Adsorption by zeolitic composition
Assignee: Shin Tohoku Chemical Ind Co Ltd
•
Filing: 1981-08-24
•
Granted: 1984-01-10
•
Expires: 2001-08-24
Abstract
Abstract Natural zeolite minerals which have a high silicon-to aluminum atomic ratio (hereinafter referred to as Si/Al ratio)and a fibrous micro-structure in at least some parts are ore-dressed and classified according to the iron impurity content converted in terms of iron oxide Fe 2 O 3 . Zeolite with high Si/Al ratio is excellent in resistance to acid and heat and can be re-activated at high temperatures. The fibrous microstructure is considered to impart a high degree of mechanical strength to the zeolite after pelletization. High-grade natural zeolites with small iron impurity content uniformly exhibit high adsorption performance. In particular, zeolite adsorbents using natural zeolite consisting principally of mordenite are very useful for various purposes. In the case of removing oxygen, the combined use of the zeolite adsorbent and an oxygen removing catalyst provides good results. By cooling the zeolite adsorbent down to low temperatures, its adsorption performance rises sharply. The zeolite adsorbent is of particular utility when employed for purification of gas, removal of water vapor from a vacuum system, removal of undesirable components and so forth.
Inventors
- 👤 Junichi Nishizawa
- 👤 Rensaku Suzuki
- 👤 Kenji Aizawa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 17:52
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/02; B01D53/04; B01D53/0407; B01D53/0423; B01J; B01J20/00; B01J20/02; B01J20/10; B01J20/16; B01J20/18; B01D2253/00; B01D2253/10; B01D2253/106; B01D2253/108; B01D2257/00; B01D2257/10; B01D2257/102; B01D2257/108; B01D2257/11
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
354 words
Method of treating a starting fluid rich in adsorbable substance for removing said adsorbable substance substantially completely therefrom to provide a treated fluid substantially free from said adsorbable substance, and carried out in a hermetic adsorption chamber of high thermal conductivity and heat resistance and capable of withstanding elevated temperatures of about 300°-600° C. and having an inlet for passing said starting fluid into said chamber, an outlet for recovering said treated fluid therefrom, thermally conductive surface means defining an internal space within said chamber for receiving a porous adsorbent therein, and means for heating said adsorbent and the adjacent thermally conductive surface means to said temperatures of about 300°-600° C., which comprises the steps of passing said starting fluid through said inlet and into adsorbing contact with a porous adsorbent received in said internal space and which is of natural zeolite mineral origin, which has been ore dressed and then classified according to its iron impurity content and which constitutes a composition corresponding to that consisting essentially of more than about 90% by weight but less than about 99.8% by weight of a granular mordenitic or granular clinoptilolitic natural zeolite mineral origin material having a silicon to aluminum atomic ratio of more than about 4, the balance being iron present as naturally occurring impurity in association with the zeolite mineral origin granular material and calculated as Fe 2 O 3 , and sufficiently to adsorb substantially completely said adsorbable substance on said composition and thereby remove said adsorbable substance from said starting fluid to provide said treated fluid substantially free from said adsorbable substance, recovering said treated fluid through said outlet, and for the purposes of reactivating said composition, thereafter interrupting the passing and recovering steps, and heating said composition and adjacent surface means by said heating means to about 300°-600° C. and sufficiently to desorb substantially completely said adsorbable substance from said composition and thereby reactivate said composition and to desorb any said adsorbable substance which has been adsorbed onto said adjacent surface means, and removing the so desorbed adsorbable substance from said chamber, and subsequently repeating said passing and recovering steps.
