Flame-resistant aqueous epoxy impregnating compositions containing nonionic surface active agents
Assignee: Isola Laminate Systems Corp
•
Filing: 1982-09-07
•
Granted: 1983-12-20
•
Expires: 2002-09-07
Abstract
Abstract Aqueous emulsions of epoxy resins, which can be used to treat glass cloth used in the preparation of printed circuit board laminates, are produced by combining an epoxy resin and a flame retardant phenol, such as tetrabromobisphenol A, with a selected nonionic surface active agent, such as an alkylaryl polyether alcohol, monomethylol dicyandiamide curing agent and, if needed, a catalyst.
Inventors
- 👤 William M. Alvino
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 20:12
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/03; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/4007; C08G59/4014; C08G59/4021; C08G59/62; C08G59/621; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/032; H05K1/0326; H05K1/0353; H05K1/0373; C08J2363/00; H05K2201/00; H05K2201/01; H05K2201/0104; H05K2201/012; H05K2203/00; H05K2203/12; H05K2203/122; Y; Y10; Y10S; Y10S428/00; Y10S428/901
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
98 words
An aqueous impregnating emulsion, said emulsion consisting essentially of the admixture of: (a) an epoxy resin; (b) a flame retardant phenol; (c) a nonionic alkylaryl polyether alcohol surface active agent having the general structural formula: ##STR2## where A is an alkyl group having from 5 to 10 carbons, y=1 to 2, and z=15 to 70; (d) a latent curing agent selected from the group consisting of monomethylol dicyandiamide and dicyandiamide; and (e) water; where the weight ratio of (epoxy resin):(flame retardant phenol):(nonionic surface active agent solids):(latent curing agent solids) is about (100):(1 to 100):(13 to 25):(2 to 10).
Claim 2
Dependent Claim
98 words
An aqueous impregnating emulsion, said emulsion consisting essentially of the admixture of: (a) an epoxy resin; (b) a flame retardant phenol; (c) a nonionic alkylaryl polyether alcohol surface active agent having the general structural formula: ##STR2## where A is an alkyl group having from 5 to 10 carbons, y=1 to 2, and z=15 to 70; (d) a latent curing agent selected from the group consisting of monomethylol dicyandiamide and dicyandiamide; and (e) water; where the weight ratio of (epoxy resin):(flame retardant phenol):(nonionic surface active agent solids):(latent curing agent solids) is about (100):(1 to 100):(13 to 25):(2 to 10).
Claim 3
Dependent Claim
102 words
An aqueous impregnating emulsion, said emulsion consisting essentially of the admixture of: (a) the reaction product of an epoxy resin and a flame retardant phenol; (b) a nonionic alkylaryl polyether alcohol surface active agent having the general structural formula: ##STR3## where A is an alkyl group having from 5 to 10 carbons, y=1 to 2, and z=15 to 70; (c) a latent curing agent selected from the group consisting of monomethylol dicyandiamide and dicyandiamide; and (d) water; where the weight ratio of (epoxy resin):(flame retardant phenol):(nonionic surface active agent solids):(latent curing agent solids) is about (100):(1 to 100):(13 to 25):(2 to 10).
Claim 4
Dependent Claim
102 words
An aqueous impregnating emulsion, said emulsion consisting essentially of the admixture of: (a) the reaction product of an epoxy resin and a flame retardant phenol; (b) a nonionic alkylaryl polyether alcohol surface active agent having the general structural formula: ##STR3## where A is an alkyl group having from 5 to 10 carbons, y=1 to 2, and z=15 to 70; (c) a latent curing agent selected from the group consisting of monomethylol dicyandiamide and dicyandiamide; and (d) water; where the weight ratio of (epoxy resin):(flame retardant phenol):(nonionic surface active agent solids):(latent curing agent solids) is about (100):(1 to 100):(13 to 25):(2 to 10).
Claim 5
Dependent Claim
48 words
The emulsion of claim 1 or claim 2, wherein the epoxy resin is selected from the group consisting of diglycidyl ethers of bisphenol A, diglycidyl ethers of bisphenol F, polyglycidyl ethers of a novolac, glycidyl esters, hydantoin epoxy resins, cycloaliphatic epoxy resins, and diglycidyl ethers of aliphatic diols.
Claim 6
Dependent Claim
16 words
The emulsion of claim 1 or claim 2, wherein the flame-retardant phenol is a halogenated phenol.
Claim 7
Dependent Claim
15 words
The emulsion of claim 1 or claim 2, wherein the flame-retardant phenol is tetrabromobisphenol A.
Claim 8
Dependent Claim
18 words
The emulsion of claim 1 or claim 2, wherein the epoxy is a diglycidyl ether of bisphenol A.
Claim 9
Dependent Claim
38 words
The emulsion of claim 1 or claim 2, wherein the curing agent is monomethylol dicyandiamide, and water is present in an amount effective to provide a solids content for the composition of from about 50% to about 70%.
Claim 10
Dependent Claim
13 words
The emulsion of claim 1 or claim 2, including a catalyst comprising benzyldimethylamine.
Claim 11
Dependent Claim
73 words
The emulsion of claim 1 or claim 2, wherein the epoxy resin is a diglycidyl ether of bisphenol A having an epoxy equivalent weight from about 180 to 215, the flame retardant phenol is tetrabromobisphenol A, the nonionic surface active agent has the following general structural formula: ##STR4## where A is an alkyl group having 8 to 9 carbons, y=1 to 2 and z=25 to 70, and the curing agent is monomethylol dicyandiamide.
Claim 12
Dependent Claim
17 words
The emulsion of claim 1 or claim 2, wherein the composition is impregnated into a porous substrate.
