Processes for manufacturing insulated-gate semiconductor devices with integral shorts
Assignee: Fairchild Semiconductor Corp
•
Filing: 1982-08-09
•
Granted: 1983-11-29
•
Expires: 2002-08-09
Abstract
Abstract Processes for manufacturing insulated-gate semiconductor devices characterized by involving a minimal number of photolithographic masking steps and being fail-safe in a number of respects. A number of process alternatives are disclosed for forming a shorting extension of a base region up through and to a portion of the surface of a source region, many of these process alternatives involving self-masking techniques to define the source region surface portion. Two general MOSFET structures are formed in accordance with the procedures of the invention. One structure has metallized gate terminal fingers, and is formed employing one-mask processes. The other structure has gate fingers encased in insulating oxide and connected to remote gate contacts. For both structures, selective oxidation of the polysilicon gate electrode material is preferred, and various approaches to this selective oxidation are described.
Inventors
- 👤 Victor A. K. Temple
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:18
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/60; H10D30/64; H10D30/66; H10D12/00; H10D12/01; H10D12/031; H10D12/032; H10D12/411; H10D12/441; H10D30/01; H10D30/021; H10D30/028; H10D30/0291; H10D62/00; H10D62/10; H10D62/17; H10D62/393; H10D84/00; H10D84/01; H10D84/0102; H10D84/0105; H10P; H10P76/00; H10P76/40; H10P30/00; H10P30/20; H10P30/22; H10P30/221; H10P30/222; Y; Y10; Y10S; Y10S438/00; Y10S438/942; Y10S438/944
Claims Analysis
Total Claims: 37
Claim 1
Independent Claim
389 words
A self-aligned process for manufacturing an insulated-gate semiconductor device including an integral short, said process comprising: providing a semiconductor wafer including a first region of one conductivity type having a principal surface, and preparing the wafer by forming on the principal surface a gate insulating region layer, forming on the gate insulating region layer a conductive gate electrode layer, and forming on the conductive gate electrode layer an overhang layer; forming an etch resist mask having openings defining the ultimate location of upper electrode regions, and then etching in areas defined by the mask openings through the overhang layer and through the conductive gate electrode layer at least to the gate insulating region layer, with lateral etching of the conductive gate electrode layer to undercut the overhand layer, thereby defining gate electrodes extending upwardly from and spaced along the first region principal surface, with overhanging portions of the overhang layer on the upper surfaces of the gate electrodes; oxidizing at least the conductive gate electrode sidewalls; introducing into the first region between the gate electrodes impurities appropriate to form a base region of opposite conductivity type and an upper electrode region of the one conductivity type within the base region, the gate electrodes serving as masks during the introduction of impurities, and diffusing the impurities introduced to appropriately locate and configure the base and upper electrode regions such that at the principal surface the base region exists as a band of opposite conductivity type between the upper electrode region and the first region, with active portions of the band underlying at least a portion of at least one gate electrode and being separated therefrom by portions of the gate insulating region layer; forming a shorting extension of the base region up through and to a portion of the surface of the upper electrode region intermediate and spaced from the gate electrodes to facilitate an ohmic connection between the base and upper electrode regions, the forming of the shorting extension being accomplished by employing the overhang of the overhang layer as a mask to define said portion of the surface of the upper electrode region; and forming a metallized gate terminal in electrical contact with the conductive gate electrodes, and forming a metallized upper electrode region terminal in electrical contact with the upper electrode region and with the shorting extension.