Claim 2
Dependent Claim
354 words
Method of treating a starting fluid rich in adsorbable substance for removing said adsorbable substance substantially completely therefrom to provide a treated fluid substantially free from said adsorbable substance, and carried out in a hermetic adsorption chamber of high thermal conductivity and heat resistance and capable of withstanding elevated temperatures of about 300°-600° C. and having an inlet for passing said starting fluid into said chamber, an outlet for recovering said treated fluid therefrom, thermally conductive surface means defining an internal space within said chamber for receiving a porous adsorbent therein, and means for heating said adsorbent and the adjacent thermally conductive surface means to said temperatures of about 300°-600° C., which comprises the steps of passing said starting fluid through said inlet and into adsorbing contact with a porous adsorbent received in said internal space and which is of natural zeolite mineral origin, which has been ore dressed and then classified according to its iron impurity content and which constitutes a composition corresponding to that consisting essentially of more than about 90% by weight but less than about 99.8% by weight of a granular mordenitic or granular clinoptilolitic natural zeolite mineral origin material having a silicon to aluminum atomic ratio of more than about 4, the balance being iron present as naturally occurring impurity in association with the zeolite mineral origin granular material and calculated as Fe 2 O 3 , and sufficiently to adsorb substantially completely said adsorbable substance on said composition and thereby remove said adsorbable substance from said starting fluid to provide said treated fluid substantially free from said adsorbable substance, recovering said treated fluid through said outlet, and for the purposes of reactivating said composition, thereafter interrupting the passing and recovering steps, and heating said composition and adjacent surface means by said heating means to about 300°-600° C. and sufficiently to desorb substantially completely said adsorbable substance from said composition and thereby reactivate said composition and to desorb any said adsorbable substance which has been adsorbed onto said adjacent surface means, and removing the so desorbed adsorbable substance from said chamber, and subsequently repeating said passing and recovering steps.
Claim 3
Dependent Claim
16 words
Method according to claim 1, wherein said composition is cooled during said passing and recovering steps.
Claim 4
Dependent Claim
33 words
Method according to claim 2, wherein said starting fluid contains water vapor and is passed into contact with said composition sufficiently to dehydrate said fluid to a dew point below about -196° C.
Claim 5
Dependent Claim
24 words
Method according to claim 1, wherein said balance of iron constitutes less than about 0.7% by weight calculated as Fe 2 O 3 .
Claim 6
Dependent Claim
22 words
Method according to claim 1, wherein said balance of iron constitutes about 0.7-1.5% by weight calculated as Fe 2 O 3 .
Claim 7
Dependent Claim
22 words
Method according to claim 1, wherein said balance of iron constitutes about 1.5-4% by weight calculated as Fe 2 O 3 .
Claim 8
Dependent Claim
222 words
Method of removing an adsorbable substance from a fluid which comprises the steps of contacting in a hermetic zone a starting fluid rich is adsorbable substance with a porous adsorbent which is of natural zeolite mineral origin, which has been ore dressed and then classified according to its iron impurity content, and which constitutes a composition corresponding to that consisting essentially of more than about 90% by weight but less than about 99.8% by weight of a granular mordenitic or granular clinoptilolitic natural zeolite mineral origin material having a silicon to aluminum atomic ratio of more than about 4, the balance being iron present as naturally occurring impurity in association with the zeolite mineral origin granular material and calculated as Fe 2 O 3 , and sufficiently to adsorb substantially completely said adsorbable substance on said composition and thereby remove said adsorbable substance from said starting fluid to provide a treated fluid substantially free from said adsorbable substance, recovering said treated fluid from said zone, and for the purposes of reactivating said composition, thereafter interrupting said contacting and recovering steps, heating said composition to about 300°-600° C. and sufficiently to desorb substantially completely said adsorbable substance from said composition and thereby reactivate said composition, and removing the so desorbed adsorbable substance from said zone, and subsequently repeating said contacting and recovering steps.
Claim 9
Dependent Claim
222 words
Method of removing an adsorbable substance from a fluid which comprises the steps of contacting in a hermetic zone a starting fluid rich is adsorbable substance with a porous adsorbent which is of natural zeolite mineral origin, which has been ore dressed and then classified according to its iron impurity content, and which constitutes a composition corresponding to that consisting essentially of more than about 90% by weight but less than about 99.8% by weight of a granular mordenitic or granular clinoptilolitic natural zeolite mineral origin material having a silicon to aluminum atomic ratio of more than about 4, the balance being iron present as naturally occurring impurity in association with the zeolite mineral origin granular material and calculated as Fe 2 O 3 , and sufficiently to adsorb substantially completely said adsorbable substance on said composition and thereby remove said adsorbable substance from said starting fluid to provide a treated fluid substantially free from said adsorbable substance, recovering said treated fluid from said zone, and for the purposes of reactivating said composition, thereafter interrupting said contacting and recovering steps, heating said composition to about 300°-600° C. and sufficiently to desorb substantially completely said adsorbable substance from said composition and thereby reactivate said composition, and removing the so desorbed adsorbable substance from said zone, and subsequently repeating said contacting and recovering steps.