Claim 13
Dependent Claim
18 words
The emulsion of claim 1 or claim 2, wherein the composition is impregnated into a glass cloth substrate.
Claim 14
Dependent Claim
31 words
The emulsion of claim 1 or claim 2, wherein the composition is impregnated into a plurality of glass cloth substrates, said substrates being heat and pressure consolidated to form a laminate.
Claim 15
Dependent Claim
41 words
The emulsion of claim 1 or claim 2, wherein the composition is impregnated into a plurality of porous substrates, said substrates being heat and pressure consolidated with at least one exterior copper conductive sheet to form a laminated copper clad laminate.
Claim 16
Independent Claim
153 words
A method of making an aqueous impregnating emulsion comprising the steps of: (a) mixing an epoxy resin and a flame retardant phenol, and heating them up to from about 80° C. to about 100° C. over from about 20 minutes to about 30 minutes, to provide a reaction product, and (b) cooling the reaction product, and then adding thereto a nonionic alkylaryl polyether alcohol surface active agent having the general structural formula: ##STR5## where A is an alkyl group having from 5 to 10 carbons, y=1 to 2, and z=15 to 70, and a latent curing agent water solution, wherein the latent curing agent is selected from the group consisting of monomethylol dicyandiamide and dicyandiamide, the latent curing agent water solution being added incrementally, to provide an emulsion; where the weight ratio of (epoxy resin):(flame retardant phenol):(nonionic surface active agent solids):(latent curing agent solids) is about (100):(1 to 100):(13 to 25):(2 to 10).
Claim 17
Independent Claim
153 words
A method of making an aqueous impregnating emulsion comprising the steps of: (a) mixing an epoxy resin and a flame retardant phenol, and heating them up to from about 80° C. to about 100° C. over from about 20 minutes to about 30 minutes, to provide a reaction product, and (b) cooling the reaction product, and then adding thereto a nonionic alkylaryl polyether alcohol surface active agent having the general structural formula: ##STR5## where A is an alkyl group having from 5 to 10 carbons, y=1 to 2, and z=15 to 70, and a latent curing agent water solution, wherein the latent curing agent is selected from the group consisting of monomethylol dicyandiamide and dicyandiamide, the latent curing agent water solution being added incrementally, to provide an emulsion; where the weight ratio of (epoxy resin):(flame retardant phenol):(nonionic surface active agent solids):(latent curing agent solids) is about (100):(1 to 100):(13 to 25):(2 to 10).
Claim 18
Dependent Claim
71 words
The method of claim 14, wherein the epoxy resin is a diglycidyl ether of bisphenol A having an epoxy equivalent weight from about 180 to 215, the flame retardant phenol is tetrabromobisphenol A, the nonionic surface active agent has the following general structural formula: ##STR6## where A is an alkyl group having from 8 to 9 carbons, y=1 to 2 and z=25 to 70, and the curing agent is monomethylol dicyandiamide.
Claim 19
Independent Claim
161 words
A method of making an aqueous impregnating emulsion comprising the steps of: (a) mixing an epoxy resin and a nonionic alkylaryl polyether alcohol surface active agent having the general structural formula: ##STR7## where A is an alkyl group having from 5 to 10 carbons, y=1 to 2, and z=15 to 70, and heating them up to from about 80° C. to about 90° C., to provide a mixture, (b) adding a flame retardant phenol to the admixture at from about 80° C. to about 90° C., and mixing for up to about 5 minutes, to provide an admixture, and (c) cooling the admixture of (b), and then adding incrementally, thereto a latent curing agent water solution, to provide an emulsion, wherein the latent curing agent is selected from the group consisting of monomethylol dicyandiamide and dicyandiamide; where the weight ratio of (epoxy resin):(flame retardant phenol):(nonionic surface active agent solids):(latent curing agent solids) is about (100):(1 to 100):(13 to 25):(2 to 10).
Claim 20
Independent Claim
161 words
A method of making an aqueous impregnating emulsion comprising the steps of: (a) mixing an epoxy resin and a nonionic alkylaryl polyether alcohol surface active agent having the general structural formula: ##STR7## where A is an alkyl group having from 5 to 10 carbons, y=1 to 2, and z=15 to 70, and heating them up to from about 80° C. to about 90° C., to provide a mixture, (b) adding a flame retardant phenol to the admixture at from about 80° C. to about 90° C., and mixing for up to about 5 minutes, to provide an admixture, and (c) cooling the admixture of (b), and then adding incrementally, thereto a latent curing agent water solution, to provide an emulsion, wherein the latent curing agent is selected from the group consisting of monomethylol dicyandiamide and dicyandiamide; where the weight ratio of (epoxy resin):(flame retardant phenol):(nonionic surface active agent solids):(latent curing agent solids) is about (100):(1 to 100):(13 to 25):(2 to 10).
Claim 21
Dependent Claim
71 words
The method of claim 16, wherein the epoxy resin is a diglycidyl ether of bisphenol A having an epoxy equivalent weight from about 180 to 215, the flame retardant phenol is tetrabromobisphenol A, the nonionic surface active agent has the following general structural formula: ##STR8## where A is an alkyl group having from 8 to 9 carbons, y=1 to 2 and z=25 to 70, and the curing agent is monomethylol dicyandiamide.
References Cited (Backward Citations)
US3983056A
Cited
US4073762A
Cited
US4115328A
Cited
US4222918A
Cited
US4311753A
Cited
US4327143A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-19 | 1987-06-20 | 1987-12-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-19 | 1991-06-20 | 1991-12-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-19 | 1995-06-20 | 1995-12-20 | $7700.00 | Window Closed / Lapsed |