Claim 2
Dependent Claim
389 words
A self-aligned process for manufacturing an insulated-gate semiconductor device including an integral short, said process comprising: providing a semiconductor wafer including a first region of one conductivity type having a principal surface, and preparing the wafer by forming on the principal surface a gate insulating region layer, forming on the gate insulating region layer a conductive gate electrode layer, and forming on the conductive gate electrode layer an overhang layer; forming an etch resist mask having openings defining the ultimate location of upper electrode regions, and then etching in areas defined by the mask openings through the overhang layer and through the conductive gate electrode layer at least to the gate insulating region layer, with lateral etching of the conductive gate electrode layer to undercut the overhand layer, thereby defining gate electrodes extending upwardly from and spaced along the first region principal surface, with overhanging portions of the overhang layer on the upper surfaces of the gate electrodes; oxidizing at least the conductive gate electrode sidewalls; introducing into the first region between the gate electrodes impurities appropriate to form a base region of opposite conductivity type and an upper electrode region of the one conductivity type within the base region, the gate electrodes serving as masks during the introduction of impurities, and diffusing the impurities introduced to appropriately locate and configure the base and upper electrode regions such that at the principal surface the base region exists as a band of opposite conductivity type between the upper electrode region and the first region, with active portions of the band underlying at least a portion of at least one gate electrode and being separated therefrom by portions of the gate insulating region layer; forming a shorting extension of the base region up through and to a portion of the surface of the upper electrode region intermediate and spaced from the gate electrodes to facilitate an ohmic connection between the base and upper electrode regions, the forming of the shorting extension being accomplished by employing the overhang of the overhang layer as a mask to define said portion of the surface of the upper electrode region; and forming a metallized gate terminal in electrical contact with the conductive gate electrodes, and forming a metallized upper electrode region terminal in electrical contact with the upper electrode region and with the shorting extension.
Claim 3
Dependent Claim
45 words
A process in accordance with claim 1, wherein the steps of introducing base region and upper electrode region impurities comprise ion implantation at angles so as to implant the entire active area of the first region principal surface except where masked by the gate electrodes.
Claim 4
Dependent Claim
36 words
A process in accordance with claim 2, wherein the steps of ion implantation are carried out prior to removal of the gate insulating region layers and the ion implantation is through the gate insulating region layers.
Claim 5
Dependent Claim
94 words
A process in accordance with claim 2, wherein the step of forming a shorting extension of the base region comprises introducing into the first region by means of of ion implantation impurities appropriate to form a shorting region of the opposite conductivity type laterally within the upper electrode region but extending downwardly into the base region, implantation of the shorting region impurities being accomplished substantially vertically with the overhang of the overhang layer serving as a mask such that only a portion of the first region principal surface between the gate electrodes is implanted.
Claim 6
Dependent Claim
17 words
A process in accordance with claim 4, wherein the overhang layer provided comprises a refractory metal silicide.
Claim 7
Dependent Claim
30 words
A process in accordance with claim 5, wherein the step of preparing the wafer further comprises forming a protective layer of silicon nitride over the refractory metal silicide overhang layer.
Claim 8
Dependent Claim
95 words
A process in accordance with claim 6, wherein the step of forming a shorting extension of the base region comprises subsequent to introduction of base region impurities but prior to implanting upper electrode region impurities, forming a self-registered implant mask over a portion of the surface between the gate electrodes by evaporating and depositing metal substantially vertically with the overhang of the second conductive gate electrode serving as a mask during evaporation deposition such that, upon subsequent implantation of the upper electrode region impurities, the area covered by the self-registered implant mask is not implanted.
Claim 9
Dependent Claim
93 words
A process in accordance with claim 1, wherein the step of forming a shorting extension of the base region comprises introducing into the first region by means of ion implantation impurities appropriate to form a shorting region of the opposite conductivity type laterally within the upper electrode region but extending downwardly into the base region, implantation of the shorting region impurities being accomplished substantially vertically with the overhang of the overhang layer serving as a mask such that only a portion of the first region principal surface between the gate electrodes is implanted.
Claim 10
Dependent Claim
42 words
A process in accordance with claim 1, wherein at least the step of introducing base region impurities comprises gas source diffusion to ensure coverage of the entire active area of the first region principal surface except where masked by the gate electrodes.