Claim 10
Dependent Claim
16 words
Method according to claim 7, wherein said composition is cooled during said passing and recovering steps.
Claim 11
Dependent Claim
31 words
Method according to claim 8, wherein said starting fluid contains water vapor and is contacted with said composition sufficiently to dehydrate said fluid to a dew point below about -196° C.
Claim 12
Dependent Claim
24 words
Method according to claim 7, wherein said balance of iron constitutes less than about 0.7% by weight calculated as Fe 2 O 3 .
Claim 13
Dependent Claim
22 words
Method according to claim 7, wherein said balance of iron constitutes about 0.7-1.5% by weight calculated as Fe 2 O 3 .
Claim 14
Dependent Claim
22 words
Method according to claim 7, wherein said balance of iron constitutes about 1.5-4% by weight calculated as Fe 2 O 3 .
Claim 15
Dependent Claim
160 words
In an adsorption equipment comprising a hermetic adsorption chamber having a porous adsorbent therein, the improvement wherein said porous adsorbent is a composition consisting essentially of more than 90% by weight but less than 99.8% by weight of a granular mordenitic or granular clinoptilolitic material having a silicon to aluminum atomic ratio of more than about 4, the balance being iron present as naturally occurring impurity in association with the mordenitic or clinoptilolitic material of the composition and calculated as Fe 2 O 3 , and wherein said hermetic adsorption chamber is made of heat resistant material and has a first opening permitting the passage therethrough of a fluid rich in adsorbable substance and a second opening permitting the passage therethrough of a fluid free of said adsorbable substance, a top wall, a bottom wall, a side wall and means for heating said adsorbent composition in said adsorption chamber and within said walls to a temperature of about 300°-600° C.
Claim 16
Dependent Claim
160 words
In an adsorption equipment comprising a hermetic adsorption chamber having a porous adsorbent therein, the improvement wherein said porous adsorbent is a composition consisting essentially of more than 90% by weight but less than 99.8% by weight of a granular mordenitic or granular clinoptilolitic material having a silicon to aluminum atomic ratio of more than about 4, the balance being iron present as naturally occurring impurity in association with the mordenitic or clinoptilolitic material of the composition and calculated as Fe 2 O 3 , and wherein said hermetic adsorption chamber is made of heat resistant material and has a first opening permitting the passage therethrough of a fluid rich in adsorbable substance and a second opening permitting the passage therethrough of a fluid free of said adsorbable substance, a top wall, a bottom wall, a side wall and means for heating said adsorbent composition in said adsorption chamber and within said walls to a temperature of about 300°-600° C.
Claim 17
Dependent Claim
29 words
Equipment according to claim 13, wherein a pretreatment chamber is connected to said first opening of said adsorption chamber and contains a catalyst which contains therein an oxidizable substance.
References Cited (Backward Citations)
US1588258A
Cited
US1874537A
Cited
US2396474A
Cited
US2591543A
Cited
US2604760A
Cited
US2874030A
Cited
US3013982A
Cited
US3013990A
Cited
US3200569A
Cited
US3255101A
Cited
US3335550A
Cited
US3283479A
Cited
US3598518A
Cited
US3469375A
Cited
US3472375A
Cited
US3701419A
Cited
US3969481A
Cited
FR2271880B1
Cited
US4025321A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-01-09 | 1987-07-11 | 1988-01-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-01-09 | 1991-07-11 | 1992-01-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-01-09 | 1995-07-11 | 1996-01-10 | $7700.00 | Window Closed / Lapsed |