Method of and solution for electroplating chromium and chromium alloys and method of making the solution
Assignee: International Business Machines Corp
•
Filing: 1982-09-22
•
Granted: 1983-11-29
•
Expires: 2002-09-22
Abstract
Abstract A plating solution and method of forming such a solution for plating chromium and its alloys from Cr(III) is disclosed. The solution is an aqueous solution of a chromium(III) thiocyanate complex having at least a ligand other than water or thiocyanate in the inner coordination sphere.
Inventors
- 👤 Donald J. Barclay
- 👤 William M. Morgan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 01:53
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/04; C25D3/06
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
92 words
An electroplating solution consisting essentially of an aqueous, time and temperature equilibrated solution of buffered chromium(III) thiocyanate complexes having at least one ligand other than thiocyanate or water selected from the group Cl -1 , Br -1 , SO 4 -2 , PO 4 -3 , and NO 3 -1 in the chromium(III) inner coordination sphere, said equilibration being equivalent to that which is achieved by heating the solution for about one hour at 80° C., and the solution concentration of chromium-to-thiocyanate being in the molar ratio of from 1-to-2 to 1-to-6.
Claim 2
Dependent Claim
92 words
An electroplating solution consisting essentially of an aqueous, time and temperature equilibrated solution of buffered chromium(III) thiocyanate complexes having at least one ligand other than thiocyanate or water selected from the group Cl -1 , Br -1 , SO 4 -2 , PO 4 -3 , and NO 3 -1 in the chromium(III) inner coordination sphere, said equilibration being equivalent to that which is achieved by heating the solution for about one hour at 80° C., and the solution concentration of chromium-to-thiocyanate being in the molar ratio of from 1-to-2 to 1-to-6.
Claim 3
Dependent Claim
62 words
A solution as claimed in claim 1 in which the complex is said chromium(III) thiocyanate complex having the general formula: ((H.sub.2 O).sub.x CR.sup.III L.sub.y (NCS).sub.z) where x is zero or a positive integer and y and z are each positive integers, the sum of x, y and z not exceeding six; and where L is a ligand other than thiocyanate or water.
Claim 4
Dependent Claim
45 words
A solution as claimed in claim 2 in which the chromium(III) thiocyanate complex is a chromium(III) thiocyanate complex having the general formula: ((H.sub.2 O).sub.6-m-n Cr.sup.III Cl.sub.m (NCS).sub.n).sup.3-m-n where m and n are each positive integers and where the sum of m+n does not exceed six.
Claim 5
Dependent Claim
45 words
A solution as claimed in claim 2 in which the mixed chromium(III) thiocyanate complexes have the general formula: ((H.sub.2 O).sub.6-2m-n Cr.sup.III (SO.sub.4).sub.m (NCS).sub.n).sup.3-2m-n where m is 1 or 2 and n is an integer of at least 1, and where 2m+n does not exceed six.
Claim 6
Dependent Claim
22 words
A solution as claimed in claim 1 in which the solution includes a member of the group sodium chloride and potassium chloride.
Claim 7
Dependent Claim
28 words
A solution as claimed in claim 1 in which the complex is chromium salt in equilibrium with a thiocyanate salt selected from the group sodium and potassium thiocyanate.
Claim 8
Dependent Claim
43 words
A solution as claimed in claim 6 in which the chromium salt is selected from the group chromium chloride (CrCl 3 .6H 2 O), chromium bromide (CrBr 3 .6H 2 O) and chromium sulphate (Cr 2 (SO 4 ) 3 .15H 2 O).
Claim 9
Dependent Claim
32 words
A solution as claimed in claim 1 in which the complex is formed by equilibrating a chromium thiocyanate salt with a salt selected from the group sodium and potassium salts of anions.
Claim 10
Dependent Claim
18 words
A solution as claimed in claim 1 in which the pH is in the range 4.0 to 2.0.
Claim 11
Dependent Claim
14 words
A solution as claimed in claim 1 which includes boric acid in saturation concentration.
Claim 12
Dependent Claim
28 words
A solution as claimed in claim 1 further characterized by a source of nickel comprising nickel sulphate (NiSO 4 .6H 2 O) whereby to plate chromium nickel alloy.
Claim 13
Dependent Claim
28 words
A solution as claimed in claim 1 further characterized by a source of cobalt comprising cobalt sulphate (CoSO 4 .7H 2 O) whereby to plate a chromium-cobalt alloy.
Claim 14
Dependent Claim
119 words
A process of plating chromium or a chromium containing alloy comprising passing an electroplating current between an anode and a cathode in a plating solution consisting essentially of, an essentially aqueous equilibrated solution of buffered chromium(III) thiocyanate complexes having at least one ligand other than thiocyanate or water selected from the group Cl -1 , Br -1 , SO 4 -2 , PO 4 -3 and NO 3 -1 in the chromium(III) inner coordination sphere in effective concentration for electroplating of chromium, the solution concentration of chromium-to-thiocyanate being in the molar ratio of from 1-to-2 to 1-to-6, and the equilibration of said solution being equivalent to that achieved by heating said solution for about one hour at 80° C.
