US4418182A — High solids coatings from new tetrahydroxy oligom…

Claim 1

Independent Claim 216 words

A thermosetting coating composition adapted for low temperature bake applications comprising: (A) a tetrahydroxy oligomer having a number average molecular weight of between about 600-2000 and being the reaction product of: (i) an ester containing pendant hydroxyl and carboxyl functionality and being made by a reaction wherein the reactants consist essentially of: (a) a C 3 -C 10 aliphatic branched diol and (b) an alkyl hexahydrophthalic anhydride, wherein (a) and (b) are combined in the reaction mixture in an amount sufficient to allow reaction in about a 1:1 molar ratio; and (ii) a diepoxide having a number average molecular weight between about 130-1500, wherein (i) and (ii) are combined in the reaction mixture in an amount sufficient to allow reaction in about a 2:1 molar ratio; (B) an amine-aldehyde crosslinking agent; (C) 0-50 weight percent based on the total weight of (A), (B), (C) and (D) of a hydroxy functional additive having a number average molecular weight (M n ) of between about 150-6000; and (D) solvent, said amine-aldehyde crosslinking agent being included in said composition in an amount sufficient to provide at least about 0.60 equivalents of nitrogen crosslinking functionality for each equivalent of hydroxyl functionality included in said composition either on said tetrahydroxy oligomer or as a hydroxyl group of said hydroxy functional additive.

Claim 2

Dependent Claim 216 words

A thermosetting coating composition adapted for low temperature bake applications comprising: (A) a tetrahydroxy oligomer having a number average molecular weight of between about 600-2000 and being the reaction product of: (i) an ester containing pendant hydroxyl and carboxyl functionality and being made by a reaction wherein the reactants consist essentially of: (a) a C 3 -C 10 aliphatic branched diol and (b) an alkyl hexahydrophthalic anhydride, wherein (a) and (b) are combined in the reaction mixture in an amount sufficient to allow reaction in about a 1:1 molar ratio; and (ii) a diepoxide having a number average molecular weight between about 130-1500, wherein (i) and (ii) are combined in the reaction mixture in an amount sufficient to allow reaction in about a 2:1 molar ratio; (B) an amine-aldehyde crosslinking agent; (C) 0-50 weight percent based on the total weight of (A), (B), (C) and (D) of a hydroxy functional additive having a number average molecular weight (M n ) of between about 150-6000; and (D) solvent, said amine-aldehyde crosslinking agent being included in said composition in an amount sufficient to provide at least about 0.60 equivalents of nitrogen crosslinking functionality for each equivalent of hydroxyl functionality included in said composition either on said tetrahydroxy oligomer or as a hydroxyl group of said hydroxy functional additive.

Claim 3

Dependent Claim 19 words

A high solids coating composition according to claim 1, wherein said aliphatic branched diol contains one primary hydroxyl group.

Claim 4

Dependent Claim 21 words

A coating composition according to claim 2 wherein the hydroxyl groups of said diol are not attached to adjacent carbon atoms.

Claim 5

Dependent Claim 13 words

A coating composition according to claim 3, wherein said diol is 2-ethyl-1,3-hexane diol.

Claim 6

Dependent Claim 27 words

A coating composition according to claim 1, wherein the alkyl group of said alkyl hexahydrophthalic anhydride comprises a lower alkyl group having up to about seven carbons.

Claim 7

Dependent Claim 16 words

A coating composition according to clam 4 or 5, wherein said anhydride is methyl hexahydrophthalic anhydride.

Claim 8

Dependent Claim 16 words

A coating composition according to clam 4 or 5, wherein said anhydride is methyl hexahydrophthalic anhydride.

Claim 9

Dependent Claim 35 words

A coating composition according to claim 1, wherein said diepoxide is selected from the group consisting of (i) condensation products of bisphenol-A with epichlorohydrin, (ii) ester diepoxides, (iii) cycloaliphatic diepoxides, and (iv) mixtures of (i)-(iii).

Claim 10

Dependent Claim 81 words

A coating composition according to claim 1 wherein said amine aldehyde crosslinking agent is selected from the group consisting of condensation products of formaldehyde with melamine, substituted melamine, urea, benzoguanamine and substituted benzoguanamine, and mixtures of said condensation products in an amount sufficient to provide between about 0.75 and about 3.75 equivalents of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in said composition either on said tetrahydroxy oligomer or as a hydroxyl group of said hydroxy functional additive.

