Bead filler rubber composition
Assignee: Bridgestone Corp
•
Filing: 1981-02-27
•
Granted: 1983-12-20
•
Expires: 2001-02-27
Abstract
Abstract A rubber composition comprising rubber, novolak-type phenolic resin and carbon black is very rigid and is adapted to be used as a bead filler rubber of a tire. Tires using the rubber composition are excellent in the high speed performance, lateral rigidity, ride feeling and durability.
Inventors
- 👤 Itsuo Miyake
- 👤 Keizo Okamoto
- 👤 Motonori Bundo
- 👤 Akihiro Noda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 23:11
CPC Classifications
B; B60; B60C; B60C15/00; B60C15/06; C; C08; C08L; C08L21/00
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
151 words
A bead filler rubber composition, consisting essentially of: (a) 100 parts by weight of a rubber selected from the group consisting of natural rubber, polyisoprene rubber, polybutadiene rubber, styrene-butadiene copolymer rubber and blends thereof; (b) 40-130 parts by weight of carbon black having an iodine adsorbability of 40-130 mg/g and a dibutyl phthalate absorbability of not higher than 130 ml/100 g; (c) 15-45 parts by weight per 100 parts by weight of carbon black of a mixture of a novolak phenolic resin selected from the group consisting of novolak phenol resin, novolak cresol resin, novolak resorcinol resin; and a novolak modified phenolic resin obtained by modifying with a compound selected from the group consisting of oils, aromatic hydrocarbons, or rubbers, wherein the mixing ratio of the novolak phenolic resin to the novolak modified phenolic resin is from 80/20 to 20/80 by weight, an effective amount of a hardener for the resin.
Claim 2
Dependent Claim
151 words
A bead filler rubber composition, consisting essentially of: (a) 100 parts by weight of a rubber selected from the group consisting of natural rubber, polyisoprene rubber, polybutadiene rubber, styrene-butadiene copolymer rubber and blends thereof; (b) 40-130 parts by weight of carbon black having an iodine adsorbability of 40-130 mg/g and a dibutyl phthalate absorbability of not higher than 130 ml/100 g; (c) 15-45 parts by weight per 100 parts by weight of carbon black of a mixture of a novolak phenolic resin selected from the group consisting of novolak phenol resin, novolak cresol resin, novolak resorcinol resin; and a novolak modified phenolic resin obtained by modifying with a compound selected from the group consisting of oils, aromatic hydrocarbons, or rubbers, wherein the mixing ratio of the novolak phenolic resin to the novolak modified phenolic resin is from 80/20 to 20/80 by weight, an effective amount of a hardener for the resin.
Claim 3
Dependent Claim
30 words
A bead filler rubber composition according to claim 1, wherein the amount of the carbon black is 60-120 parts by weight based on 100 parts by weight of the rubber.
Claim 4
Dependent Claim
32 words
A bead filler rubber composition according to claim 1, wherein the amount of the novolak-type phenolic resin is 20-40 parts by weight based on 100 parts by weight of the carbon black.
Claim 5
Dependent Claim
24 words
A bead filler rubber composition according to claim 1, wherein the mixing ratio of the novolak phenolic resin/the modified novolak phenolic resin is 60/40-40/60.
Claim 6
Dependent Claim
37 words
A bead filler rubber composition according to claim 1 wherein said novolak modified phenolic resins are novolak phenolic resins modified with an oil selected from the group consisting of rosin oil, tall oil and cashew nut oil.
Claim 7
Dependent Claim
36 words
A bead filler rubber composition according to claim 1, wherein said novolak modified phenolic resins are novolak phenolic resins modified with an oil selected from the group consisting of linoleic acid, oleic acid and linolenic acid.
Claim 8
Dependent Claim
33 words
A bead filler rubber composition according to claim 1, wherein said novolak modified phenolic resins are novolak phenolic resins modified with an aromatic hydrocarbon selected from the group consisting of xylene and mesitylene.
Claim 9
Dependent Claim
24 words
A bead filler rubber composition according to claim 1, wherein said novolak modified phenolic resins are novolak phenolic resins modified with a nitrile rubber.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-19 | 1987-06-20 | 1987-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-19 | 1991-06-20 | 1991-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-19 | 1995-06-20 | 1995-12-20 | $7700.00 | Window Closed / Lapsed |