Abrasion-resistant granular zeolite and process for preparation thereof
Assignee: Mizusawa Industrial Chemicals Ltd
•
Filing: 1982-03-08
•
Granted: 1983-12-13
•
Expires: 2002-03-08
Abstract
Abstract Disclosed is an abrasion-resistant granular zeolite formed from a mixture of a synthetic zeolite and a clay binder, said granular zeolite comprising a core composed of a synthetic zeolite clay binder mixture containing the synthetic zeolite at a content higher than the average synthetic zeolite content in the granular zeolite and a shell composed of a synthetic zeolite-clay binder mixture containing the clay binder at a content higher than the average clay binder content in the granular zeolite. This granular zeolite is excellent in both the zeolitic characteristics such as adsorbability and ion exchange capacity and the mechanical strength characteristics such as abrasion resistance and compression strength.
Inventors
- 👤 Masahide Ogawa
- 👤 Tetsuo Masuko
- 👤 Kunio Goto
- 👤 Hideo Sugai
- 👤 Masao Takahashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 10:14
CPC Classifications
B; B01; B01J; B01J20/00; B01J20/28; B01J20/28014; B01J20/28016; B01J20/28019; B01D; B01D53/00; B01D53/26; B01D53/28; B01J20/02; B01J20/10; B01J20/16; B01J20/18; B01J20/183; B01J20/30; B01J20/32; B01J20/3291; B01J20/3293; B01J39/00; B01J39/08; B01J39/14; C; C01; C01B; C01B3/00; C01B3/50; C01B3/56; C01B2203/00; C01B2203/04; C01B2203/042; C01B2203/0465; C01B2203/047; C01B2203/0475; C01B2203/0485; C01B2203/0495; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
168 words
An abrasion-resistant granular zeolite formed from a mixture of a synthetic crystalline zeolite and a clay binder, said granular zeolite comprising a core composed of a synthetic zeolite-clay binder mixture containing the synthetic zeolite at a content higher than the average synthetic zeolite content in the total granular zeolite and a shell composed of a synthetic zeolite-clay binder mixture containing the clay binder at a content higher than the average clay binder content in the total granular zeolite, wherein the core and shell are present at a core/shell weight ratio of from 99/1 to 80/20, the core contains the synthetic zeolite and clay binder at a zeolite/binder weight ratio of from 90/10 to 60/40, the shell contains the clay binder and synthetic zeolite at a binder/zeolite weight ratio of from 95/5 to 30/70, the shell contains the clay binder at a content higher by at least 10 by weight than the binder content in the core, and said core and shell being calcined to harden the clay binder.
Claim 2
Dependent Claim
168 words
An abrasion-resistant granular zeolite formed from a mixture of a synthetic crystalline zeolite and a clay binder, said granular zeolite comprising a core composed of a synthetic zeolite-clay binder mixture containing the synthetic zeolite at a content higher than the average synthetic zeolite content in the total granular zeolite and a shell composed of a synthetic zeolite-clay binder mixture containing the clay binder at a content higher than the average clay binder content in the total granular zeolite, wherein the core and shell are present at a core/shell weight ratio of from 99/1 to 80/20, the core contains the synthetic zeolite and clay binder at a zeolite/binder weight ratio of from 90/10 to 60/40, the shell contains the clay binder and synthetic zeolite at a binder/zeolite weight ratio of from 95/5 to 30/70, the shell contains the clay binder at a content higher by at least 10 by weight than the binder content in the core, and said core and shell being calcined to harden the clay binder.
Claim 3
Dependent Claim
23 words
A granular zeolite as set forth in claim 1, wherein the synthetic zeolite is zeolite A, zeolite X, zeolite Y or synthetic mordenite.
Claim 4
Dependent Claim
28 words
A granular zeolite as set forth in claim 1, wherein the clay binder is a kaolin type clay mineral, a palygorskite clay mineral or a smectite clay mineral.
Claim 5
Dependent Claim
25 words
A granular zeolite as set forth in claim 1, wherein core and shell are present at a core/shell weight ratio of from 98/2 to 85/15.
Claim 6
Dependent Claim
72 words
A granular zeolite as set forth in claim 1, wherein the core contains the synthetic zeolite and clay binder at a zeolite/binder weight ratio of from 88/12 to 70/30, the shell contains the clay binder and synthetic zeolite at a binder/zeolite weight ratio of from 70/30 to 50/50, and the shell contains the clay binder at a content higher by at least 15% by weight than the binder content in the core.
Claim 7
Dependent Claim
136 words
A process for the preparation of an abrasion-resistant granular zeolite, which comprises the steps of granulating a primary mixture containing a synthetic zeolite and a clay binder at a zeolite/binder weight ratio of from 90/10 to 60/40 by using an aqueous solution of a water-soluble polymeric binder as a granulating medium, thereby to form wet core particles, dry-blending the resulting wet core particles with a secondary powdery mixture containing the synthetic zeolite and the clay binder at a binder/zeolite weight ratio of from 95/5 to 30/70 to form a shell coating of said powdery mixture on the surface of the core particles, said secondary mixture containing the clay binder at a content higher by at least 10% by weight than the clay binder content in the primary mixture and drying and calcining the resulting coated particles.
Claim 8
Dependent Claim
136 words
A process for the preparation of an abrasion-resistant granular zeolite, which comprises the steps of granulating a primary mixture containing a synthetic zeolite and a clay binder at a zeolite/binder weight ratio of from 90/10 to 60/40 by using an aqueous solution of a water-soluble polymeric binder as a granulating medium, thereby to form wet core particles, dry-blending the resulting wet core particles with a secondary powdery mixture containing the synthetic zeolite and the clay binder at a binder/zeolite weight ratio of from 95/5 to 30/70 to form a shell coating of said powdery mixture on the surface of the core particles, said secondary mixture containing the clay binder at a content higher by at least 10% by weight than the clay binder content in the primary mixture and drying and calcining the resulting coated particles.
Claim 9
Dependent Claim
54 words
A process according to claim 6, wherein the water-soluble polymeric binder is present in an amount of 0.01 to 5% by weight, as solids, based on the total amount of the synthetic zeolite and clay binder and the amount of said aqueous solution is 20 to 70% by weight based on the total amount.
Claim 10
Dependent Claim
39 words
A process according to claim 6, wherein granulation of the core is performed by rolling granulation, and the secondary powdery mixture for the shell is added to the resulting wet core particles and rolling granulation is carried out again.
References Cited (Backward Citations)
US2973327A
Cited
US3055841A
Cited
US3065054A
Cited
US3262890A
Cited
US3219590A
Cited
US3181231A
Cited
US3356450A
Cited
US4157375A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-12 | 1987-06-13 | 1987-12-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-12 | 1991-06-13 | 1991-12-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-12 | 1995-06-13 | 1995-12-13 | $7700.00 | Window Closed / Lapsed |