Claim 11
Dependent Claim
44 words
A process in accordance with claim 1, wherein the steps of introducing base region and upper electrode region impurities comprise gas source diffusion to ensure coverage of the entire active area of the first region principal surface except where masked by the gate electrodes.
Claim 12
Dependent Claim
93 words
A process in accordance with claim 10, wherein the step of forming a shorting extension of the base region comprises introducing into the first region by means of ion implantation impurities appropriate to form a shorting region of the opposite conductivity type laterally within the upper electrode region but extending downwardly into the base region, implantation of the shorting region impurities being accomplished substantially vertically with the overhang of the overhang layer serving as a mask such that only a portion of the first region principal surface between the gate electrodes is implanted.
Claim 13
Dependent Claim
17 words
A process in accordance with claim 11, wherein the overhang layer provided comprises a refractory metal silicide.
Claim 14
Dependent Claim
29 words
A process in accordance with claim 12, wherein the step of preparing the wafer further comprises forming a protective layer of nitride over the refractory metal silicide overhang layer.
Claim 15
Dependent Claim
178 words
A process in accordance with claim 1, wherein the steps of introducing base region and upper terminal region impurities and forming a shorting extension of the base region comprise: first, providing a bare semiconductor surface in the region between the gate electrodes; second, pre-depositing base region impurities on the bare semiconductor surface from a gas source while growing minimal oxide; third, forming a nitride layer on the entire exposed surface between the gate electrodes; fourth, forming a self-registered metal etchant mask over a portion of the nitride layer on the exposed surface by evaporating and depositing metal substantially vertically with the overhang of the overhang layer serving as a mask during evaporation deposition; fifth, forming a nitride diffusion mask by selectively etching to remove the nitride layer and any oxide on the exposed surface except where masked by the etchant mask, and then selectively etching to remove the metal etchant mask; sixth, introducing and diffusing upper electrode region impurities from a gas source except where masked by the nitride diffusion mask; and seventh, removing the nitride diffusion mask.
Claim 16
Dependent Claim
17 words
A process in accordance with claim 14, wherein the overhang layer provided comprises a refractory metal silicide.
Claim 17
Dependent Claim
30 words
A process in accordance with claim 15, wherein the step of preparing the wafer further comprises forming a protective layer of silicon nitride over the refractory metal silicide overhang layer.
Claim 18
Dependent Claim
125 words
A process in accordance with claim 1, wherein the steps of introducing base region and upper electrode region impurities and forming a shorting extension of the region comprise: first, providing a bare semiconductor surface in the region between the gate electrodes; second, pre-depositing base region impurities on the bare semiconductor surface from a gas source while growing minimal oxide; third, forming a self-registered nitride diffusion mask on a portion of the surface between the gate electrodes by introducing nitrogen by means of substantially vertical ion implantation, with the overhang of the overhang layer serving as a mask during implantation; fourth, introducing and diffusing upper electrode region impurities from a gas source where masked by the nitride diffusion mask; and fifth, removing the nitride diffusion mask.
Claim 19
Dependent Claim
90 words
A process in accordance with claim 1, wherein the steps of introducing base region and source region impurities comprise: first, providing a bare semiconductor surface in the region between the gate electrodes; second, diffusing from a gas source base region impurities into the region between the gate electrodes while growing minimal oxide; and third, introducing by means of ion implantation impurities appropriate to form the upper electrode region, implantation of the upper terminal region impurities being accomplished at angles so as to implant the entire area between the gate electrodes.
Claim 20
Dependent Claim
93 words
A process in accordance with claim 18, wherein the step of forming a shorting extension of the base region comprises subsequent to introduction of base region impurities but prior to implanting upper electrode region impurities, forming a self-registered implant mask over a portion of the surface between the gate electrodes by evaporating and depositing metal substantially vertically with the overhang of the overhang layer serving as a mask during evaporation deposition, such that upon subsequent implantation of the upper terminal region impurities the area covered by the self-registered implant mask is not implanted.