Claim 15
Dependent Claim
119 words
A process of plating chromium or a chromium containing alloy comprising passing an electroplating current between an anode and a cathode in a plating solution consisting essentially of, an essentially aqueous equilibrated solution of buffered chromium(III) thiocyanate complexes having at least one ligand other than thiocyanate or water selected from the group Cl -1 , Br -1 , SO 4 -2 , PO 4 -3 and NO 3 -1 in the chromium(III) inner coordination sphere in effective concentration for electroplating of chromium, the solution concentration of chromium-to-thiocyanate being in the molar ratio of from 1-to-2 to 1-to-6, and the equilibration of said solution being equivalent to that achieved by heating said solution for about one hour at 80° C.
Claim 16
Dependent Claim
57 words
The process of claim 13 wherein the chromium(III) complex has the formula: (H.sub.2 O).sub.x Cr.sup.III L.sub.y (NCS).sub.2 where x is zero or a positive integer and y and z are each positive integers, and where the sum of x, y and z does not exceed six; and where L is the ligand other than water or thiocyanate.
Claim 17
Dependent Claim
35 words
The process of claim 14 wherein the chromium(III) complex has the formula: ((H.sub.2 O).sub.6-m-n Cr.sup.III Cl.sub.m (NCS).sub.n).sup.3-m-n where m and n are each positive integers and where the sum of m+n does not exceed six.
Claim 18
Dependent Claim
39 words
The process of claim 14 wherein the chromium(III) complex has the formula: ((H.sub.2 O).sub.6-2m-n Cr.sup.III (SO.sub.4).sub.m (NCS).sub.n).sup.3-2m-n where m is 1 or 2 and n is an integer of at least 1 and where 2m+n does not exceed six.
Claim 19
Independent Claim
96 words
A method of preparing a chromium plating solution comprising equilibrating in an essentially aqueous, buffered solution, a chromium(III) salt selected from the groups of chloride, bromide, sulfate, phosphate and nitrate, and a thiocyanate salt selected from the group of sodium and potassium thiocyanate, the solution concentration of chromium(III)-to-thiocyanate being in the molar ratio of from 1-to-2 to 1-to-6, and the equilibrating of said solution being equivalent to that achieved by heating the solution for about one hour and at a temperature of 80° C. such that said equilibrated plating solution consists essentially of chromium(III) thiocyanate complexes.
Claim 20
Independent Claim
96 words
A method of preparing a chromium plating solution comprising equilibrating in an essentially aqueous, buffered solution, a chromium(III) salt selected from the groups of chloride, bromide, sulfate, phosphate and nitrate, and a thiocyanate salt selected from the group of sodium and potassium thiocyanate, the solution concentration of chromium(III)-to-thiocyanate being in the molar ratio of from 1-to-2 to 1-to-6, and the equilibrating of said solution being equivalent to that achieved by heating the solution for about one hour and at a temperature of 80° C. such that said equilibrated plating solution consists essentially of chromium(III) thiocyanate complexes.
Claim 21
Independent Claim
106 words
A method of preparing a chromium plating solution comprising equilibrating in an essentially aqueous buffered solution, a chromium(III) thiocyanate salt with a salt selected from the group sodium and potassium salts of an anion selected from the group of Cl -1 , Br -1 , SO 4 -2 , PO 4 -3 and NO 3 -1 , the solution's chromium(III)-to-thiocyanate concentrations being in the molar ratio of from 1-to-2 to 1-to-6, and the solution's equilibration being equivalent to that which is achieved by heating the solution for about one hour at 80° C., such that the resulting equilibrated solution consists essentially of the chromium(III) thiocyanate complexes.
Claim 22
Independent Claim
106 words
A method of preparing a chromium plating solution comprising equilibrating in an essentially aqueous buffered solution, a chromium(III) thiocyanate salt with a salt selected from the group sodium and potassium salts of an anion selected from the group of Cl -1 , Br -1 , SO 4 -2 , PO 4 -3 and NO 3 -1 , the solution's chromium(III)-to-thiocyanate concentrations being in the molar ratio of from 1-to-2 to 1-to-6, and the solution's equilibration being equivalent to that which is achieved by heating the solution for about one hour at 80° C., such that the resulting equilibrated solution consists essentially of the chromium(III) thiocyanate complexes.
References Cited (Backward Citations)
US2088615A
Cited
US2822326A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-28 | 1987-05-30 | 1987-11-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-28 | 1991-05-30 | 1991-11-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-28 | 1995-05-30 | 1995-11-29 | $7700.00 | Window Closed / Lapsed |