Method of mixing elastomeric polymers for improved physical properties
Assignee: Motors Liquidation Co
•
Filing: 1982-08-30
•
Granted: 1983-12-13
•
Expires: 2002-08-30
Abstract
Abstract A method of mixing crosslinkable elastomeric polymers and reinforcing fillers has been developed that yields significant improvements in physical properties compared to like polymers mixed by conventional methods. The method entails working a filler-polymer mixture at a temperature between the glass transition temperature and the liquid-liquid temperature of the uncrosslinked polymer to enhance filler integration. The mixture is then heated to a temperature greater than the flow temperature of the uncrosslinked polymer and worked so that air bubbles dispersed in the mixture are eliminated. The heating and cooling steps are repeated until the filler particles are thoroughly integrated and substantially all air bubbles are eliminated.
Inventors
- 👤 Michael C. H. Lee
- 👤 Darrel S. Nelson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:55
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08J3/203
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
158 words
A method of improving the physical properties of a crosslinked elastomeric polymer containing a particulate filler comprising the steps of dispersing said filler in the polymer before it is crosslinked; reducing the temperature of the filler and polymer mixture to a temperature between the glass transition temperature and the liquid liquid temperature of the uncrosslinked polymer; working said polymer at said reduced temperature so as to create shear between the polymer and filler to encourage mixing thereof; heating said mixture to a temperature greater than the flow temperature of the uncrosslinked polymer; working said polymer at said elevated temperature such that air bubbles dispersed in the mixture migrate to and are broken at the surface thereof; and repeating said cooling and heating cycles until the particulate filler is uniformly dispersed in the polymer matrix and substantially all the air bubbles are eliminated, said method enhancing the reinforcing effect of the particles in the elastomer after it is crosslinked.
Claim 2
Independent Claim
158 words
A method of improving the physical properties of a crosslinked elastomeric polymer containing a particulate filler comprising the steps of dispersing said filler in the polymer before it is crosslinked; reducing the temperature of the filler and polymer mixture to a temperature between the glass transition temperature and the liquid liquid temperature of the uncrosslinked polymer; working said polymer at said reduced temperature so as to create shear between the polymer and filler to encourage mixing thereof; heating said mixture to a temperature greater than the flow temperature of the uncrosslinked polymer; working said polymer at said elevated temperature such that air bubbles dispersed in the mixture migrate to and are broken at the surface thereof; and repeating said cooling and heating cycles until the particulate filler is uniformly dispersed in the polymer matrix and substantially all the air bubbles are eliminated, said method enhancing the reinforcing effect of the particles in the elastomer after it is crosslinked.
Claim 3
Independent Claim
114 words
A method of improving the reinforcing properties of carbon black in elastomeric polymers comprising the steps of attriting the carbon black particles to substantially reduce their size and lower their pH; mixing said attrited carbon black with the polymer before it is crosslinked; subjecting said mixture to shear stress while it is at a first temperature between the glass transition temperature and the liquid-liquid transition temperature of the uncrosslinked polymer; working said mixture at a second temperature above the flow temperature of the uncrosslinked polymer to eliminate microvoids therein; repeating said steps at said first and second temperatures until the attrited black is uniformly dispersed throughout the uncrosslinked polymer; and thereafter crosslinking said polymer.
Claim 4
Independent Claim
114 words
A method of improving the reinforcing properties of carbon black in elastomeric polymers comprising the steps of attriting the carbon black particles to substantially reduce their size and lower their pH; mixing said attrited carbon black with the polymer before it is crosslinked; subjecting said mixture to shear stress while it is at a first temperature between the glass transition temperature and the liquid-liquid transition temperature of the uncrosslinked polymer; working said mixture at a second temperature above the flow temperature of the uncrosslinked polymer to eliminate microvoids therein; repeating said steps at said first and second temperatures until the attrited black is uniformly dispersed throughout the uncrosslinked polymer; and thereafter crosslinking said polymer.
Claim 5
Dependent Claim
11 words
The method of claim 1 where the elastomeric polymer is polychloroprene.
Claim 6
Dependent Claim
24 words
The method of claim 1 where the elastomeric polymer is taken from the group consisting of polychloroprene, polypropylene oxide, chlorosulfonated polyethylene and natural rubber.
Claim 7
Dependent Claim
17 words
The method of claim 1 where the improved physical properties include increased tensile strength and ultimate elongation.
Claim 8
Dependent Claim
12 words
The method of claim 1 where the particulate filler is carbon black.
Claim 9
Dependent Claim
12 words
The method of claim 1 where the particulate filler is silicon dioxide.
Claim 10
Dependent Claim
11 words
The method of claim 2 where the elastomeric polymer is polychloroprene.
Claim 11
Dependent Claim
24 words
The method of claim 2 where the elastomeric polymer is taken from the group consisting of polychloroprene, polypropylene oxide, chlorosulfonated polyethylene and natural rubber.
References Cited (Backward Citations)
US4285897A
Cited
US4342670A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-12 | 1987-06-13 | 1987-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-12 | 1991-06-13 | 1991-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-12 | 1995-06-13 | 1995-12-13 | $7700.00 | Window Closed / Lapsed |