Claim 11

Dependent Claim 79 words

A composition in accordance with claim 1, wherein said hydroxy functional additive is a polyol selected from the group consisting of (i) hydroxy functional polyesters, (ii) hydroxy functional polyethers, (iii) hydroxy functional oligoesters, (iv) monomeric polyols, (v) hydroxy functional copolymers formed from monoethylenically unsaturated monomers, one or more of which bears hydroxy functionality and which is included in said copolymer in amounts ranging from about 10 to about 50 weight percent of said copolymer, and (vi) mixtures of (i)-(v).

Claim 12

Dependent Claim 30 words

A composition in accordance with claim 1, wherein said composition further comprises up to 15 weight percent based on the total weight of the composition of a flow control additive.

Claim 13

Dependent Claim 106 words

A tetrahydroxy oligomer having a number average molecular weight between about 600-2000 and being the reaction product of: (i) an ester containing pendant hydroxyl and carboxyl functionality and being made by reacting: (a) a C 3 -C 10 aliphatic branched diol, and (b) an alkyl hexahydrophthalic anhydride, wherein (a) and (b) are combined in the reaction mixture in an amount sufficient to allow reaction in about a 1:1 molar ratio; and (ii) a diepoxide having a number average molecular weight between about 130-1500, wherein (i) and (ii) are combined in the reaction mixture in an amount sufficient to allow reaction in about a 2:1 molar ratio.

Claim 14

Dependent Claim 106 words

A tetrahydroxy oligomer having a number average molecular weight between about 600-2000 and being the reaction product of: (i) an ester containing pendant hydroxyl and carboxyl functionality and being made by reacting: (a) a C 3 -C 10 aliphatic branched diol, and (b) an alkyl hexahydrophthalic anhydride, wherein (a) and (b) are combined in the reaction mixture in an amount sufficient to allow reaction in about a 1:1 molar ratio; and (ii) a diepoxide having a number average molecular weight between about 130-1500, wherein (i) and (ii) are combined in the reaction mixture in an amount sufficient to allow reaction in about a 2:1 molar ratio.

Claim 15

Dependent Claim 17 words

A tetrahydroxy oligomer according to claim 11, wherein said aliphatic branched diol contains one primary hydroxy group.

Claim 16

Dependent Claim 21 words

A tetrahydroxy oligomer according to claim 12, wherein the hydroxyl groups of said diol are not attached to adjacent carbon atoms.

Claim 17

Dependent Claim 13 words

A tetrahydroxy oligomer according to claim 13, wherein said diol is 2-ethyl-1,3-hexane diol.

Claim 18

Dependent Claim 27 words

A tetrahydroxy oligomer according to claim 11, wherein the alkyl group of said alkyl hexahydrophthalic anhydride comprises a lower alkyl group having up to about seven carbons.

Claim 19

Dependent Claim 16 words

A tetrahydroxy oligomer according to claim 14 or 15 wherein said anhydride is methyl hexahydrophthalic anhydride.

Claim 20

Dependent Claim 35 words

A tetrahydroxy oligomer according to claim 11, wherein said diepoxide is selected from the group consisting of: (i) condensation products of bisphenol-A with epichlorohydrin, (ii) ester diepoxides, (iii) cycloaliphatic diepoxides, and (iv) mixtures of (i)-(iii).

Claim 21

Dependent Claim 256 words

A high solids thermosetting coating composition adapted for low temperature bake applications which contains greater than about 60 percent by weight of nonvolatile solids, and which exclusive of pigments, and other nonreactive components, consists essentially of: (A) a tetrahydroxy oligomer having a number average molecular weight of between about 600-2000 and being the reaction product of: (i) an ester containing pendant hydroxyl and carboxyl functionality and being made by reacting: (a) a C 3 -C 10 aliphatic branched diol and (b) an alkyl hexahydrophthalic anhydride, wherein (a) and (b) are combined in the reaction mixture in an amount sufficient to allow reaction in about a 1:1 molar ratio; and (ii) a diepoxide having a number average molecular weight between about 130-1500, wherein (i) and (ii) are combined in the reaction mixture in an amount sufficient to allow reaction in about 2:1 molar ratio; (B) an amine-aldehyde crosslinking agent; (C) 0-50 percent based on the total weight of (A), (B), (C), (D) and (E) of a hydroxy functional additive having a number average molecular weight (M n ) of between about 150-6000; (D) solvent; and (E) up to 15 weight percent based on the total weight of (A), (B), (C), (D) and (E) of a flow control additive, said amine-aldehyde crosslinking agent being included in said composition in an amount sufficient to provide at least about 0.60 equivalents of nitrogen corsslinking functionality for each equivalent of hydroxyl functionality included in said composition either on said tetrahydroxy oligomer or as a hydroxyl group of said hydroxy functional additive.

