at the anode in the range of from about 0.1 mA/cm 2 d-c to about 10 mA/cm 2 d-c and measuring the degree of non-linearity occurring in the relationship between d-c cell voltage and time, (8) measuring the value of the transient voltage, the depth of the minimum occurring as the d-c cell voltage varies with time, (9) comparing the values obtained in steps (4), (7) and (8) to standardized values to determine the corrosion susceptibility of said alloy body.
Claim 24
Dependent Claim
320 words
An electrochemical process for predicting the ability of a zirconium-base alloy body to resist nodular corrosion in a boiling water nuclear reactor during normal operation, comprising the steps of: (1) chemically polishing a pre-determined area of a surface of said alloy body, (2) making said pre-determined area the anode in an electrochemical cell, (3) applying to said cell constant direct current providing a current density at the anode in the range of from about 0.1 mA/cm 2 d-c to about 10 mA/cm 2 d-c and simultaneously applying to said cell alternating current providing a current density at the anode having a workable signal-to-noise ratio and monitoring the quadrature component of the a-c cell voltage response thereto as a function of time, (4) measuring the value of the depth of the minimum occurring in the quadrature component of the a-c cell voltage-versus-time relationship after a d-c cell voltage of at least 8 volts has been reached, (5) ceasing the application of alternating current to said cell, (6) decreasing the constant direct current previously applied to said cell by a step-change to a constant value providing a current density of less than one-half the direct current density utilized in step (3) and monitoring the d-c cell voltage response, which exhibits a transient, as a function of time until the cell voltage again starts to increase in value, (7) re-applying to said cell a value of constant direct current providing a current density at the anode in the range of from about 0.1 mA/cm 2 d-c to about 10 mA/cm 2 d-c and measuring the degree of non-linearity occurring in the relationship between d-c cell voltage and time, (8) measuring the value of the transient voltage, the depth of the minimum occurring as the d-c cell voltage varies with time, (9) comparing the values obtained in steps (4), (7) and (8) to standardized values to determine the corrosion susceptibility of said alloy body.
Claim 25
Dependent Claim
33 words
The process of claim 20 wherein the alternating current density at the anode has a value in the range of from 0.1 percent to 10 percent of the initial d-c current density value.
Claim 26
Dependent Claim
28 words
The process recited in claim 20 wherein the ratio of the initial constant direct current to the constant direct current applied after the step-change is about 5:1. PG,39
Claim 27
Dependent Claim
25 words
The process of claim 20 wherein the applied a-c current has a frequency in the range of from about 2 Hz to about 60 Hz.
Claim 28
Dependent Claim
17 words
The process of claim 23 wherein the applied a-c current has a frequency of about 30 Hz.
Claim 29
Dependent Claim
11 words
The process of claim 20 wherein the zirconium-base alloy is Zircaloy-2.
Claim 30
Dependent Claim
20 words
The process of claim 20 wherein the initial direct current density at the anode is about 0.5 mA/cm 2 .
Claim 31
Dependent Claim
138 words
An electrochemical process for predicting the ability of a zirconium-base alloy body to resist nodular corrosion in a boiling water nuclear reactor during normal operation, comprising the steps of: (1) chemically polishing a pre-determined area of a surface of said alloy body, (2) making said predetermined area the anode in an electrochemical cell, (3) appplying constant d-c current, alone or with superimposed constant a-c current to said cell, (4) determining at least one electrochemical kinetic parameter of said pre-determined area selected from the group consisting of (a) the minimum in the a-c quadrature voltage component of the a-c cell voltage, (b) the magnitude of the transient in the d-c cell voltage-versus-time relationship and (c) the degree of non-linearity in the d-c cell voltage-versus-time relationship, and (5) comparing said at least one parameter to a standard for such parameter.
Claim 32
Dependent Claim
138 words
An electrochemical process for predicting the ability of a zirconium-base alloy body to resist nodular corrosion in a boiling water nuclear reactor during normal operation, comprising the steps of: (1) chemically polishing a pre-determined area of a surface of said alloy body, (2) making said predetermined area the anode in an electrochemical cell, (3) appplying constant d-c current, alone or with superimposed constant a-c current to said cell, (4) determining at least one electrochemical kinetic parameter of said pre-determined area selected from the group consisting of (a) the minimum in the a-c quadrature voltage component of the a-c cell voltage, (b) the magnitude of the transient in the d-c cell voltage-versus-time relationship and (c) the degree of non-linearity in the d-c cell voltage-versus-time relationship, and (5) comparing said at least one parameter to a standard for such parameter.
Claim 33
Dependent Claim
32 words
The process recited in claim 27 wherein constant d.c. current is applied to the electrochemical cell and the parameter determined is the magnitude of the transient in the d-c cell voltage-versus-time relationship.
Claim 34
Dependent Claim
39 words
The process recited in claim 27 wherein constant d.c. current with superimposed constant a.c. current is applied to the electrochemical cell and the parameter determined is the minimum in the a-c quadrature voltage component of the a-c cell voltage.
Claim 35
Dependent Claim
31 words
The process recited in claim 27 wherein constant d-c current is applied to the electrochemical cell and the parameter determined is the degree of non-linearity in the d-c cell voltage-versus-time relationship.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-09 | 1987-07-11 | 1988-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-09 | 1991-07-11 | 1992-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-09 | 1995-07-11 | 1996-01-10 | $7700.00 | Window Closed / Lapsed |