Claim 21
Dependent Claim
16 words
A process in accordance with claim 19, wherein the overhang layer provided comprises refractory metal silicide.
Claim 22
Dependent Claim
30 words
A process in accordance with claim 20, wherein the step of preparing the wafer further comprises forming a protective layer of silicon nitride over the refractory metal silicide overhang layer.
Claim 23
Dependent Claim
40 words
A process in accordance with claim 1, wherein the overhang layer is formed of a conductive material in electrical contact with the conductive gate electrode layer and at least portions of the overhang layer remain in the final device structure.
Claim 24
Dependent Claim
16 words
A process in accordance with claim 22, wherein the overhang layer provided comprises a refractory metal.
Claim 25
Dependent Claim
29 words
A process in accordance with claim 23, wherein the step of preparing the wafer further comprises forming a protective nitride layer over the refractory metal of the overhang layer.
Claim 26
Dependent Claim
17 words
A process in accordance with claim 22, wherein the overhang layer provided comprises a refractory metal silicide.
Claim 27
Dependent Claim
30 words
A process in accordance with claim 25, wherein the step of preparing the wafer further comprises forming a protective layer of silicon nitride over the refractory metal silicide overhang layer.
Claim 28
Dependent Claim
117 words
A process in accordance with claim 22, which comprises removing all non-conductive layers over the upper electrode region and ensuring that an insulating layer is provided over the overhang layer portions such that the gate electrodes are encased in insulation, providing another mask with a window defining at least one gate contact area on a portion of the wafer other than at an active device region, employing the window in the other mask to etch through the insulating layer over the gate electrode area to form a contact opening, removing the other mask, evaporating metal onto the wafer, and patterning by means of yet another mask to define separate upper electrode region terminals and gate electrode terminals.
Claim 29
Dependent Claim
118 words
A process in accordance with claim 1, wherein the gate insulating region layer is formed including at least one oxide layer and a nitride layer covering the oxide layer; and wherein the step of oxidizing at least the gate electrode sidewalls comprises thermally selectively oxidizing the gate electrode sidewalls to grow an oxide layer thicker than the one oxide layer in the gate insulating region layer, with oxidation of the upper electrode region between the gate electrodes being masked by the nitride layer in the gate insulating region layer; and said process further comprises removing the nitride and oxide layers of the gate insulating layer region between the gate electrodes to expose semiconductor in the upper electrode region.
Claim 30
Dependent Claim
72 words
A process in accordance with claim 1, wherein the step of oxidizing at least the gate electrode sidewalls comprises thermally selectively oxidizing the gate electrode sidewalls by forming a nitride oxidation mask layer over the upper electrode region between the polysilicon gate electrodes; and said process further comprises removing the nitride oxidation mask layer and the gate insulating layer region between the gate electrodes to expose semiconductor in the upper electrode region.
Claim 31
Dependent Claim
18 words
A process in accordance with claim 29, wherein the nitride oxidation mask layer is formed by ion implantation.
Claim 32
Dependent Claim
21 words
A process in accordance with claim 29, wherein the nitride oxidation mask layer is formed by directional low pressure vapor deposition.
Claim 33
Dependent Claim
17 words
A process in accordance with claim 29, wherein the nitride oxidation mask layer is formed by sputtering.
Claim 34
Dependent Claim
62 words
A process in accordance with claim 1, which comprises removing all non-conductive layers over the upper electrode region and over the gate electrodes, and wherein the metallized upper electrode region terminal and the gate electrode terminal are formed by depositing metal onto the wafer surface to form automatically separated areas of metallization over the upper electrode region and over the gate electrode.
Claim 35
Dependent Claim
113 words
A process in accordance with claim 1, which comprises removing all non-conductive layers over the upper electrode region and providing an insulating layer over the gate electrodes such that the gate electrodes are encased in insulation, providing another mask with a window defining at least one gate contact area on a portion of the wafer other than at an active device region, employing the window in the other mask to etch through the insulating layer over the gate electrode area to form a contact opening, removing the other mask, evaporating metal onto the wafer, and patterning by means of yet another mask to define separate upper electrode region terminals and gate electrode terminals.
