Assignee: ConocoPhillips Co
•
Filing: 1981-06-29
•
Granted: 1983-11-15
•
Expires: 2001-06-29
Abstract
Abstract A method is provided for the production of ultrahigh molecular weight drag reducing substances and the like comprising: (a) preparing under an inert atmosphere a catalyst comprising: (1) titanium halide of the general formula TiXm wherein m=2.5 to 4.0 and X is a halogen; (2) a co-catalyst such as an organo-aluminum or organo-aluminum halide of the formula AlRnX3-n where R is a hydrocarbon radical containing from 1 to 20 carbon atoms, X is a halogen and n is 2 or 3; (3) a monoether compound of the formula R1OR2 where R1, and R2 are, independently, aryl, alkyl, cycloalkyl, aralkyl, or alkaryl, each having up to 20 carbon atoms, and placing the catalyst in contact with; (b) alpha-monoolefinic hydrocarbons having from 2 to 30 carbon atoms under suitable temperature conditions to provide an ultrahigh molecular weight hydrocarbon soluble polymer, then (c) ceasing polymerization at a polymer content of 20% by weight or less, based on the total reaction mixture.
Inventors
- 👤 Mark P. Mack
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 04:53
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
145 words
A method for the production of non-crystalline hydrocarbon soluble ultrahigh molecular weight drag reducing polymers comprising (a) preparing under an inert atmosphere a catalyst comprising; (1) titanium trichloride (2) a co-catalyst comprising an organo-aluminum or organo-aluminum halide of the general formula AlR n X 3-n where R is a hydrocarbon radical, X is a halogen or hydrogen and n is 2 or 3; and a (3) a monoether compound of the general formula R 1 OR 2 , wherein R 1 and R 2 are, independently, aryl, alkyl, cycloalkyl, aralkyl or alkaryl each containing from 1 to 20 carbon atoms and placing the catalyst in contact with; (b) C 2 -C 30 α-monoolefinic hydrocarbons under temperature conditions suitable to form high molecular weight polymers, then (c) ceasing polymerization at a polymer content level of 20% by weight or less, based on the total reaction mixture.
Claim 2
Independent Claim
145 words
A method for the production of non-crystalline hydrocarbon soluble ultrahigh molecular weight drag reducing polymers comprising (a) preparing under an inert atmosphere a catalyst comprising; (1) titanium trichloride (2) a co-catalyst comprising an organo-aluminum or organo-aluminum halide of the general formula AlR n X 3-n where R is a hydrocarbon radical, X is a halogen or hydrogen and n is 2 or 3; and a (3) a monoether compound of the general formula R 1 OR 2 , wherein R 1 and R 2 are, independently, aryl, alkyl, cycloalkyl, aralkyl or alkaryl each containing from 1 to 20 carbon atoms and placing the catalyst in contact with; (b) C 2 -C 30 α-monoolefinic hydrocarbons under temperature conditions suitable to form high molecular weight polymers, then (c) ceasing polymerization at a polymer content level of 20% by weight or less, based on the total reaction mixture.
Claim 3
Dependent Claim
126 words
A method as described in claim 1 wherein the catalyst comprises: (a) crystalline titanium trichloride prepared by a method selected from the group consisting of (1) reducing titanium tetrachloride with a metal (2) reducing titanium tetrachloride with hydrogen, (3) reducing titanium tetrachloride with an organo metallic compound, and (4) milling titanium trichloride with the salt of a Group III metal (b) 2.5 to 10 weight percent based on the weight of the titanium trichloride component of a saturated monocyclic of bicyclic monoterpenic ketone selected from the group consisting of menthone, carvomenthone, thujone, verbanone, verbenone, camphor, and fenchone, and (c) 0-1.0 weight percent based upon the total weight of the titanium trichloride component of compound selected from the group consisting of Group IA and IIA metal halides.
Claim 4
Dependent Claim
17 words
A method as described in claim 2 wherein the alpha-monoolefins contain from 8 to 10 carbon atoms.
Claim 5
Dependent Claim
27 words
A method as described in claim 3 wherein polymerization is ceased at a polymer content level of about 10-12% by weight, based on the total reaction mixture.
Claim 6
Dependent Claim
49 words
A method as described in claim 3 wherein the co-catalyst is selected from the group consisting of trimethylaluminum, triethylaluminum, tri-n-propylaluminum, tri-n-butylaluminum, triisobutylaluminum, tri-n-hexylaluminum, tri(2-methyl pentyl) aluminum, tri-n-octylaluminum, diethylaluminum hydride, diisobutylaluminum hydrides, dimethylaluminum chloride, diethylaluminum chloride, diethylaluminum bromide, diethylaluminum iodide, di-n-propylaluminum chloride, di-n-butylaluminum chloride, diisobutylaluminum chloride, and mixtures of these.
Claim 7
Dependent Claim
26 words
A method as described in claim 5 wherein the ratio of the aluminum to ether to titanium compound is from about 1/0.01/1 to about 15/5/5, respectively.
Claim 8
Dependent Claim
28 words
A method as described in claim 6 wherein the mole ratio of the ether component to the aluminum alkyl component is from about 0.01 to about 1, respectively.
Claim 9
Dependent Claim
18 words
A method as described in claim 7 wherein the polymerization is carried out in an inactive hydrocarbon solvent.
Claim 10
Dependent Claim
28 words
A method as described in claim 8 wherein the solvent is selected from the group consisting of pentane, hexane, heptane, octane, benzene, toluene, xylene, and mixtures of these.
Claim 11
Dependent Claim
17 words
A method as described in claim 9 wherein the polymerization is carried out under an inert atmosphere.
Claim 12
Dependent Claim
22 words
A method as described in claim 10 wherein the inert atmosphere is selected from the group consisting of nitrogen, xeon, and argon.
Claim 13
Dependent Claim
23 words
A method as described in claim 1 wherein the catalyst is TiCl 3 .nAlCl 3 , wherein n is from 0.0 to 0.50.
References Cited (Backward Citations)
GB835759A
Cited
US3116274A
Cited
US2895915A
Cited
GB918740A
Cited
US3367909A
Cited
US3355379A
Cited
US3692676A
Cited
US4142991A
Cited
US4124530A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-14 | 1987-05-16 | 1987-11-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-14 | 1991-05-16 | 1991-11-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-14 | 1995-05-16 | 1995-11-15 | $7700.00 | Window Closed / Lapsed |