Method for production of high fluoride compatibility dentifrice abrasives and compositions

Claim 1

A method for the production of an abrasive composition comprising a precipitated amorphous silicon dioxide, which silicon dioxide has been prepared from a fresh water alkali metal silicate solution by acidulation, and has been intimately reacted with a compound of an alkaline earth metal so as to have present therein about 10-300 parts per million of alkaline earth metal ions in said amorphous silicon dioxide and which exhibits a Radioactive Dentin Abrasion value of at least 40, a pack density of about 0.24 to 0.55 grams per milliliter, an oil absorption of about 70-95 ccs/100 grams, a BET surface area of about 100-250 m 2 /g, and a percent loss on ignition of about 4-6%, said abrasive composition, when incorporated into toothpaste compositions containing a fluoride therapeutic agent, providing a toothpaste composition which exhibits minimal loss of soluble fluoride upon storage at normal temperatures, and providing a fluoride compatibility value to the toothpaste of at least 90%, said method comprising (a) forming an aqueous solution of an alkali metal silicate having an SiO 2 to X 2 O mole ratio of about 2.0 to 2.7, wherein X is alkali metal, at a reaction temperature in the range of about 77° to 91° C., (b) acidulating said alkali metal silicate solution with a mineral acid until precipitation of silicon dioxide is substantially complete, then continuing the mineral acid addition until the pH is 6.0 or less, (c) digesting by heating at a temperature for a period of 10-30 minutes, (d) filtering the resulting slurry and washing the solid product with fresh water, (e) reslurrying the resulting wet cake in water and under agitation conditions, (f) adding sufficient alkaline earth metal ion in the form of a sufficiently soluble alkaline earth metal compound in sufficient amount to add to said wet cake alkaline earth metal ions in the range of 10-300 parts per million based on the dry recoverable product in said slurry, (g) agitating the resulting mixture to provide adherence of the effective level of said alkaline earth metal treatment on the surface of said silicon dioxide, and (h) drying and recovering the solid abrasive composition.

Claim 2

A method for the production of an abrasive composition comprising a precipitated amorphous silicon dioxide, which silicon dioxide has been prepared from a fresh water alkali metal silicate solution by acidulation, and has been intimately reacted with a compound of an alkaline earth metal so as to have present therein about 10-300 parts per million of alkaline earth metal ions in said amorphous silicon dioxide and which exhibits a Radioactive Dentin Abrasion value of at least 40, a pack density of about 0.24 to 0.55 grams per milliliter, an oil absorption of about 70-95 ccs/100 grams, a BET surface area of about 100-250 m 2 /g, and a percent loss on ignition of about 4-6%, said abrasive composition, when incorporated into toothpaste compositions containing a fluoride therapeutic agent, providing a toothpaste composition which exhibits minimal loss of soluble fluoride upon storage at normal temperatures, and providing a fluoride compatibility value to the toothpaste of at least 90%, said method comprising (a) forming an aqueous solution of an alkali metal silicate having an SiO 2 to X 2 O mole ratio of about 2.0 to 2.7, wherein X is alkali metal, at a reaction temperature in the range of about 77° to 91° C., (b) acidulating said alkali metal silicate solution with a mineral acid until precipitation of silicon dioxide is substantially complete, then continuing the mineral acid addition until the pH is 6.0 or less, (c) digesting by heating at a temperature for a period of 10-30 minutes, (d) filtering the resulting slurry and washing the solid product with fresh water, (e) reslurrying the resulting wet cake in water and under agitation conditions, (f) adding sufficient alkaline earth metal ion in the form of a sufficiently soluble alkaline earth metal compound in sufficient amount to add to said wet cake alkaline earth metal ions in the range of 10-300 parts per million based on the dry recoverable product in said slurry, (g) agitating the resulting mixture to provide adherence of the effective level of said alkaline earth metal treatment on the surface of said silicon dioxide, and (h) drying and recovering the solid abrasive composition.