Process for preparing ABS polymeric polyblends
Assignee: Bayer Antwerpen NV
•
Filing: 1981-08-06
•
Granted: 1983-12-06
•
Expires: 2001-08-06
Abstract
Abstract The invention relates to a process for preparing ABS polyblends having small and large grafted rubber particles dispersed therein providing polyblends having greater toughness and chemical resistance. The process includes extracting small grafted rubber particles into a separated monomer phase which is mass polymerized to a first melt, mixing said first melt with a second melt having present larger grafted rubber particles to form a third melt which is devolatilized to an ABS polyblend having a bimodal grafted rubber particle size distribution.
Inventors
- 👤 Robert H. M. Simon
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 21:40
CPC Classifications
C; C08; C08F; C08F285/00; C08F279/00; C08F279/02; C08F279/04
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
363 words
A process for producing ABS polymeric polyblends having dispersed alkadiene rubber particles grafted with monovinylidene aromatic and alkenenitrile monomers, said rubber particles having a bimodal rubber particle size distribution and being dispersed in a matrix copolymer of said monomers, the sequential steps: consisting essentially of: A. grafting by aqueous emulsion graft polymerization an alkadiene rubber with a monovinylidene aromatic monomer and an alkenenitrile monomer to produce first graft rubber particles in an aqueous latex having a particle size of about 0.01 to 0.8 microns, B. mixing with said latex, having 30 to 400 parts per hundred parts of latex rubber solids by weight, at least one additional monoethylenically unsaturated monomer selected from the group consisting of monovinylidene aromatic monomers and alkenenitrile monomers, C. extracting said first grafted rubber particles from said aqueous latex into the additional monomer forming a dispersion of said particles in the additional monomer, and leaving a separate free water phase, D. separating said free water phase from said additional monomer containing the first grafted rubber particles and adjusting said additional monomer with at least one monoethylenically unsaturated monomer such that the weight ratio of monoethylenically unsaturated aromatic to alkenyl nitrile monomer is about 80:20 to 20:80, E. subjecting said first grafted rubber particles dispersed in said adjusted additional monomer having said weight ratio to mass polymerization conditions to produce a composition comprising said grafted rubber particles dispersed in a first matrix copolymer of said adjusted additional monomers as a first melt, F. mixing said first melt with a second melt prepared by mass polymerization forming a second matrix copolymer of monovinylidene aromatic and alkenyl nitrile monomers having second grafted rubber particles dispersed therein, said second particles having a rubber particle size of about 1.0 to 10 microns being grafted with alkenyl nitrile and monovinylidene aromatic monomers forming a third melt having said first and second grafted rubber particles dispersed in said first and second matrix copolymers, G. devolatilizing said third melt so as to remove unreacted monomers providing said ABS polyblend comprising said first and second matrix copolymers having said first and second grafted rubber particles dispersed therein such that said rubber particles have a bimodal particle size distribution.
Claim 2
Dependent Claim
363 words
A process for producing ABS polymeric polyblends having dispersed alkadiene rubber particles grafted with monovinylidene aromatic and alkenenitrile monomers, said rubber particles having a bimodal rubber particle size distribution and being dispersed in a matrix copolymer of said monomers, the sequential steps: consisting essentially of: A. grafting by aqueous emulsion graft polymerization an alkadiene rubber with a monovinylidene aromatic monomer and an alkenenitrile monomer to produce first graft rubber particles in an aqueous latex having a particle size of about 0.01 to 0.8 microns, B. mixing with said latex, having 30 to 400 parts per hundred parts of latex rubber solids by weight, at least one additional monoethylenically unsaturated monomer selected from the group consisting of monovinylidene aromatic monomers and alkenenitrile monomers, C. extracting said first grafted rubber particles from said aqueous latex into the additional monomer forming a dispersion of said particles in the additional monomer, and leaving a separate free water phase, D. separating said free water phase from said additional monomer containing the first grafted rubber particles and adjusting said additional monomer with at least one monoethylenically unsaturated monomer such that the weight ratio of monoethylenically unsaturated aromatic to alkenyl nitrile monomer is about 80:20 to 20:80, E. subjecting said first grafted rubber particles dispersed in said adjusted additional monomer having said weight ratio to mass polymerization conditions to produce a composition comprising said grafted rubber particles dispersed in a first matrix copolymer of said adjusted additional monomers as a first melt, F. mixing said first melt with a second melt prepared by mass polymerization forming a second matrix copolymer of monovinylidene aromatic and alkenyl nitrile monomers having second grafted rubber particles dispersed therein, said second particles having a rubber particle size of about 1.0 to 10 microns being grafted with alkenyl nitrile and monovinylidene aromatic monomers forming a third melt having said first and second grafted rubber particles dispersed in said first and second matrix copolymers, G. devolatilizing said third melt so as to remove unreacted monomers providing said ABS polyblend comprising said first and second matrix copolymers having said first and second grafted rubber particles dispersed therein such that said rubber particles have a bimodal particle size distribution.
Claim 3
Dependent Claim
25 words
A process of claim 1 wherein said monovinylidene aromatic monomer is selected from the group consisting of styrene, alphamethyl styrene, chlorostyrene, bromostyrene and paramethyl styrene.