Claim 36
Dependent Claim
343 words
A self-aligned process for manufacturing an insulated-gate semiconductor device including an integral short, said process comprising: providing a semiconductor wafer including a first region of one conductivity type having a principal surface, and preparing the wafer by forming on the principal surface a gate insulating region layer and forming on the gate insulating region layer a conductive gate electrode layer; forming an etch resist mask having openings defining the ultimate location of upper electrode regions, and then etching in areas defined by the mask openings through the gate electrode layer at least to the gate insulating region layer, thereby defining gate electrodes extending upwardly from and spaced along the first region principal surface; oxidizing at least the gate electrode sidewalls; introducing into the first region between the gate electrodes impurities appropriate to form a base region of opposite conductivity type and an upper electrode region of the one conductivity type within the base region, and diffusing the impurities introduced to appropriately locate and configure the base and upper electrode regions such that at the principal surface the base region exists as a band of opposite conductivity type between the upper electrode region and the first region, with active portions of the band underlying at least a portion of at least one gate electrode and separated by portions of the gate insulating layer, the base region impurities being first introduced, and the upper electrode region impurities being subsequently introduced by ion implantation at sharp angles such that the surface between the gate electrodes is covered except for an intermediate portion shadowed by the gate electrodes, the unshadowed intermediate portion being a shorting extension of the base region up through and to a portion of the surface of the upper electrode region intermediate and spaced from the gate electrodes to facilitate an ohmic connection between the base and upper electrode regions; and forming a metallized gate terminal in electrical contact with the gate electrodes, and forming a metallized upper electrode region terminal in electrical contact with the upper electrode region and with the shorting extension.
Claim 37
Dependent Claim
343 words
A self-aligned process for manufacturing an insulated-gate semiconductor device including an integral short, said process comprising: providing a semiconductor wafer including a first region of one conductivity type having a principal surface, and preparing the wafer by forming on the principal surface a gate insulating region layer and forming on the gate insulating region layer a conductive gate electrode layer; forming an etch resist mask having openings defining the ultimate location of upper electrode regions, and then etching in areas defined by the mask openings through the gate electrode layer at least to the gate insulating region layer, thereby defining gate electrodes extending upwardly from and spaced along the first region principal surface; oxidizing at least the gate electrode sidewalls; introducing into the first region between the gate electrodes impurities appropriate to form a base region of opposite conductivity type and an upper electrode region of the one conductivity type within the base region, and diffusing the impurities introduced to appropriately locate and configure the base and upper electrode regions such that at the principal surface the base region exists as a band of opposite conductivity type between the upper electrode region and the first region, with active portions of the band underlying at least a portion of at least one gate electrode and separated by portions of the gate insulating layer, the base region impurities being first introduced, and the upper electrode region impurities being subsequently introduced by ion implantation at sharp angles such that the surface between the gate electrodes is covered except for an intermediate portion shadowed by the gate electrodes, the unshadowed intermediate portion being a shorting extension of the base region up through and to a portion of the surface of the upper electrode region intermediate and spaced from the gate electrodes to facilitate an ohmic connection between the base and upper electrode regions; and forming a metallized gate terminal in electrical contact with the gate electrodes, and forming a metallized upper electrode region terminal in electrical contact with the upper electrode region and with the shorting extension.
References Cited (Backward Citations)
US4084986A
Cited
US4232439A
Cited
US4148054A
Cited
US4290844A
Cited
US4319395A
Cited
US4242791A
Cited
US4344081A
Cited
US4345265A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-28 | 1987-05-30 | 1987-11-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-28 | 1991-05-30 | 1991-11-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-28 | 1995-05-30 | 1995-11-29 | $7700.00 | Window Closed / Lapsed |