Claim 22

Dependent Claim 256 words

A high solids thermosetting coating composition adapted for low temperature bake applications which contains greater than about 60 percent by weight of nonvolatile solids, and which exclusive of pigments, and other nonreactive components, consists essentially of: (A) a tetrahydroxy oligomer having a number average molecular weight of between about 600-2000 and being the reaction product of: (i) an ester containing pendant hydroxyl and carboxyl functionality and being made by reacting: (a) a C 3 -C 10 aliphatic branched diol and (b) an alkyl hexahydrophthalic anhydride, wherein (a) and (b) are combined in the reaction mixture in an amount sufficient to allow reaction in about a 1:1 molar ratio; and (ii) a diepoxide having a number average molecular weight between about 130-1500, wherein (i) and (ii) are combined in the reaction mixture in an amount sufficient to allow reaction in about 2:1 molar ratio; (B) an amine-aldehyde crosslinking agent; (C) 0-50 percent based on the total weight of (A), (B), (C), (D) and (E) of a hydroxy functional additive having a number average molecular weight (M n ) of between about 150-6000; (D) solvent; and (E) up to 15 weight percent based on the total weight of (A), (B), (C), (D) and (E) of a flow control additive, said amine-aldehyde crosslinking agent being included in said composition in an amount sufficient to provide at least about 0.60 equivalents of nitrogen corsslinking functionality for each equivalent of hydroxyl functionality included in said composition either on said tetrahydroxy oligomer or as a hydroxyl group of said hydroxy functional additive.

Claim 23

Dependent Claim 19 words

A high solids coating composition according to claim 18, wherein said aliphatic branched diol contains one primary hydroxyl group.

Claim 24

Dependent Claim 24 words

A coating composition according to claim 19, wherein the hydroxyl groups of said diol are not attached to adjacent carbon atoms of the diol.

Claim 25

Dependent Claim 13 words

A coating composition according to claim 20, wherein said diol is 2-ethyl-1,3-hexane diol.

Claim 26

Dependent Claim 27 words

A coating composition according to claim 21, wherein the alkyl group of said alkyl hexadrophthalic anhydride comprises a lower alkyl group having up to about seven carbons.

Claim 27

Dependent Claim 16 words

A coating composition according to claim 21 or 22, wherein said anhydride is methyl hexahydrophthalic anhydride.

Claim 28

Dependent Claim 35 words

A coating composition according to claim 18, wherein said diepoxide is selected from the group consisting of: (i) condensation products of bisphenol-A with epichlorohydrin, (ii) ester diepoxides, (iii) cycloaliphatic diepoxides, and (iv) mixtures of (i)-(iii).

Claim 29

Dependent Claim 80 words

A coating composition according to claim 18, wherein said amine-aldehyde crosslinking agent is selected from the group consisting of condensation products of formaldehyde with melamine, substituted melamine, urea, benzoquamine and substituted benzoquanamine, and mixtures of said condensation products in an amount sufficient to provide between about 0.75 and about 3.75 equivalents of nitrogen crosslinking functionality for each equivalent of hydroxy functionality included in said composition either on said tetrahydroxy oligomer or as a hydroxyl group of said hydroxy functional additive.

Claim 30

Dependent Claim 79 words

A coating composition according to claim 18, wherein said hydroxy functional additive is a polyol selected from the group consisting of (i) hydroxy functional polyesters, (ii) hydroxy functional polyethers, (iii) hydroxy functional oligoesters, (iv) monomeric polyols, (v) hydroxy functional copolymers formed from monoethylenically unsaturated monomers, one or more of which bears hydroxy functionality and which is included in said copolymer in amounts ranging from about 10 to about 50 weight percent of said copolymer, and (vi) mixtures of (i)-(v).

Annuity Stage	Window Opens	Payment Deadline	Surcharge Period Until	Estimated Fee	Status
3.5 Years (Year 4)	1986-11-28	1987-05-30	1987-11-29	$2000.00	Window Closed / Lapsed
7.5 Years (Year 8)	1990-11-28	1991-05-30	1991-11-29	$3760.00	Window Closed / Lapsed
11.5 Years (Year 12)	1994-11-28	1995-05-30	1995-11-29	$7700.00	Window Closed / Lapsed

High solids coatings from new tetrahydroxy oligomers

Abstract

Inventors

Bibliographic Details

Claims Analysis

References Cited (Backward Citations)

USPTO Annuity & Maintenance Windows

Assigned Categories & Tags

Assign Category Tag