Water-impermeable polyolefin foam and process for preparing the same
Assignee: Kanegafuchi Chemical Industry Co Ltd
•
Filing: 1982-09-29
•
Granted: 1983-11-15
•
Expires: 2002-09-29
Abstract
Abstract A substantially water-impermeable polyolefin foam made of expandable polyolefin beads. The polyolefin foam is prepared by a particular process in which after heating expandable polyolefin beads and before cooling the heated beads in a mold, the heated beads were allowed to stand in the state that the polyolefin resin maintains the flowability.
Inventors
- 👤 Masahiro Ushirokawa
- 👤 Takeshi Iwahama
- 👤 Kenichi Senda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:59
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/22; C08J9/228; C08J9/232; B; B29; B29C; B29C44/00; B29C44/34; B29C44/36; B29C44/38; B29C44/44; B29C44/445; B29C44/3415; B29C44/3426; B29K; B29K2023/00; B29K2995/00; B29K2995/0037; B29K2995/0068; B29K2995/0069; C08J2323/00; C08J2323/02; Y; Y10; Y10S; Y10S264/00; Y10S264/09; Y10S264/18
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
119 words
A substantially water-impermeable polyolefin molded foam of expanded polyolefin beads, said molded foam being prepared by the steps of filling a mold with expandable beads, heating the expandable beads to melt-adhere the surface of the beads to each other and to expand the beads, allowing the resultant heated beads to stand in the state that the polyolefin resin maintains its flowability whereby voids between the beads are decreased so that the resultant molded foam will have a water-impermeability measured by the volume of leakage of pressurized air of 0.020 kg/cm 2 through the thickness of the foam of not more than 10 ml/100 cm 2 min, cooling the heated beads and removing the resultant molded foam from the mold.
Claim 2
Dependent Claim
119 words
A substantially water-impermeable polyolefin molded foam of expanded polyolefin beads, said molded foam being prepared by the steps of filling a mold with expandable beads, heating the expandable beads to melt-adhere the surface of the beads to each other and to expand the beads, allowing the resultant heated beads to stand in the state that the polyolefin resin maintains its flowability whereby voids between the beads are decreased so that the resultant molded foam will have a water-impermeability measured by the volume of leakage of pressurized air of 0.020 kg/cm 2 through the thickness of the foam of not more than 10 ml/100 cm 2 min, cooling the heated beads and removing the resultant molded foam from the mold.
Claim 3
Dependent Claim
19 words
The substantially water-impermeable polyolefin molded foam of claim 1, wherein the beads are heated to above about 95° C.
Claim 4
Dependent Claim
21 words
The substantially water-impermeable polyolefin molded foam of claim 1, wherein the resultant heated beads are allowed to stand for 45-90 seconds.
Claim 5
Dependent Claim
27 words
The substantially water-impermeable polyolefin molded foam of claim 1, wherein the heated beads are allowed to stand until the intercellular pressure lowers to 1.0 kg/cm 2 G.
Claim 6
Dependent Claim
49 words
The substantially water-impermeable polyolefin molded foam of claim 1, wherein the expanded beads are filled in the mold in the state that the volume of the cavity of the mold is increased, and after the heating and before the cooling, the cavity volume is decreased to a prescribed volume.
Claim 7
Dependent Claim
42 words
The substantially water-impermeble polyolefin molded foam of claim 1, wherein after heating the beads, the volume of the cavity of the mold is increased; and before cooling the heated beads, the increased volume of the cavity is decreased to a prescribed volume.
Claim 8
Dependent Claim
22 words
The substantially water-impermeble polyolefin molded foam of claim 6, wherein the increased volume of the cavity is decreased to the original volume.
References Cited (Backward Citations)
US2823213A
Cited
US2948664A
Cited
US3616365A
Cited
US3743611A
Cited
US3709806A
Cited
US3953558A
Cited
US3959189A
Cited
US4108934A
Cited
US4247650A
Cited
US4275023A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-11-14 | 1987-05-16 | 1987-11-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-11-14 | 1991-05-16 | 1991-11-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-11-14 | 1995-05-16 | 1995-11-15 | $7700.00 | Window Closed / Lapsed |