Plasma polymerized color coatings
Assignee: Battelle Development Corp
•
Filing: 1981-12-14
•
Granted: 1983-12-06
•
Expires: 2001-12-14
Abstract
Abstract Thin, pinhole-free, adherent, colored polymeric coatings and articles are produced by plasma polymerization followed by a heat treatment. The polymer precursor is mixed with a dye or pigment and shaped into a self-supporting thin article or applied to a substrate. The coating or article is then polymerized under plasma conditions created by an applied electrical field. Subsequent heat treatment further cures the polymer and makes the coating adherent to the substrate.
Inventors
- 👤 Francis A. Sliemers
- 👤 Vincent D. McGinniss
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 11:21
CPC Classifications
C; C08; C08F; C08F2/00; C08F2/46; C08F2/52; B; B05; B05D; B05D3/00; B05D3/14; B05D3/141; B05D3/145; B05D3/147; B29; B29C; B29C71/00; B29C71/02; B05D3/02; B05D3/0209; B05D3/0254; B05D3/04; B05D3/0486; B05D3/0493; B29C2791/00; B29C2791/001; B29K; B29K2105/00; B29K2105/24
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
138 words
A process for producing an adherent, colored-polymer coating on a substrate comprising (A) coating a substrate with a layer of a plasma-reactive precursor and an additive comprising a dye, pigment or a material capable of reacting under plasma conditions to form a dye or pigment, (B) introducing the coated substrate into plasma polymerization apparatus having a low-pressure environment comprising a plasma-forming inert gas, (C) producing a glow discharge for a time sufficient to form a plasma from the inert gas and to initiate free radical formation, polymerization and crosslinking throughout the thickness of the plasma reactive precursor layer forming a partially cured coating on the substrate, and thereafter (D) heat treating the partially cured coating at a temperature and for a time sufficient to complete the cure reaction and increase the adherence of the coating to the substrate.
Claim 2
Dependent Claim
138 words
A process for producing an adherent, colored-polymer coating on a substrate comprising (A) coating a substrate with a layer of a plasma-reactive precursor and an additive comprising a dye, pigment or a material capable of reacting under plasma conditions to form a dye or pigment, (B) introducing the coated substrate into plasma polymerization apparatus having a low-pressure environment comprising a plasma-forming inert gas, (C) producing a glow discharge for a time sufficient to form a plasma from the inert gas and to initiate free radical formation, polymerization and crosslinking throughout the thickness of the plasma reactive precursor layer forming a partially cured coating on the substrate, and thereafter (D) heat treating the partially cured coating at a temperature and for a time sufficient to complete the cure reaction and increase the adherence of the coating to the substrate.
Claim 3
Dependent Claim
15 words
The process of claim 1 which comprises heat treating the plasma-exposed layer in non-oxidizing atmosphere.
Claim 4
Dependent Claim
16 words
The process of claim 2 which comprises heat treating the plasma-exposed layer in a low-pressure environment.
Claim 5
Dependent Claim
29 words
The process of claim 1 wherein the heat treatment is carried out at a temperature of at least about 10° C. above the glass transition temperature of the precursor.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-12-05 | 1987-06-06 | 1987-12-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-12-05 | 1991-06-06 | 1991-12-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-12-05 | 1995-06-06 | 1995-12-06 | $7700.00 | Window Closed / Lapsed |