Claim 4
Dependent Claim
19 words
A process of claim 1 wherein said alkenenitrile monomer is selected from the group consisting of acrylonitrile and methacrylonitrile.
Claim 5
Dependent Claim
33 words
A process of claim 1 wherein said monoethylenically unsaturated monomers used in step (B) are a mixture of styrene and acrylonitrile, said mixture containing not more than about 50% by weight of styrene.
Claim 6
Dependent Claim
14 words
A process of claim 1 wherein said monomer used in step (B) is styrene.
Claim 7
Dependent Claim
14 words
A process of claim 1 wherein said monomer used in step (B) is acrylonitrile.
Claim 8
Dependent Claim
58 words
A process of claim 1 wherein said adjusted additional monomer having said weight ratio is adjusted in step (E) with said aromatic and nitrile monomers such that the rubber moiety of the dispersed rubber particles is present in the ABS polyblend formed in step (G) in an amount of 3 to 50% by weight of said ABS polyblend.
Claim 9
Dependent Claim
26 words
A process of claim 1 wherein said third melt is heated to temperatures of 180° to 250° C. before devolatilization is carried out in step (G).
Claim 10
Dependent Claim
17 words
A process of claim 1 wherein said mass polymerization is carried out at 100° to 200° C.
Claim 11
Dependent Claim
31 words
A process of claim 1 wherein said mass polymerization is carried out under continuous mass polymerization conditions in a stirred tank flow through reactor being cooled by evaporation of said monomers.
Claim 12
Dependent Claim
18 words
A process of claim 1 wherein said grafted rubber latex is coagulated prior to extraction into said monomer.
Claim 13
Dependent Claim
34 words
A process of claim 11 wherein said coagulation is carried out by mixing said latex with a sufficient amount of a coagulant selected from the group consisting of acids, salts, polyelectrolytes and cationic surfactants.
Claim 14
Dependent Claim
16 words
A process of claim 12 wherein said salt is aluminum sulfate, sodium chloride or magnesium sulfate.
Claim 15
Dependent Claim
31 words
A process of claim 1 wherein said additional monomer used in step (B) contain at least one saturated solvent for a graft copolymer of said monovinylidene aromatic and alkenyl nitrile monomers.
Claim 16
Dependent Claim
38 words
A process of claim 14 wherein said solvent has a boiling point between 25° to 250° C. as is present in said monomers in an amount of about 10 to 40% by weight of said monomers and solvent.
Claim 17
Dependent Claim
27 words
A process of claim 15 wherein said solvent is selected from the group consisting of nitriles, hydrocarbons, halogenated hydrocarbons, lower carboxylic esters, cyclic ethers, formamides and acetamides.
Claim 18
Dependent Claim
10 words
A process of claim 16 wherein said solvent is propionitrile.
Claim 19
Dependent Claim
15 words
A process of claim 14 wherein the graft and matrix copolymer is a styrene-acrylonitrile copolymer.
Claim 20
Dependent Claim
61 words
A process of claim 1 wherein said mass polymerization is carried out to about 50 to 90% conversion of said monomers wherein said rubber becomes dispersed as second grafted rubber particles having a particle size of about 1.0 to 10 microns and having present about 1 to 5 parts of said monomers as grafted and occluded copolymer per part of rubber.
Claim 21
Dependent Claim
66 words
A process of claim 1 wherein said first melt and said second melt are mixed in weight ratios such that the rubber moiety of said ABS polyblend is about 50 to 90% by weight of said first grafted rubber particles and 10 to 50% by weight of said second grafted rubber particles, said rubber moiety being about 5 to 50% by weight of said ABS polyblend.
Claim 22
Dependent Claim
24 words
A process of claim 1 wherein said first melt has a rubber moiety of about 15 to 45% by weight based on said melt.
Claim 23
Dependent Claim
24 words
A process of claim 1 wherein said second melt has a rubber moiety of about 2 to 15% by weight based on said melt.
Claim 24
Dependent Claim
29 words
A process of claim 1 wherein said first grafted rubber particles have present about 10 to 250 parts of said monomer grafted as copolymer per 100 parts of rubber.
Claim 25
Dependent Claim
66 words
A process of claim 1 wherein steps (E), (F) and (G) are carried out continuously by feeding said adjusted additional monomer having said weight ratio continuously to a mass polymerization reaction zone forming said first melt continuously as an effluent from said zone, mixing said second melt continuously with said first melt forming said third melt and continuously devolatilizing said third melt to said ABS polyblend.
Claim 26
Dependent Claim
52 words
A process of claim 1 wherein said second melt has been extended with additional matrix copolymer in amounts sufficient to prepare said polyblends with a matrix phase of about 55 to 95% by weight of said polyblend wherein said additional matrix copolymer is comprised of said monovinylidene aromatic and alkenyl nitrile monomers.
References Cited (Backward Citations)
US3576910A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-05 | 1987-06-06 | 1987-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-05 | 1991-06-06 | 1991-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-05 | 1995-06-06 | 1995-12-06 | $7700.00 | Window Closed / Lapsed |