Powder molding method and powder compression molded composite article having a rest-curve like boundary
Assignee: Nippon Piston Ring Co Ltd
•
Filing: 1982-02-23
•
Granted: 1983-12-06
•
Expires: 2002-02-23
Abstract
Abstract A powder compression molding method for producing a multilayer powder compression molded article having a plurality of different material layers disposed in a compression direction utilizes relative movements between an upper punch, a lower punch, a die having a step formed therein, and two feed shoes. The powder compression molded article thus formed requires a reduced amount of a special layer. The powder compression molding method includes forming a first space by moving the die relative to the lower punch, introducing a first powder into the first space through a first feed shoe, lowering the lower punch relative to the die to form a second space so that an upper surface of the first powder on the step of the die and on the lower punch has a nonuniform height, introducing a second powder into the second space, and moving the upper punch towards the lower punch to compress the first and second powders.
Inventors
- 👤 Tadashi Ebihara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:33
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/02; B22F3/03; B22F7/00; B22F7/06; B30; B30B; B30B11/00; B30B11/02; B30B11/027; B30B15/00; B30B15/30; B30B15/302; B30B15/304; B30B15/306; F; F01; F01L; F01L3/00; F01L3/22; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12042; Y10T428/12146
Claims Analysis
Total Claims: 41
Claim 1
Independent Claim
120 words
A powder compression molding method for producing a multi-layer powder compression molded article having a plurality of different material layers disposed in a compression direction by utilizing relative movements of an upper punch, a lower punch, a die, and first and second feed shoes, the method comprising the steps of: forming a first space between the die and the lower punch, the die having a step formed therein; introducing a first powder into the first space; lowering the lower punch relative to the die to form a second space above a top surface of the first powder; introducing a second powder into the second space; and compressing the first and second powders to form the multi-layer powder compression molded article.
Claim 2
Dependent Claim
120 words
A powder compression molding method for producing a multi-layer powder compression molded article having a plurality of different material layers disposed in a compression direction by utilizing relative movements of an upper punch, a lower punch, a die, and first and second feed shoes, the method comprising the steps of: forming a first space between the die and the lower punch, the die having a step formed therein; introducing a first powder into the first space; lowering the lower punch relative to the die to form a second space above a top surface of the first powder; introducing a second powder into the second space; and compressing the first and second powders to form the multi-layer powder compression molded article.
Claim 3
Dependent Claim
22 words
The method claimed in claim 1, wherein the step is formed on at least part of an inside surface of the die.
Claim 4
Dependent Claim
19 words
The method claimed in claim 2, wherein the step is formed on the entire inside surface of the die.
Claim 5
Dependent Claim
49 words
The method claimed in claim 2 wherein lowering the lower punch relative to the die forms the top surface of the first powder over the step of the die and over the lower punch, the top surface of the first powder having a non-uniform height in the compression direction.
Claim 6
Dependent Claim
36 words
The method claimed in claim 4, wherein a shape of the top surface is controlled by controlling the rate of relative descent and the total amount of relative descent between the lower punch and the die.
Claim 7
Dependent Claim
36 words
The method claimed in claim 5, wherein the first powder is introduced into the first space by the first feed shoe and the second powder is introduced into the second space by the second feed shoe.
Claim 8
Dependent Claim
39 words
The method claimed in claim 6, further comprising the step of removing the compression molded article by raising the upper punch relative to the die and the lower punch and then raising the lower punch relative to the die.
Claim 9
Dependent Claim
56 words
The method claimed in claim 7, further comprising the step of placing the first feed shoe at a suction charging point prior to the introduction of the first powder into the first space; and placing the second feed shoe at a second charging point prior to the introduction of the second powder into the second space.
Claim 10
Dependent Claim
33 words
The method claimed in claim 8, wherein the second powder is introduced into the second space simultaneously with the relative movement between the die and the lower punch when forming the second space.
Claim 11
Dependent Claim
27 words
The method claimed in claim 6, wherein the first and second powders are compressed by lowering the upper punch relative to the die and the lower punch.
Claim 12
Dependent Claim
24 words
The method claimed in claim 10, wherein the first and second powders are compressed by also raising the lower punch relative to the step.
Claim 13
Dependent Claim
36 words
The method claimed in claim 11, wherein a final position of a top surface of the lower punch is even with a bottom surface of the step after the first and second powders have been compressed.
Claim 14
Dependent Claim
35 words
The method claimed in claim 11, wherein a final position of a top surface of the lower punch is below a bottom surface of the step after the first and second powders have been compressed.
Claim 15
Dependent Claim
35 words
The method claimed in claim 11, wherein a final position of a top surface of the lower punch is above a bottom surface of the step after the first and second powders have been compressed.
Claim 16
Dependent Claim
34 words
The method claimed in claim 12, 13 or 14, wherein while compressing the first and second powders, the lower punch is raised and the upper punch is lowered simultaneously at approximately the same speed.
Claim 17
Dependent Claim
40 words
The method claimed in claim 12, 13 or 14, wherein while compressing the first and second powders, after the upper punch contacts the top surface of the second powder only the upper punch is moved to cause the powder compression.
Claim 18
Dependent Claim
134 words
A powder compression molding method for producing a multi-layer powder compression molded article having a plurality of different material layers disposed in a compression direction by utilizing relative movements of an upper punch, a lower punch, a die, a core rod, and first and second shoes, the method comprising the steps of: forming a first space between the die, core rod, and the lower punch, at least one of the die and the core rod having a step formed therein; introducing a first powder into the first space; lowering the lower punch relative to the die and the core rod to form a second space above a top surface of the first powder; introducing a second powder into the second space; and compressing the first and second powders to form the compression molded article.
