US4421898A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Sulfonated polymer and compositions thereof
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1981-12-21
•
Granted: 1983-12-20
•
Expires: 2001-12-21
Abstract
Abstract This invention relates to unique and novel compositions based on chemically combining a sulfonated polymer and a tertiary amine terminated polylactone composition. The resulting amine neutralized sulfonated polymer compositions have a variety of uses including those as diverse as adhesive agents, thermoplastic elastomers, additive uses wherein these materials can be utilized to compatibilize two different polymers which are normally incompatible. These compositions can also be blended with fillers and/or oils when the sulfonated polymer is elastomeric. The materials display thermoplastic character.
Inventors
- 👤 Robert D. Lundberg
- 👤 Warren A. Thaler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 01:33
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/26; C08L23/32; C08F; C08F8/00; C08F8/34; C08F8/36; C08F2800/00; C08F2800/20
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
175 words
A sulfonated polymer which has about 10 to about 200 meq. of sulfonate groups per 100 grams of said sulfonated polymer, said sulfonate groups being neutralized with a polycaprolactone polymer having the formula: ##STR3## wherein n=1 to 500, m=1 to 20, R 1 or R 2 is selected from the group consisting of alkyl and cycloalkyl groups having about 1 to about 20 carbon atoms, R 1 is selected from the group consisting of hydrogen, alkyl and cycloalkyl groups having about 1 to about 20 carbon atoms and aryl groups, and R 4 and R 5 are selected from the group consisting of hydrogen, alkyl, cycloalkyl and aryl groups, wherein said sulfonated polymer is formed from an elastomeric polymer selected from the group consisting of Butyl rubber and an EPDM terpolymer or from a polymer selected from the group consisting of polystyrene, poly-t-butylstyrene, polychlorostyrene and poly-2-methylstyrene, said polycaprolactone polymer having an M n as measured by GPC of about 200 to about 50,000 and a melting point from below room temperature to about 55° C.
Claim 2
Dependent Claim
175 words
A sulfonated polymer which has about 10 to about 200 meq. of sulfonate groups per 100 grams of said sulfonated polymer, said sulfonate groups being neutralized with a polycaprolactone polymer having the formula: ##STR3## wherein n=1 to 500, m=1 to 20, R 1 or R 2 is selected from the group consisting of alkyl and cycloalkyl groups having about 1 to about 20 carbon atoms, R 1 is selected from the group consisting of hydrogen, alkyl and cycloalkyl groups having about 1 to about 20 carbon atoms and aryl groups, and R 4 and R 5 are selected from the group consisting of hydrogen, alkyl, cycloalkyl and aryl groups, wherein said sulfonated polymer is formed from an elastomeric polymer selected from the group consisting of Butyl rubber and an EPDM terpolymer or from a polymer selected from the group consisting of polystyrene, poly-t-butylstyrene, polychlorostyrene and poly-2-methylstyrene, said polycaprolactone polymer having an M n as measured by GPC of about 200 to about 50,000 and a melting point from below room temperature to about 55° C.
Claim 3
Dependent Claim
21 words
A polymer according to claim 1 wherein R 1 and R 2 are an alkyl group and R 3 is hydrogen.
Claim 4
Dependent Claim
22 words
A polymer according to claim 1 wherein either R 1 or R 2 is a methyl group and R 3 is hydrogen.
Claim 5
Dependent Claim
21 words
A polymer according to claim 1, wherein R 1 and R 2 are both methyl groups and R 3 is hydrogen.
Claim 6
Dependent Claim
19 words
A polymer according to claim 1, wherein R 1 , R 2 , and R 3 are methyl groups.
Claim 7
Dependent Claim
45 words
A polymer according to claim 1 wherein said EPDM terpolymer consists essentially of about 40 to about 75 wt. % of ethylene, of about 10 to about 53 wt. % of propylene and of about 2 to about 10 wt. % of a nonconjugated diene.
Claim 8
Dependent Claim
23 words
A polymer according to claim 6, wherein said nonconjugated diene is selected from the group consisting of 1,4-hexadiene, dicyclopentadiene, 5-alkylidene-2-norbornenes, 5-alkenyl-2-norbornenes and tetrahydroindene.
Claim 9
Dependent Claim
12 words
A polymer according to claim 7, wherein said nonconjugated diene is 5-ethylidene-2-norbornene.
References Cited (Backward Citations)
US3642728A
Cited
US3972961A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-19 | 1987-06-20 | 1987-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-19 | 1991-06-20 | 1991-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-19 | 1995-06-20 | 1995-12-20 | $7700.00 | Window Closed / Lapsed |