Claim 19
Dependent Claim
134 words
A powder compression molding method for producing a multi-layer powder compression molded article having a plurality of different material layers disposed in a compression direction by utilizing relative movements of an upper punch, a lower punch, a die, a core rod, and first and second shoes, the method comprising the steps of: forming a first space between the die, core rod, and the lower punch, at least one of the die and the core rod having a step formed therein; introducing a first powder into the first space; lowering the lower punch relative to the die and the core rod to form a second space above a top surface of the first powder; introducing a second powder into the second space; and compressing the first and second powders to form the compression molded article.
Claim 20
Dependent Claim
22 words
The method claimed in claim 17, wherein the step is formed on at least part of an inside surface of the die.
Claim 21
Dependent Claim
24 words
The method claimed in claim 18, wherein an additional step is formed on at least part of an outside surface of the core rod.
Claim 22
Dependent Claim
57 words
The method claimed in claim 19, wherein the top surface of the first powder is highest in the compression direction at opposite sides of the molded article which are parallel to the compression direction, and the height of the top surface in the compression direction is smallest approximately midway between the opposite sides of the molded article.
Claim 23
Dependent Claim
45 words
The method claimed in claim 17, wherein lowering the lower punch relative to the die forms the top surface of the first powder over the at least one step and over the lower punch, the top surface having a non-uniform height in the compression direction.
Claim 24
Dependent Claim
42 words
The method claimed in claim 21 or 20, wherein a shape of the top surface of the first powder is controlled by controlling the rate of relative descent and the total amount of relative descent between the lower punch and the die.
Claim 25
Dependent Claim
36 words
The method claimed in claim 17, wherein the first powder is introduced into the first space by the first feed shoe and the second powder is introduced into the second space by the second feed shoe.
Claim 26
Dependent Claim
40 words
The method claimed in claim 23, wherein the first and second powders are compressed by lowering the upper punch relative to the die, the core rod and the lower punch, and the lower punch is raised relative to the step.
Claim 27
Dependent Claim
35 words
The method claimed in claim 24, wherein a final position of a top surface of the lower punch is even with the bottom surface of at least one of the steps after the powder compression.
Claim 28
Dependent Claim
34 words
The method claimed in claim 24, wherein a final position of a top surface of the lower punch is below a bottom surface of at least one of the steps after the powder compression.
Claim 29
Dependent Claim
34 words
The method claimed in claim 24, wherein a final position of a top surface of the lower punch is above a bottom surface of at least one of the steps after the powder compression.
Claim 30
Dependent Claim
31 words
The method claimed in claim 24, wherein while compressing the first and second powders, the lower punch is raised and the upper punch is lowered simultaneously at approximately the same speed.
Claim 31
Dependent Claim
37 words
The method claimed in claim 24, wherein while compressing the first and second powders, after the upper punch contacts the top surface of the second powder only the upper punch is moved to cause the powder compression.
Claim 32
Dependent Claim
42 words
The method claimed in claim 24, further comprising the step of removing the compression molded article by raising the upper punch relative to the die, the core rod and the lower punch, and then raising the lower punch relative to the die.
Claim 33
Dependent Claim
56 words
The method claimed in claim 23, further comprising the steps of placing the first feed shoe at a suction charging point prior to the introduction of the first powder into the first space; and placing the second feed shoe at a second charging point prior to the introduction of the second powder into the second space.
Claim 34
Dependent Claim
33 words
The method claimed in claim 31, wherein the first powder is introduced into the second space simultaneously with the relative movement between the die and the lower punch when forming the second space.
Claim 35
Dependent Claim
77 words
A powder compression molded article comprising a first and a second layer, the first and second layers comprising different materials, a boundary between the different material layers having a rest-curve like shape formed by relative movement between a punch and a die after said first layer in powder form is deposited on an upper surface of said punch and said die but prior to said second layer in powder form being deposited on said first powder layer.
Claim 36
Dependent Claim
77 words
A powder compression molded article comprising a first and a second layer, the first and second layers comprising different materials, a boundary between the different material layers having a rest-curve like shape formed by relative movement between a punch and a die after said first layer in powder form is deposited on an upper surface of said punch and said die but prior to said second layer in powder form being deposited on said first powder layer.
Claim 37
Dependent Claim
16 words
The article claimed in claim 33, wherein said powder compression molded article comprises a metallurgical article.
Claim 38
Dependent Claim
52 words
The article claimed in claim 33, wherein the boundary layer in cross section is highest in the compression direction at opposite sides of the molded article which are parallel to the compression direction and the height of the boundary layer in the compression direction is smallest about midway between the opposite sides.
Claim 39
Dependent Claim
16 words
The article claimed in claim 35, wherein said powder compression molded article comprises a metallurgical article.
Claim 40
Dependent Claim
91 words
The article claimed in claim 33 wherein the second powder layer in cross section has a shape resembling a triangle with an edge of the second powder layer being a vertex of the triangle, the height of the second layer in the compression direction being smallest at a first side of the article and the height of the second layer continuously increasing and being largest at a second side of the molded article which is opposite to the first side, the first and second sides being parallel to the compression direction.
Claim 41
Dependent Claim
16 words
The article claimed in claim 37, wherein said powder compression molded article comprises a metallurgical article.
References Cited (Backward Citations)
US2208054A
Cited
US2753859A
Cited
US2753858A
Cited
US3198856A
Cited
US3391444A
Cited
US3666456A
Cited
US3752003A
Cited
US3770332A
Cited
US3938814A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-05 | 1987-06-06 | 1987-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-05 | 1991-06-06 | 1991-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-05 | 1995-06-06 | 1995-12-06 | $7700.00 | Window Closed / Lapsed |